Flame suppression agent, system and uses
View Patent ↗Aqueous droplets encapsulated in a flame retardant polymer are useful in suppressing combustion. Upon exposure to a flame, the encapsulated aqueous droplets rupture and vaporize, removing heat and displacing oxygen to retard the combustion process. The polymer encapsulant, through decomposition, may further add free radicals to the combustion atmosphere, thereby further retarding the combustion process. The encapsulated aqueous droplets may be used as a replacement to halon, water mist and dry powder flame suppression systems.
1. A flame suppression agent, comprising:
aqueous droplets encapsulated in a flame retardant polymer, whereby said flame suppression agent is capable of suppressing flames; and wherein said flame suppression agent is non-toxic.
2. The flame suppression agent of claim 1 , wherein the aqueous droplets have a size of approximately 5-250 microns.
3. The flame suppression agent of claim 1 , wherein the aqueous droplets consist essentially of water.
4. The flame suppression agent of claim 1 , wherein the aqueous droplets comprise water and a gelling agent.
5. The flame suppression agent of claim 4 , wherein the gelling agent is selected from the group consisting of gelatin and methyl cellulose.
6. The flame suppression agent of claim 1 , wherein the flame retardant polymer decomposes under heat to produce free radicals.
7. The flame suppression agent of claim 6 , wherein the flame retardant polymer is a halogenated polymer.
8. The flame suppression agent of claim 7 , wherein the flame retardant polymer is a brominated polymer.
9. The flame suppression agent of claim 8 , wherein the brominated polymer is poly(4-bromostyrene).
10. The flame suppression agent of claim 8 , wherein the brominated polymer is poly(1,6-hexamethylene tetrabromoterephthalamide).
11. A method of suppressing a flame, comprising:
applying polymer-encapsulated aqueous droplets to the flame to suppress the flame, wherein said polymer-encapsulated aqueous droplets comprise aqueous droplets encapsulated in a flame retardant polymer; and wherein said flame suppression agent is non-toxic.
12. The method of claim 11 , wherein the aqueous droplets contain essentially water.
13. The method of claim 11 , wherein the aqueous droplets contain water and a gelling agent.
14. The method of claim 11 , wherein the aqueous droplets are encapsulated in a polymer which decomposes to produce free radicals.
15. The method of claim 14 , wherein the aqueous droplets are encapsulated in a halogenated polymer.
16. The method of claim 15 , wherein the halogenated polymer is a brominated polymer.
17. The method of claim 16 , wherein the brominated polymer is selected from the group consisting of poly(4-bromostyrene) and poly(1,6-hexamethylene tetrabromoterephthalamide).
18. A fire suppression system, comprising:
a container containing encapsulated aqueous droplets, wherein said encapsulated aqueous droplets comprise aqueous droplets encapsulated in a flame retardant polymer; and wherein said flame suppression agent is non-toxic; and
a dispenser for dispensing the encapsulated aqueous droplets from the container upon demand to suppress flames.
19. The fire suppression system of claim 18 , wherein the aqueous droplets contain essentially water.
20. The fire suppression system of claim 18 , wherein the aqueous droplets contain water and a gelling agent.
21. The fire suppression system of claim 18 , wherein the container is a pressurized container.
22. The fire suppression system of claim 18 , wherein the fire suppression system is a dry powder fire extinguisher.
23. The fire suppression system of claim 18 , wherein the aqueous droplets are encapsulated in a polymer which decomposes to produce free radicals.
24. The fire suppression system of claim 23 , wherein the aqueous droplets are encapsulated in a halogenated polymer.
25. The fire suppression system of claim 24 , wherein the halogenated polymer is a brominated polymer.
26. The fire suppression system of claim 25 , wherein the brominated polymer is selected from the group consisting of poly(4-bromostyrene) and poly(1,6-hexamethylene tetrabromoterephthalamide).