Growth of carbon nanotubes on carbon or metal substrates
The invention relates to the growth of carbon nanotubes on a substrate, in particular a carbon or metal substrate on which the growth of such nanotubes is usually difficult. Accordingly, the invention includes a first phase that comprises depositing a ceramic sub-layer, followed by a second phase that comprises depositing carbon nanotubes on said sub-layer in a single step and in a single and same growth reactor. The growth can advantageously be carried out by chemical vapor deposition.
1. A process for growing carbon nanotubes on a substrate, wherein there is provided:
a first phase of depositing a ceramic sub-layer on the substrate,
followed by a second phase of depositing carbon nanotubes on said ceramic sub-layer, the first phase and the second phase being performed successively in a single reactor without exposing the substrate to the outside atmosphere between the first phase and the second phase.
2. The process according to claim 1 , wherein the substrate comprises a carbon-containing surface receiving at least a part of the deposited ceramic sub-layer.
3. The process according to claim 1 , wherein the substrate comprises a metal surface receiving at least a part of the deposited ceramic sub-layer.
4. The process according claim 1 , wherein the growth of the sub-layer and the nanotubes is realized by chemical vapor deposition.
5. The process according to claim 1 , wherein the ceramic sub-layer is deposited by pyrolysis, in the reactor, of a first liquid containing a precursor of said ceramic.
6. The process according to claim 1 , wherein the carbon nanotubes are deposited by pyrolysis, in the reactor, of a second liquid containing a carbon precursor.
7. The process according to claim 6 , wherein the second liquid additionally comprises a metal precursor providing the catalyst for growing the nanotubes.
8. The process according to claim 5 , wherein said reactor is located downstream of an evaporator and said first liquid is introduced by spraying in droplet form in the evaporator.
9. The process according to claim 6 , wherein said reactor is located downstream of an evaporator and said second liquid is introduced by spraying in droplet form in the evaporator.
10. The process according to claim 8 , wherein the droplets are introduced into the evaporator by pulses of a chosen frequency.
11. The process according to claim 1 , wherein the sub-layer is deposited at a pressure in the range of 30 to 150 mbar and the carbon nanotubes are deposited at a pressure in the range of 200 to 1000 mbar.
12. The process according to claim 1 , wherein the first and second phases are conducted at temperatures between 200 and 1200° C.
13. The process according to claim 1 , wherein the length of the carbon nanotubes is proportional to the thickness of the ceramic sub-layer.
14. The multilayer structure obtained by implementing the process according to claim 1 , comprising a layer of carbon nanotubes deposited on at least one ceramic sub-layer.
15. The structure according to claim 14 , wherein the carbon nanotubes deposited on the ceramic sub-layer have a density on the order of 10 9 to 10 10 nanotubes per cm 2 .
16. A reinforcement fiber covered with a multilayer structure according to claim 13 .
17. A reinforcement fiber covered with a multilayer structure according to claim 14 .
18. An organic matrix composite material, incorporating at least one reinforcement fiber according to claim 16 .
19. A metal substrate covered with a multilayer structure according to claim 13 .
20. A metal substrate covered with a multilayer structure according to claim 14 .
21. A material for storing energy, comprising a substrate according to claim 19 .
22. The process according to claim 1 , wherein said process is implemented in a device, the device comprising said reactor and an evaporator located upstream of said reactor, said reactor receiving at least a ceramic precursor and a carbon precursor, the device further comprising a system for injecting said ceramic precursor and said carbon precursor in the form of liquid droplets into the evaporator.