Polymeric compositions
A one or two part organopolysiloxane composition capable of cure to an elastomeric body, the composition comprising a polymer having a polymer backbone selected from an organopolysiloxane backbone and a telechelic backbone, which polymer has not less than two reactable silicon-bonded groups selected from alkenyl group, condensable groups, silyl-hydride groups, 5 to 50% by weight of the composition of an extender; a suitable cure catalyst; and optionally a siloxane and/or silane cross-linker having at least two groups per molecule which are reactable with the reactable groups in (a) and/or one or more fillers. The extender is selected from an alicyclic ester having at least two ester groups, and a boiling point of at least 180° C. or a mixture thereof having a boiling point range commencing at 180° C. or above; each ester group being the same or different and comprising from 2 to 30 carbon atoms.
1. A one or two part organopolysiloxane composition capable of cure to an elastomeric body, the composition comprising:
a) a polymer having a polymer backbone selected from an organopolysiloxane backbone and a telechelic backbone, which polymer has not less than two reactable silicon-bonded groups selected from unsaturated groups, and condensable groups;
b) if required, a siloxane and/or silane cross-linker having at least two groups per molecule which are reactable with the reactable groups in (a);
c) 5 to 50% by weight of the composition of an extender;
d) a suitable cure catalyst; and optionally
e) one or more fillers;
wherein the extender is selected from an alicyclic ester having at least two ester groups, and a boiling point of at least 180° C. or a mixture thereof having a boiling point range commencing at 180° C. or above; each ester group being the same or different and comprising from 2 to 30 carbon atoms, and wherein the unsaturated groups are cured by a catalyst consisting of an organic peroxide.
2. A composition in accordance with claim 1 wherein the extender is a cyclohexane compound comprising from 2 to 4 ester groups.
3. A composition in accordance with claim 1 wherein the extender is selected from the group of 1,2-cyclohexane dicarboxylic acid dialkylesters, 1,3-cyclohexane dicarboxylic acid dialkylesters, 1,4-cyclohexane dicarboxylic acid dialkylesters, 1,2,3-cyclohexane tricarboxylic acid trialkylesters, 1,2,4-cyclohexane tricarboxylic acid trialkylesters and 2,3,4-cyclohexane tricarboxylic acid trialkylesters, 1,2-cyclohexane dialkylcarboxylic acid dialkylesters, 1,3-cyclohexane dialkylcarboxylic acid dialkylesters, 1,4-cyclohexane dialkylcarboxylic acid dialkylesters, 1,2,3-cyclohexane trialkylcarboxylic acid trialkylesters, 1,2,4-cyclohexane trialkylcarboxylic acid trialkylesters and 2,3,4-cyclohexane trialkylcarboxylic acid trialkylesters.
4. A composition in accordance with claim 1 wherein the extender is selected from the group of cyclohexane dicarboxylic acid di-isooctyl ester, cyclohexane dicarboxylic acid di-isononyl ester cyclohexane, dicarboxylic acid di-isodecyl ester, and cyclohexane dicarboxylic acid di-dodecyl ester.
5. A composition in accordance with claim 1 wherein the organopolysiloxane containing polymer has not less than two reactable silicon-bonded, condensable groups.
6. A composition in accordance with claim 5 wherein the cross-linking agent is selected from one or more of the following alkyltrialkoxysilanes, alkenyltrialkoxy silanes, alkenyl alkyl dialkoxysilanes, and alkenyl alkyl dialkoxysilanes.
7. A composition in accordance with claim 5 wherein the catalyst is selected from the group of a titanate, a zirconate, a chelated titanate, a chelated zirconate, or an organotin compound.
8. A composition in accordance with claim 1 wherein the organopolysiloxane containing polymer has not less than two reactable silicon-bonded, unsaturated groups selected from alkenyl groups, alkynyl groups, acrylate groups, and/or alkylacrylate groups.
9. A composition in accordance with claim 1 further comprising a filler selected from one or more of high surface area fumed and precipitated silicas, calcium carbonate, crushed quartz, diatomaceous earths, barium sulphate, iron oxide, titanium dioxide and carbon black, talc, wollastonite, pyrophyllite, aluminite, calcium sulphate (anhydrite), gypsum, calcium sulphate, magnesium carbonate, clays such as kaolin, aluminium trihydroxide, magnesium hydroxide (brucite), graphite, copper carbonate, nickel carbonate, barium carbonate, and/or strontium carbonate.
10. A composition in accordance with claim 1 further comprising one or more of the following additives: rheological modifiers; adhesion promoters, pigments, Heat stabilizers, Flame retardants, UV stabilizers, Chain extenders, electrically and/or heat conductive fillers, Fungicides and/or biocides.
11. A method of sealing a space between two units, said method comprising applying a composition according to claim 5 to the space, and causing or allowing the composition to cure.
12. A sealant composition comprising the composition in accordance with claim 1 .
13. A silicone rubber composition comprising the composition in accordance with claim 1 .
14. A glazing structure or building unit which includes a sealant derived from a composition according to claim 1 .
15. A multi-pack sealant composition according to claim 1 comprising a first pack comprising polymer (a) and filler (e) (when required) and a second pack comprising catalyst (d) and cross-linker (b) and wherein optional additives are in either or both said first and second packs.
16. A method of sealing a space between two units, said method comprising applying a composition in accordance with claim 1 and causing or allowing the composition to cure.