Aqueous polyurethane resin, hydrophilic resin, and film
An aqueous polyurethane resin is prepared by reaction of an isocyanate group-terminated prepolymer with a chain extender containing polyamine. The isocyanate group-terminated prepolymer is obtained by reaction of at least a polyisocyanate containing 50 wt % or more of a non-multiple ring polyisocyanate that does not contain an aromatic ring and an aliphatic ring, or contains one aromatic ring or aliphatic ring; polyoxyethylene polyol; and a polyoxyethylene side chain-containing active compound having two or more hydroxyl groups or isocyanate groups at its molecular terminal and having a polyoxyethylene group in the side chain.
1. A hydrophilic resin comprising a first aqueous resin and a second aqueous resin, wherein
the first aqueous resin is an aqueous polyurethane resin obtained by reaction of an isocyanate group-terminated prepolymer with a chain extender containing diamines such that the equivalent ratio of an amino group in the chain extender relative to the isocyanate group in the isocyanate group-terminated prepolymor is 0.8 to 1.2,
wherein the isocyanate group-terminated prepolymer is obtained by reaction of components consisting of:
a polyisocyanate consisting of bis(isocyanatomethyl)cyclohexane,
a polyol component containing polyoxyethylen glycol having the number average molecular weight of 300 to 6000, and
a polyoxyethylene side chain-containing active compound having two or more hydroxyl groups or isocyanate groups at its molecular terminal and having a polyoxyethylene group in its side chain,
the second aqueous resin is an aqueous polyurethane resin obtained by reaction of an isocyanate group-terminated prepolymer with a chain extender containing diamines such that the equivalent ratio of an amino group in the chain extender relative to the isocyanate group in the isocyanate group-terminated prepolymer is 0.8 to 1.2,
wherein the isocyanate group-terminated prepolymer is obtained by reaction components consisting of:
a polyisocyanate consisting of methylenebis(cyclohexyl isocyanate),
a polyol component containing polytetramethylene ether glycol having the number average molecular weight of 300 to 10000, and
an ionic group-containing active compound having both carboxylic acid and two or more hydroxyl groups, wherein the content of the ionic group-containing active compound is 1.5 to 8 wt % relative to the total amount of the raw materials of the second aqueous resin.
2. The hydrophilic resin according to claim 1 , which is used as a coating agent for a moisture-permeation and water-proof treatment.
3. A film obtained by using a hydrophilic resin, wherein the hydrophilic resin comprises a first aqueous resin and a second aqueous resin, wherein
the first aqueous resin is an aqueous polyurethane resin obtained by reaction of an isocyanate group-terminated prepolymer with a chain extender containing diamines
such that the equivalent ratio of an amino group in the chain extender relative to the isocyanate group in the isocyanate group-terminated prepolymer is 0.8 to 1.2,
wherein the isocyanate group-terminated prepolymer is obtained by reaction components consisting of:
a polyisocyanate consisting of bis(isocyanatomethyl)cyclohexane,
a polyol component containing polyoxyethylene glycol having the number average molecular weight of 300 to 6000, and
a polyoxyethylene side chain-containing active compound having two or more hydroxyl groups or isocyanate groups at its molecular terminal and having a polyoxyethylene group in its side chain,
the second aqueous resin is an aqueous polyurethane resin obtained by reaction of an isocyanate group-terminated prepolymer with a chain extender containing diamines such that the equivalent ratio of an amino group in the chain extender relative to the isocyanate group in the isocyanate group-terminated prepolymer is 0.8 to 1.2, wherein the isocyanate group-terminated prepolymer is obtained by reaction components consisting of:
a polyisocyanate consisting of methylenebis(cyclohexyl isocyanate),
a polyol component containing polytetramethylene ether glycol having the number average molecular weight of 300 to 10000, and
an ionic group-containing active compound having both carboxylic acid and two or more hydroxyl groups, wherein the content of the ionic group-containing active compound is 1.5 to 8 wt % relative to the total amount of the raw materials of the second aqueous resin.