Devices and methods for tissue engineering
A resorbable tissue scaffold fabricated from bioactive glass fiber forms a rigid three-dimensional porous matrix having a bioactive composition. Porosity in the form of interconnected pore space is provided by the space between the bioactive glass fiber in the porous matrix. Strength of the bioresorbable matrix is provided by bioactive glass that fuses and bonds the bioactive glass fiber into the rigid three-dimensional matrix. The resorbable tissue scaffold supports tissue in-growth to provide osteoconductivity as a resorbable tissue scaffold, used for the repair of damaged and/or diseased bone tissue.
1. A resorbable three-dimensional tissue scaffold comprising:
bioactive glass fibers;
bioactive glass bonding to at least a portion of the bioactive glass fibers; and
pore space within the three-dimensional tissue scaffold by volatile components removed during the bioactive glass bonding to the bioactive glass fibers,
wherein the pore space creates a porosity between about 40% and about 85% in the resorbable three-dimensional tissue scaffold.
2. tissue scaffold according to claim 1 wherein the pore space within the three-dimensional tissue scaffold has a pore size between about 100 μm and about 500 μm.
3. The tissue scaffold according to claim 2 wherein the pore size has a bi-modal size distribution.
4. The tissue scaffold according to claim 1 wherein a plurality of the bioactive glass fibers are bonded to adjacent bioactive glass fibers providing bundles of bonded bioactive glass fibers.
5. The tissue scaffold according to claim 1 wherein the bioactive glass fibers comprise sodium carbonate, calcium carbonate, phosphorus pentoxide, about 45 mol % to about 60 mol % silica, and an about 2 to an about 10 molar ratio of calcium to phosphate.
6. The tissue scaffold according to claim 1 wherein the bioactive glass fibers comprise glass fiber having a composition in respective mol % quantities of 6% Na 2 O; 7.9% K 2 O; 7.7% MgO; 22.1% CaO; 0% B 2 O 3 ; 1.7% P 2 O 5 ; and 54.6% SiO 2 .
7. The tissue scaffold according to claim 1 wherein the bioactive glass fibers have a diameter ranging from about 1 μm to about 200 μm.
8. The tissue scaffold according to claim 7 wherein the bioactive glass fibers have a diameter ranging from about 5 μm to about 100 μm.
9. A bioactive tissue scaffold comprising:
a rigid three-dimensional matrix of a bioactive composition formed from a process comprising:
mixing a bioactive fiber, a binder, a bioactive glass powder bonding agent, a pore former, and a liquid into a plastically formable batch;
forming the plastically formable batch into a shaped object;
drying the shaped object to remove the liquid;
removing the binder;
removing the pore former; and
heating the shaped object to fuse and bond the bioactive fiber into the rigid three-dimensional matrix using the bioactive glass powder bonding agent with pore space defined by the pore former.
10. The bioactive tissue scaffold according to claim 9 wherein the bioactive glass powder bonding agent is the same composition as the bioactive fiber.
11. The bioactive tissue scaffold according to claim 9 wherein the bioactive fiber comprises sodium carbonate, calcium carbonate, phosphorus pentoxide, about 45 mol % to about 60 mol % silica and an about 2 to an about 10 molar ratio of calcium to phosphate.
12. The bioactive tissue scaffold according to claim 9 wherein the bioactive fiber comprises a mixture of bioactive fiber having different compositions.
13. The bioactive tissue scaffold according to claim 9 wherein the bioactive glass powder bonding agent has a particle size between about 1 to about 1000 times smaller than the diameter of the bioactive glass fiber.
14. The bioactive tissue scaffold according to claim 9 wherein the pore former has a particle size between about 0.1 and about 100 times the bioactive fiber diameter.