Method for producing paper, paperboard and cardboard having high dry strength
Process for the production of paper, board and cardboard having high dry strength by addition of an aqueous composition comprising a nanocellulose and at least one polymer selected from the group consisting of the anionic polymers and water-soluble cationic polymers, draining of the paper stock and drying of the paper products.
1. A process for the production of paper, board, and cardboard having high dry strength, the process comprising:
(I) metering into a paper stock an aqueous composition comprising a nanocellulose comprising cellulose fibers and at least one anionic polymer and optionally a water-soluble cationic polymer;
(II) draining the paper stock, to obtain paper product; and
(III) drying the paper product;
wherein the anionic polymer comprises, as polymerized units:
(a) at least one monomer selected from the group consisting of a C 1 - to C 20 -alkyl acrylate, a C 1 - to C 20 -alkyl methacrylate, a vinyl ester of a saturated carboxylic acid comprising up to 20 carbon atoms, a vinylaromatic comprising up to 20 carbon atoms, an ethylenically unsaturated nitrile, a vinyl ester of a saturated, monohydric alcohol comprising 1 to 10 carbon atoms, a vinyl halide, and an aliphatic hydrocarbon comprising 2 to 8 carbon atoms and one or two double bonds;
(b) at least one anionic monomer selected from the group consisting of an ethylenically unsaturated C 3 - to C 8 -carboxylic acid, a vinylsulfonic acid, acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, vinylphosphonic acid, and salts thereof;
(c) optionally, at least one monomer selected from the group consisting of a C 1 - to C 10 -hydroxyalkyl acrylate, a C 1 - to C 10 -hydroxyalkyl methacrylate, acrylamide, methacrylamide, an N—C 1 - to C 20 -alkylacrylamide, and an N—C 1 - to C 20 -alkylmethacrylamide; and
(d) optionally, a monomer comprising at least two ethylenically unsaturated double bonds in the molecule.
2. The process of claim 1 , wherein the nanocellulose has a length dimension below 1000 μm and a fiber thickness in a range from 50 μm to 3 nm.
3. The process of claim 2 , wherein at least 80% of the cellulose fibers of the nanocellulose have a fiber thickness in a range from 50 μm to 3 nm.
4. The process of claim 3 , wherein at least 80% of the cellulose fibers of the nanocellulose have a fiber thickness in a range from 1 μm to 5 nm.
5. The process of claim 1 , wherein the nanocellulose has a length dimension below 1000 μm a fiber thickness in a range from 50 μm to 3 nm, and
wherein the nanocellulose further comprises from 5 ppm to 2% by weight of an ionic fluid, based on a total mass of the nanocellulose.
6. The process of claim 5 , wherein at least 80% of the cellulose fibers of the nanocellulose have a fiber thickness of from 50 μM to 3 nm and comprise from 5 ppm to 2% by weight of an ionic liquid, based on a total mass of the nanocellulose.
7. The process of claim 1 , wherein the anionic polymer comprises, as polymerized units:
(c) at least 60 mol % of at least one monomer selected from the group consisting of a C 1 - to C 20 -alkyl acrylate, a C 1 - to C 20 -alkyl methacrylate, vinyl acetate, vinyl propionate, styrene, α-methylstyrene, p-methylstyrene, α-butylstyrene, 4-n-butylstyrene, 4-n-decylstyrene, acrylonitrile, methacrylonitrile, butadiene, and isoprene; and
(d) from 0.5 to 9 mol % of an ethylenically unsaturated C 3 - to C 5 -carboxylic acid.
8. The process of claim 1 , wherein the anionic polymer comprises, as polymerized units, at least 80 mol % of a monomer of group (a).
9. The process of claim 1 , wherein the anionic polymer comprises, as monomer of group (a), a mixture comprising, as polymerized units:
(i) at least one selected from the group consisting of a C 1 - to C 20 -alkyl acrylate and a C 1 - to C 20 -alkyl methacrylate; and
(ii) at least one selected from the group consisting of styrene, α-methylstyrene, p-methylstyrene, α-butylstyrene, 4-n-butylstyrene, butadiene and isoprene,
wherein a weight ratio of (i) to (ii) is from 10:90 to 90:10, based on a total weight of the mixture.
10. The process of claim 1 , wherein a molar mass M w of the cationic polymer is in the range from 5000 to 5 million g/mol.
11. The process of claim 1 , wherein a charge density of the cationic polymer is in a range from 0.5 to 23 meq/g.
12. The process of claim 1 , wherein the water-soluble cationic polymer comprises a polymer comprising a vinylamine unit.
13. The process of claim 2 , wherein the nanocellulose has a length dimension in a range from 100 nm to 500 μm and a fiber thickness in a range from 1 μm to 5 nm.
14. The process of claim 2 , wherein the nanocellulose has a length dimension in a range from 100 nm to 100 μm and a fiber thickness in a range from 1 μm to 5 nm.
15. The process of claim 2 , wherein the nanocellulose has a length dimension in a range from 100 nm to 50 μm and a fiber thickness in a range from 1 μm to 5 nm.
16. The process of claim 2 , wherein the nanocellulose has a length dimension in a range from 100 nm to 10 μm and a fiber thickness in a range from 1 μm to 5 nm.
17. An aqueous composition, comprising:
a nanocellulose comprising cellulose fibers, wherein at least 80% of the cellulose fibers have a fiber thickness of from 50 μm to 3 nm, and from 5 ppm to 2% by weight of an ionic liquid, based on a total mass of the nanocellulose;
at least one anionic polymer; and
optionally, a water-soluble cationic polymer;
wherein the anionic polymer comprises, as polymerized units:
(a) at least one monomer selected from the group consisting of a C 1 - to C 20 -alkyl acrylate, a C 1 - to C 20 -alkyl methacrylate, a vinyl ester of a saturated carboxylic acid comprising up to 20 carbon atoms, a vinylaromatic comprising up to 20 carbon atoms, an ethylenically unsaturated nitrile, a vinyl ester of a saturated, monohydric alcohol comprising 1 to 10 carbon atoms, a vinyl halide, and an aliphatic hydrocarbon comprising 2 to 8 carbon atoms and one or two double bonds;
(b) at least one anionic monomer selected from the group consisting of an ethylenically unsaturated C 3 - to C 8 -carboxylic acid, a vinylsulfonic acid, acrylamido-2-methylpropanesulfonic acid, styrenesulfonic acid, vinylphosphonic acid, and salts thereof;
(c) optionally, at least one monomer selected from the group consisting of a C 1 - to C 10 -hydroxyalkyl acrylate, a C 1 - to C 10 -hydroxyalkyl methacrylate, acrylamide, methacrylamide, an N—C 1 - to C 20 -alkylacrylamide, and an N—C 1 - to C 20 -alkylmethacrylamide; and
(d) optionally, a monomer comprising at least two ethylenically unsaturated double bonds in the molecule.