Molecular sieve adsorbent blends and uses thereof
A process for the production and use of a molecular sieve blend with improved performance characteristics produced by preparing or obtaining a hydrophilic zeolite, particularly a hydrophilic zeolite 3A with a low SiO 2 :Al 2 O 3 ratio, preparing or obtaining a hydrophobic silica binder, particularly a hydrophobic colloidal silica, mixing the zeolite with the silica binder to form a mixture, and forming the mixture into the molecular sieve blend.
1. A process for dehydration of a gaseous or a liquid hydrocarbon feed stream containing water comprising
passing the components of the hydrocarbon feed stream over or through a molecular sieve blend produced by a process comprising preparing or obtaining a hydrophilic zeolite;
preparing or obtaining a hydrophobic silica binder comprising a colloidal silica;
mixing the hydrophilic zeolite with the hydrophobic silica binder and calcining at about 600° C. to produce a mixture; and
forming the molecular sieve blend from the mixture into a shaped body selected from beads, pellets, tablets and extrudates.
2. The process of claim 1 , wherein the hydrophilic zeolite comprises a zeolite 3 A.
3. The process of claim 1 , wherein the hydrophilic zeolite has a SiO 2 /Al 2 O 3 ratio of less than 50.
4. The process of claim 2 , wherein the hydrophilic zeolite has a SiO 2 /Al 2 O 3 ratio of less than 5.
5. The process of claim 1 wherein the hydrophobic silica binder comprises from about 5% to 30%, by weight, of the molecular sieve blend.
6. The process of claim 1 wherein the hydrophobic silica binder comprises from about 5% to 20%, by weight, of the molecular sieve blend.
7. The process of claim 1 wherein the hydrophobic silica binder comprises from about 5% to 10%, by weight, of the molecular sieve blend.
8. The process of claim 1 , wherein the hydrophilic zeolite is ion exchanged with potassium ions to at least about 25 percent.
9. The process of claim 1 , wherein the hydrophilic zeolite is ion exchanged with potassium ions to at least about 40 percent.
10. The process of claim 1 , wherein the hydrophobic silica binder exhibits a water adsorption capacity after 7.5 hours of less than 5.5 wt.%.
11. The process of claim 1 , wherein the hydrophobic silica binder exhibits a water adsorption rate per minute after 60 minutes of less than 0.05 wt.%.
12. The process of claim 1 , wherein the hydrophilic zeolite exhibits a water adsorption capacity after 7.5 hours greater than 5.5%.
13. The process of claim 1 , wherein the hydrophilic zeolite exhibits a water adsorption rate per minute after 60 minutes greater than 0.05 wt.%.
14. The process of claim 1 , wherein the adsorbent blend has a mass transfer value of at least 0.20, as measured by the uptake of water in the presence of ethanol.
15. The process of claim 1 , wherein the adsorbent blend exhibits a coking rate of less than 5.0×10 −9 mmol/g/min when the adsorbent blend is exposed to a nitrogen gas stream at 450° C. containing 4% by volume of 1,3-butadiene at a flow rate of 60 m/min.
16. The process of claim 1 wherein the selectivity of the mixture of the hydrophilic zeolite with the hydrophobic silica binder is greater than 10° C.
17. The process of claim 1 further comprising adding from about 0.25 to about 10 percent, by weight, of a pore forming agent to the mixture prior to forming the adsorbent blend.
18. A process for removal of water from a gaseous or liquid ethanol stream containing water comprising
passing the ethanol stream over or through a molecular sieve blend produced by a process comprising
preparing or obtaining a hydrophilic zeolite 3 A;
preparing or obtaining a hydrophobic silica binder comprising a colloidal silica;
mixing the zeolite 3 A with the hydrophobic silica binder and calcining at about 600° C. to produce a mixture; and
forming the molecular sieve blend from the mixture into a shaped body selected from beads, pellets, tablets and extrudates.
19. A process to separate n-paraffins from a mixture of iso-paraffins and n-paraffins comprising
passing the mixture over or through a molecular sieve blend produced by a process comprising
preparing or obtaining a hydrophilic zeolite 3 A;
preparing or obtaining an hydrophobic silica binder comprising a colloidal silica;
mixing the zeolite with the hydrophobic binder and calcining at about 600° C. to produce a mixture; and
forming the molecular sieve blend from the mixture into a shaped body selected from beads, pellets, tablets and extrudates.
20. A process for the drying of a cracked, hydrocarbon gas stream comprising
passing the cracked hydrocarbon gas stream over or through a molecular sieve blend produced by a process comprising
preparing or obtaining a hydrophilic zeolite product;
preparing or obtaining a hydrophobic silica binder comprising a colloidal silica;
mixing the zeolite with the silica binder and calcining at about 600° C. to produce a mixture; and
forming the molecular sieve water blend from the mixture into a shaped body selected from beads, pellets, tablets and extrudates.