Coated article and method for making the same
A coated article is described. The coated article includes a substrate, a magnesium oxide-alumina compound layer formed on the substrate, and an anti-fingerprint layer formed on the magnesium oxide-alumina compound layer. The anti-fingerprint layer is a layer of magnesium-aluminum-oxygen-fluorine having the chemical formula of MgAlO x F y , wherein 0<x<2.5, 0<y<5. A method for making the coated article is also described.
1. A coated article, comprising:
a substrate;
a magnesium oxide-alumina compound layer formed on the substrate; and
an anti-fingerprint layer directly formed on and contacting the magnesium oxide-alumina compound layer, the anti-fingerprint layer being a magnesium-aluminum-oxygen-fluorine layer, the magnesium-aluminum-oxygen-fluorine having a chemical formula of MgAlO x F y , with 0<x<2.5, 0<y<5.
2. The coated article as claimed in claim 1 , wherein the magnesium oxide-alumina compound layer has a non-crystalline structure.
3. The coated article as claimed in claim 1 , wherein the magnesium oxide-alumina compound layer has a thickness of about 500 nm-600 nm.
4. The coated article as claimed in claim 1 , wherein the anti-fingerprint layer has a non-crystalline structure.
5. The coated article as claimed in claim 4 , wherein the anti-fingerprint layer has a nano-dimensioned rough surface.
6. The coated article as claimed in claim 4 , wherein the anti-fingerprint layer has a thickness of about 200 nm-400 nm.
7. The coated article as claimed in claim 1 , wherein the anti-fingerprint layer is formed by magnetron sputtering or fluoridating the magnesium oxide-alumina compound layer.
8. The coated article as claimed in claim 1 , wherein the substrate is made of metal material selected from a group consisting of stainless steel, aluminum, aluminum alloy, copper, copper alloy, and zinc; or the substrate is made of ceramic or glass.
9. The coated article as claimed in claim 1 , wherein the anti-fingerprint layer has a contact angle of about 102.5°-117.8° with water-oil droplets.
10. The coated article as claimed in claim 1 , further comprising a magnesium-aluminum alloy transition layer formed between the substrate and the magnesium oxide-alumina compound layer.