Method of preparing highly ordered mesoporous silica nanoparticles using the addition of transition metal salts
Disclosed is a method of preparing mesoporous silica nanoparticles using hydrothermal synthesis, including adding a transition metal when reacting a surfactant and a silica precursor. The mesoporous silica nanoparticles are high functional particles able to be used as an adsorbent, a sensor, a membrane, a catalyst and a catalyst support, thanks to their large surface area and nano-sized pores. The mesoporous silica nanoparticles are functionally advantageous in terms of increased material diffusion rate and reactivity, easy recycling after use as a catalyst and slow inactivation, compared to conventional mesoporous silica, and are prepared through a very simple process among methods of controlling the particle size of mesoporous silica to a nano size.
1. A method of preparing mesoporous silica nanoparticles using hydrothermal synthesis, comprising adding a transition metal salt when reacting a surfactant and a silica precursor in a mixture solution of the surfactant, water, and an acid,
wherein molar ratios of the silica precursor to the surfactant are 0.01-0.02.
2. The method as set forth in claim 1 , wherein the transition metal salt is a transition metal salt of one or more transition metals selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper and zinc.
3. The method as set forth in claim 1 . wherein the surfactant is a poly(alkyleneoxide)block copolymer.
4. The method as set forth in claim 1 , wherein the silica precursor is tetraethylorthosilicate.
5. The method as set forth in claim 1 , wherein the reacting of the surfactant and the silica precursor is performed at 30-50° C.
6. The method as set forth in claim 1 , comprising:
mixing Pluoronic P123, water and an acid, thus preparing a mixture solution;
adding a transition metal salt to the mixture solution and mixing the transition metal salt and the mixture solution, thus preparing a transition metal salt-added mixture solution;
adding tetraethylorthosilicate to the transition metal salt-added mixture solution and stirring the tetraethylorthosilicate and the transition metal salt-added mixture solution at temperatures of 30-50° C., thus preparing a tetraethylorthosilicate-added mixture solution;
aging the tetraethylorthosilicate-added mixture solution at temperatures of 110-130° C. in a steel pressurizer to obtain a resultant mesoporous silica; and
washing the mesoporous silica, drying the washed mesoporous silica at room temperature, and calcining the dried mesoporous silica at a temperature of 550° C.