Microparticles with hierarchical porosity
The present disclosure provides oxide microparticles with engineered hierarchical porosity and methods of manufacturing the same. Also described are structures that are formed by templating, impregnating, and/or precipitating the oxide microparticles and method for forming the same. Suitable applications include catalysts, electrocatalysts, electrocatalysts support materials, capacitors, drug delivery systems, sensors and chromatography.
1. A method comprising:
providing an aqueous sol phase comprising an oxide precursor and an ionic surfactant;
providing an oil phase comprising a non-ionic surfactant; wherein
when adsorbed, the ionic and non-ionic surfactants are able to decrease the interfacial tension sufficiently to lead to spontaneous formation of microemulsion drops; and
the ionic surfactant is soluble only in the sol phase and the non-ionic surfactant is soluble only in the aqueous phase; and
producing an emulsion by combining the aqueous sol phase with the oil phase; wherein the emulsion contains larger droplets containing:
oil microemulsion droplets; and
ionic micelles.
2. The method of claim 1 further comprising subjecting the larger droplets to polymerization and oil and solvent removal to produce oxide microparticles having a bimodal porous network comprising nanopores and mesopores.
3. The method of claim 2 further comprising:
providing a second precursor, wherein said second precursor is a precursor to a secondary material
exposing the microparticles to the second precursor under suitable conditions such that the second precursor is able to at least partially infiltrate the bimodal porous network; and
decomposing the second precursor so as to produce microparticles impregnated with the secondary material.
4. The method of claim 3 further comprising removing the oxide material such that microparticles formed from the secondary material remain substantially intact.
5. The method of claim 3 further comprising:
providing a third precursor wherein the third precursory is a precursor to a tertiary material;
exposing the microparticles to the third precursor under suitable conditions such that the third precursor is able to at least partially infiltrate the bimodal porous network; and
decomposing the third precursor so as to produce microparticles impregnated with nanoparticles formed from the secondary material.
6. The method of claim 5 further comprising selecting the size of the nanoparticles formed from the secondary material by selecting the ionic surfactant.
7. The method of claim 5 wherein the second and third precursors are exposed to the microparticles simultaneously.
8. The method of claim 5 comprising:
exposing the microparticles to the second precursor;
heat-treating the microparticles; and then
exposing the microparticles to the third precursor.
9. The method of claim 3 wherein the secondary material is carbon.
10. The method of claim 5 wherein the secondary material is carbon.
11. The method of claim 5 wherein the tertiary material is platinum.