Polyolefin and composition for pipe systems and sheets
A polyolefin composition for pipes comprising (percent by weight): A) from 1% to 9.5%; of a copolymer of propylene and hexene-1 wherein said copolymer comprises from 0.1 to 5% of recurring units derived from hexene-1; B) from 80.5% to 99% of a heterophasic polypropylene composition comprising: B1) from 50% to 85% of a propylene homopolymer, said propylene polymer being insoluble in xylene at ambient temperature in an amount over 85% having a polydispersity Index ranging from 3 to 10; and a Melt Index from 0.5 to 10 dg/min; B2) from 5% to 50% of a copolymer of ethylene and propylene having an ethylene derived units content ranging from 30% to 70%; said polymeric composition having a Melt Index from 0.05 to 10 dg/min.
1. A polyolefin composition comprising (percent by weight):
A) from 1.0% to 9.5%; of a copolymer of propylene and 1-hexene wherein said copolymer comprises from 0.1 to 5% of recurring units derived from 1-hexene; and
B) from 80.5% to 99% of a heterophasic polypropylene composition comprising:
B1) from 50% to 85% of a propylene homopolymer, said propylene polymer being insoluble in xylene at ambient temperature in an amount over 85% having a polydispersity Index ranging from 3 to 10; and a Melt Index from 0.5 to 10 dg/min; and
B2) from 5% to 50% of a copolymer of ethylene and propylene having an ethylene derived units content ranging from 30% to 70%;
said polymeric composition having a Melt Index from 0.05 to 10 dg/min.
2. The polyolefin composition according to claim 1 having a Flexural Modulus higher than 1500 MPa.
3. The polyolefin composition according to claim 1 comprising (percent by weight):
A) 2% to 8%, of the copolymer of propylene and 1-hexene; and
B) from 82% to 98%, of the heterophasic polypropylene.
4. The polyolefin composition according to claim 1 wherein the propylenen/hexane-1 component A contains from 0.3 to 3% recurring units derived from hexene-1.
5. The polyolefin composition according to claim 1 wherein the heterophasic propylene composition component B comprises:
B1) from 60% to 82% of the propylene homopolymer described in claim 1 ; and
B2) from 8% to 40% of a copolymer of ethylene and propylene having an ethylene derived units content ranging from 40% to 60%.
6. Pipe systems and sheets comprising a polyolefin composition according to claim 1 .
7. Mono- or multilayer pipes and sheets wherein at least one layer comprises the polyolefin composition according to claim 1 .