Flame-protected impact-modified polycarbonate compositions
The present invention relates to flame-protected impact-modified polycarbonate compositions, wherein the compositions are free of rubber-free polyalkyl (alkyl)acrylate. The present invention further relates to the use of the polycarbonate compositions in the production of molded bodies, and to the molded bodies themselves.
1. A composition comprising
A) from 77 to 90 parts by weight (based on the sum of components A+B+C) of linear and/or branched aromatic polycarbonate and/or aromatic polyester carbonate,
B) from 6 to 12 parts by weight (based on the sum of components A+B+C) of graft polymer having
B.1 from 5 to 30 wt. % (in each case based on the graft polymer B) of a shell of at least one vinyl monomer and
B.2 from 95 to 70 wt. % (in each case based on the graft polymer B) of one or more graft bases of silicone-acrylate composite rubber,
C) from 4 to 10 parts by weight (based on the sum of components A+B+C) of phosphorus compounds according to formula (VIII)
wherein
R 1 , R 2 , R 3 and R 4 , independently of one another, represent optionally halo-substituted C 1 -C 8 -alkyl, in each case optionally halo- and/or alkyl-substituted C 5 -C 6 -cycloalkyl, C 6 -C 10 -aryl or C 7 -C 12 -aralkyl,
the substituents n independently of one another represent 0 or 1,
the substituents q independently of one another represent 0, 1, 2, 3 or 4,
N represents from 0.1 to 10,
R 5 and R 6 , independently of one another, represent C 1 -C 4 -alkyl, or halogen, and
Y represents a single bond, C 1 -C 7 -alkylidene, C 1 -C 7 -alkylene, C 5 -C 12 -cyclo-alkylene, C 5 -C 12 -cycloalkylidene, —O—, —S—, —SO—, —SO 2 — or —CO—,
D) from 0 to 3 parts by weight (based on the sum of components A+B+C) of at least one anti-dripping agent, and
E) from 0 to 3 parts by weight (based on the sum of components A+B+C) of thermoplastic vinyl (co)polymer (E.1) and/or polyalkylene terephthalate (E.2); and
F) from 0 to 20 parts by weight (based on the sum of components A+B+C) of at least one further additive,
wherein the weight ratio of component B to the phosphorus content from component C is in a range of from 16 to 22 to 1, and
wherein the composition is free of rubber-free polyalkyl (alkyl)acrylate wherein the composition has
a fire behavior UL94V of V0 and a transition temperature tough/brittle notched impact test of no greater than −15° C.
2. A composition according to claim 1 comprising from 8.5 to 10 parts by weight (based on the sum of components A+B+C) of component B.
3. A composition according to claim 1 , wherein the monomers B.1 are at least one selected from the group consisting of methyl methacrylate, ethyl methacrylate, 2-ethylhexyl methacrylate, allyl methacrylate, methyl acrylate, ethyl acrylate, n-butyl acrylate and tert-butyl acrylate.
4. A composition according to claim 1 comprising from 5.2 to 6.5 parts by weight (based on the sum of components A+B+C) of component C.
5. A composition according to claim 1 comprising as component C a mixture of a monophosphate and an oligophosphate according to formula (VIII), wherein the average value of N is from 0.1 to 10.
6. A composition according to claim 1 , wherein N is from 1.06 to 1.15.
7. A composition according to claim 1 comprising from 0.1 to 0.6 parts by weight (based on the sum of components A+B+C) of component D.
8. A composition according to claim 1 , wherein the composition is free of thermoplastic vinyl (co)polymers (E.1) and/or polyalkylene terephthalates (E.2).
9. A composition according to claim 1 comprising from 0.1 to 10 parts by weight (based on the sum of components A+B+C) of component F.
10. A composition according to claim 1 comprising as component F at least one additive selected from the group consisting of lubricants and demoulding agents, nucleating agents, antistatics, stabilisers, colourings, pigments, fillers, reinforcing agents and very finely divided inorganic compounds, wherein the very finely divided inorganic compounds have an average particle diameter of less than or equal to 200 nm.
11. A composition according to claim 1 , wherein the weight ratio of component B to the phosphorus content from component C is in a range of from 17 to 19 to 1.
12. An injection-moulded or thermoformed moulded body formed from a composition according to claim 1 .
13. Moulded body comprising a composition according to claim 1 .
14. Moulded body according to claim 13 , wherein the moulded body is part of a motor vehicle, bus, lorry, motor caravan, track vehicle, water craft or other vehicle or is a cover plate for the construction sector, flat wall element, partition wall, strip for protecting walls and edges, profile for electrical installation conduits, cable guide, conductor rail cover, window and door profile, furniture part or part of a traffic sign.
15. Moulded body according to claim 13 , wherein the moulded body is a side wall, cladding or a cover for an airbag or a ventilator, a side part, a handle or part of a headrest or a storage area of a motor vehicle, bus, lorry or motor caravan.
16. A composition comprising
A) from 77 to 90 parts by weight (based on the sum of components A+B+C) of linear polycarbonate,
B) from 6 to 12 parts by weight (based on the sum of components A+B+C) of graft polymer having
B.1 from 5 to 30 wt. % (in each case based on the graft polymer B) of a shell of at least one vinyl monomer and
B.2 from 95 to 70 wt. % (in each case based on the graft polymer B) of one or more graft bases of silicone-acrylate composite rubber,
C) from 4 to 10 parts by weight (based on the sum of components A+B+C) of phosphorus compounds according to formula (VIII)
wherein
R 1 , R 2 , R 3 and R 4 , independently of one another, represent optionally halo-substituted C 1 -C 8 -alkyl, in each case optionally halo- and/or alkyl-substituted C 5 -C 6 -cycloalkyl, C 6 -C 10 -aryl or C 7 -C 12 -aralkyl,
the substituents n independently of one another represent 0 or 1,
the substituents q independently of one another represent 0, 1, 2, 3 or 4,
N represents from 0.1 to 10,
R 5 and R 6 , independently of one another, represent C 1 -C 4 -alkyl, or halogen, and
Y represents a single bond, C 1 -C 7 -alkylidene, C 1 -C 7 -alkylene, C 5 -C 12 -cyclo-alkylene, C 5 -C 12 -cycloalkylidene, —O—, —S—, —SO—, —SO 2 — or —CO—,
D) from 0 to 3 parts by weight (based on the sum of components A+B+C) of anti-dripping agents, and
E) from 0 to 3 parts by weight (based on the sum of components A+B+C) of thermoplastic vinyl (co)polymer (E.1) and/or polyalkylene terephthalate (E.2); and
F) from 0 to 20 parts by weight (based on the sum of components A+B+C) of at least one further additive,
wherein the weight ratio of component B to the phosphorus content from component C is in a range of from 16 to 22 to 1, and
wherein the composition is free of rubber-free polyalkyl (alkyl)acrylate wherein the composition has
a fire behavior UL94V of V0 and a transition temperature tough/brittle notched impact test of no greater than −15° C.
17. A composition according to claim 16 , wherein present the composition is free of thermoplastic vinyl (co)polymers (E.1) and polyalkylene terephthalates (E.2).
18. A composition consisting of
A) from 77 to 90 parts by weight (based on the sum of components A+B+C) of linear and/or branched aromatic polycarbonate and/or aromatic polyester carbonate,
B) from 6 to 12 parts by weight (based on the sum of components A+B+C) of graft polymer having
B.1 from 5 to 30 wt. % (in each case based on the graft polymer B) of a shell of at least one vinyl monomer and
B.2 from 95 to 70 wt. % (in each case based on the graft polymer B) of one or more graft bases of silicone-acrylate composite rubber,
C) from 4 to 10 parts by weight (based on the sum of components A+B+C) of phosphorus compounds according to formula (VIII)
wherein
R 1 , R 2 , R 3 and R 4 , independently of one another, represent optionally halo-substituted C 1 -C 8 -alkyl, in each case optionally halo- and/or alkyl-substituted C 5 -C 6 -cycloalkyl, C 6 -C 10 -aryl or C 7 -C 12 -aralkyl,
the substituents n independently of one another represent 0 or 1,
the substituents q independently of one another represent 0, 1, 2, 3 or 4,
N represents from 0.1 to 10,
R 5 and R 6 , independently of one another, represent C 1 -C 4 -alkyl, or halogen, and
Y represents a single bond, C 1 -C 7 -alkylidene, C 1 -C 7 -alkylene, C 5 -C 12 -cyclo-alkylene, C 5 -C 12 -cycloalkylidene, —O—, —S—, —SO—, —SO 2 — or —CO—,
D) from 0 to 3 parts by weight (based on the sum of components A+B+C) of anti-dripping agents, and
E) from 0 to 3 parts by weight (based on the sum of components A+B+C) of thermoplastic vinyl (co)polymer (E.1) and/or polyalkylene terephthalate (E.2); and
F) from 0 to 20 parts by weight (based on the sum of components A+B+C) of at least one further additive,
wherein the weight ratio of component B to the phosphorus content from component C is in a range of from 16 to 22 to 1, and
wherein the composition is free of rubber-free polyalkyl (alkyl)acrylate wherein the composition has
a fire behavior UL94V of V0 and a transition temperature tough/brittle notched impact test of no greater than −15° C.
19. A composition consisting of
A) from 77 to 90 parts by weight (based on the sum of components A+B+C) of linear polycarbonate,
B) from 6 to 12 parts by weight (based on the sum of components A+B+C) of graft polymer having
B.1 from 5 to 30 wt. % (in each case based on the graft polymer B) of a shell of at least one vinyl monomer and
B.2 from 95 to 70 wt. % (in each case based on the graft polymer B) of one or more graft bases of silicone-acrylate composite rubber,
C) from 4 to 10 parts by weight (based on the sum of components A+B+C) of phosphorus compounds according to formula (VIII)
wherein
R 1 , R 2 , R 3 and R 4 , independently of one another, represent optionally halo-substituted C 1 -C 8 -alkyl, in each case optionally halo- and/or alkyl-substituted C 5 -C 6 -cycloalkyl, C 6 -C 10 -aryl or C 7 -C 12 -aralkyl,
the substituents n independently of one another represent 0 or 1,
the substituents q independently of one another represent 0, 1, 2, 3 or 4,
N represents from 0.1 to 10,
R 5 and R 6 , independently of one another, represent C 1 -C 4 -alkyl, or halogen, and
Y represents a single bond, C 1 -C 7 -alkylidene, C 1 -C 7 -alkylene, C 5 -C 12 -cyclo-alkylene, C 5 -C 12 -cycloalkylidene, —O—, —S—, —SO—, —SO 2 — or —CO—,
D) from 0 to 3 parts by weight (based on the sum of components A+B+C) of anti-dripping agents, and
F) from 0 to 20 parts by weight (based on the sum of components A+B+C) of at least one further additive,
wherein the weight ratio of component B to the phosphorus content from component C is in a range of from 16 to 22 to 1,
wherein the composition is free of rubber-free polyalkyl (alkyl)acrylate, and
wherein the composition is free of thermoplastic vinyl (co)polymers (E.1) and polyalkylene terephthalates (E.2) wherein the composition has
a fire behavior UL94V of V0 and a transition temperature tough/brittle notched impact test of no greater than −15° C.