Excellent heat-dissipating black resin composition, method for treating a zinc coated steel sheet using the same and steel sheet treated thereby

1. A heat-dissipating black resin composition, comprising, based on 100 parts by weight of the heat-dissipating black resin composition:

10 to 60 parts by weight of a resin composition in which at least one main resin and a melamine-based curing agent are mixed in a weight ratio of 10:2-7, the main resin being selected from the group consisting of polyester resin, epoxy resin, polyolefin resin, polyurethane resin, fluorine resin, phenol resin, acryl resin and polycarbonate resin;

1 to 10 parts by weight of at least one pigment selected from the group consisting of carbon black and carbon nano tube;

1 to 10 parts by weight of a matting agent including silica and titania at a weight ratio of 9:1;

0.1 to 2 parts by weight of at least one selected from the group consisting of 3-aminopropyltriethoxy silane, 3-glycidoxypropyltrimethoxy silane, 3-methaglyoxypropyltrimethoxy silane, 3-mercaptopropyltrimethoxy silane, N-(beta-aminoethyl)-gamma-aminopropyltrimethoxysilane, gamma-glycidoxypropyltriethoxysilane and gamma-glycidoxytrimethyldimethoxysilane;

0.1 to 2 parts by weight of a phosphate-based additive; and

a solvent.

2. The heat-dissipating black resin composition of claim 1 , wherein the main resin has a molecular weight of 2,000 to 20,000.

3. The heat-dissipating black resin composition of claim 1 , wherein the melamine-based curing agent is at least one selected from the group consisting of melamine, butoxymethyl melamine, hexamethoxymethyl melamine and trimethoxymethyl melamine.

4. The heat-dissipating black resin composition of claim 1 , wherein the mixing ratio of the main resin and the melamine-based curing agent is in a range of 10:3-5.

5. The heat-dissipating black resin composition of claim 1 , wherein the pigment has an average particle size of 10 to 30 nanometers.

6. The heat-dissipating black resin composition of claim 1 , wherein the matting agent has an average particle size of 10 micrometers or less.

7. The heat-dissipating black resin composition of claim 1 , further comprising at least one selected from the group consisting of a crosslinking promoter, wax, a curing catalyst, a pigment antiagglomerant, and an antifoaming agent.

8. The heat-dissipating black resin composition of claim 7 , wherein the crosslinking promoter is a zirconium compound and/or a titanium compound.

9. The heat-dissipating black resin composition of claim 8 , wherein the titanium compound is at least one selected from the group consisting of isopropyl ditriethanolamino titanate, titanium lactate chelate and titanium acetylacetonate.

10. The heat-dissipating black resin composition of claim 8 , wherein the zirconium compound is at least one selected from the group consisting of zirconium lactate, zirconium acetylacetonate and zirconium triethanolaminate.

11. The heat-dissipating black resin composition of claim 7 , wherein the wax is at least one selected from the group consisting of polyolefin wax, ester wax and polyethylene wax.

12. The heat-dissipating black resin composition of claim 7 , wherein the curing catalyst is dodecylbenzenesulfonic acid, para-toluene sulfonic acid or their mixture.

13. The heat-dissipating black resin composition of claim 7 , wherein the antifoaming agent is N-methylethanolamine.

14. The heat-dissipating black resin composition of claim 7 , wherein the phosphate-based additive is at least one selected from the group consisting of zinc phosphate and magnesium phosphate.

15. A steel sheet comprising a base steel sheet; and a heat-dissipating black resin layer formed of a dry coating film and having a thickness of 3 to 30 micrometers, the dry coating film being prepared by coating one or both surfaces of the base steel sheet with the heat-dissipating black resin composition as defined in claim 1 .

16. The steel sheet of claim 15 , wherein the base steel sheet is selected from the group consisting of a galvanizing steel (GI steel), a galvannealed steel (GA steel), an electrogalvanized steel (EG steel) and a rust-proof steel.