Diffusively light reflective paint composition, method for making paint composition, and diffusively light reflective articles

1. A diffusively light reflective paint composition comprising a paint carrier, hollow and solid microspheres, and between about 1% by weight and about 90% by weight macroporous polymeric particles having an average diameter between about 1 micron and about 300 microns, wherein the macroporous polymeric particles are selected from the group consisting of flash spun plexifilamentary film-fibril materials, microcellular foamed polyester sheets, biaxially-stretched polyester films, and combinations thereof.

2. The paint composition of claim 1 having a light reflectance of between about 95% to about 98% measured at 550 nm when said composition is dried on a rigid surface.

3. The paint composition of claim 1 , wherein the microspheres are plastic, ceramic, or glass.

4. The paint composition of claim 3 having a light reflectance of between about 95% to about 98% measured at 550 nm when said composition is dried on a rigid surface.

5. The paint composition of claim 1 comprising between about 0.5% and about 10% by weight hollow and solid microspheres.

6. The paint composition of claim 1 wherein the volumetric ratio of hollow to solid microspheres is between about 1:4 to about 3:4.

7. The paint composition of claim 1 comprising between about 5% and about 80% by weight macroporous polymeric particles.

8. The paint composition of claim 7 comprising between about 5% and about 20% by weight macroporous polymeric particles.

9. The paint composition of claim 1 , wherein the macroporous polymeric particles have an average diameter between about 3 microns and about 200 microns.

10. The paint composition of claim 9 , wherein the macroporous polymeric particles have an average diameter between about 100 microns and about 200 microns.

11. The paint composition of claim 1 further comprising a pigment.

12. The paint composition of claim 11 , wherein the pigment comprises between about 0.5% by weight and about 50% by weight TiO 2 particles.

13. The paint composition of claim 1 further comprising an additive selected from the group consisting of wetting agents, dispersants, antistatic agents, UV inhibitors, optical brighteners, wax lubricants, antioxidants, antimicrobial agents and mixtures thereof.

14. The paint composition of claim 1 wherein the paint carrier further comprises a binder selected from the group consisting of acrylic binders, polyurethane binders, polyester binders and epoxy-based binders, and mixtures thereof.

15. The paint composition of claim 1 , wherein the paint carrier further comprises an epoxy/acrylate hybrid binder.

16. The paint composition of claim 1 , wherein the film-fibril material comprises high density polyethylene.

17. The paint composition of claim 1 , wherein the microcellular foamed polyester sheet comprises polyethylene terephthalate.

18. A diffusively light reflective article comprising a substrate having at least one light reflective surface having a layer thereon of the diffusively light reflective paint composition of claim 1 .

19. The article of claim 18 wherein the layer of paint has a thickness between about 0.025 mm and about 1 mm.

20. The article of claim 18 wherein the article is a luminaire and the substrate comprises a rigid housing.

21. The article of claim 18 wherein the at least one light reflective surface has a light reflectance of at least about 97% measured at 550 nm.

22. The article of claim 18 , wherein the diffusively light reflective paint composition further comprises an epoxy/acrylate hybrid binder.

23. The article of claim 18 , wherein the microspheres are present from about 0.5% to about 10% by weight, based on the paint composition.

24. The article of claim 18 , wherein the volumetric ratio of hollow to solid microspheres is between about 1:4 to about 3:4.

25. A diffusively light reflective paint composition comprising a paint carrier, hollow and solid microspheres, and between about 1% by weight and about 90% by weight, based on the paint composition, of macroporous polymeric particles having an average diameter between about 1 micron and about 300 microns and having micropores, microvoids, or fibril fractures between 0.3 and 0.7 microns in diameter, wherein the macroporous polymeric particles are selected from the group consisting of flash spun plexifilamentary film-fibril materials, microcellular foamed polyester sheets, biaxially-stretched polyester films, and combinations thereof.

26. The paint composition of claim 25 , wherein the microspheres are plastic, ceramic, or glass.