Chemical solution seed layer for rabits tapes
A method for making a superconducting article includes the steps of providing a biaxially textured substrate. A seed layer is then deposited. The seed layer includes a double perovskite of the formula A 2 B′B″O 6 , where A is rare earth or alkaline earth metal and B′ and B″ are different rare earth or transition metal cations. A superconductor layer is grown epitaxially such that the superconductor layer is supported by the seed layer.
1. A method of making a superconducting article, comprising the steps of:
providing a biaxially textured metal or alloy substrate;
epitaxially depositing directly on the substrate by a chemical solution process a biaxially textured seed layer comprising a double perovskite on the substrate, the seed layer comprising a double perovskite of the formula A2B′B″O6, where A is rare earth or alkaline earth metal and B′ and B″ are different rare earth or transition metal cations; and
epitaxially depositing directly on the seed layer a biaxially textured superconductor layer such that the superconductor layer is supported by the seed layer.
2. The method of claim 1 , wherein the chemical solution process is selected from MOD, sol-gel alkoxide, TFA-MOD, non-fluorine processes, and reduced fluorine processes.
3. The method of claim 1 , wherein A is selected from the group consisting of Ba, Ca, or Sr.
4. The method of claim 1 , wherein B′ is selected from the group consisting of Y and/or RE.
5. The method of claim 1 , wherein B″ is Nb or Ta.
6. The method of claim 1 , wherein the seed layer is Ba 2 (Y and/or RE)NbO 6 or Ba 2 (Y and/or RE)TaO 6 .
7. The method of claim 1 wherein at least a portion of said substrate comprises at least one of the group consisting of Ni—W, Ni—Cr, Ni—Cr—W, Ni—Cr—V, Ni—V, Cu—Ni, Cu—Pd, and Ni—Mn.
8. The method of claim 1 wherein said superconducting layer is REBCO.
9. A method of making a superconducting article, comprising the steps of:
providing a biaxially textured metal or alloy substrate;
epitaxially depositing directly on the substrate by a chemical solution process a biaxially textured seed layer comprising a double perovskite on the substrate, the seed layer comprising a double perovskite of the formula A2B′B″O6, where A is rare earth or alkaline earth metal and B′ and B″ are different rare earth or transition metal cations; and
epitaxially depositing a biaxially textured superconductor layer such that the superconductor layer is supported by the seed layer; and;
epitaxially depositing a biaxially textured buffer layer between said double perovskite seed layer and the superconductor layer that is different from the material comprising the double perovskite seed layer.
10. The method of claim 9 , wherein the superconductor layer comprises YBCO.