Use of monazite or xenotime solution precursors to increase the density and shear strength of oxide composites
Aqueous precursor solutions are described that comprise at least one monazite-based material precursor, at least one xenotime-based material precursor or a combination thereof; and a plurality of fine suspended particles of an oxide material. Contemplated oxide composites, as described herein, comprise a plurality of fibers surrounded by at least one monazite or xenotime-based material, wherein the oxide composite has nearly a fully dense matrix. Contemplated embodiments disclosed herein provides a method for producing an oxide composite with nearly fully dense matrix and with all fibers surrounded by a monazite- or xenotime-based material that prevents embrittlement at temperatures at least as high as 1200° C. Oxide composites are described that contain a plurality of fibers, a matrix containing at least one or more oxide materials, and at least one monazite-based material, xenotime-based material or combination thereof, wherein the monazite-based or xenotime-based material is formed from the aqueous precursor solutions disclosed herein. Contemplated methods of production include: a) providing a composite comprising oxide-reinforcing fibers and a porous matrix of oxide materials, and b) infiltrating the porosity in the matrix with a solution that contains precursors for at least one monazite-based material, at least one xenotime-based material or a combination thereof; and c) heat treating the composite to convert the precursors to monazite, xenotime, or combinations thereof.
1. A method of forming an oxide composite comprising:
providing a composite comprising oxide-reinforcing fibers and a porous matrix of oxide materials,
applying as coatings on the fibers precursors for at least one monazite-based material, at least one xenotime-based material or a combination thereof,
infiltrating the porosity in the matrix with a solution that contains the precursors,
filling void space in the matrix with the precursors, and
heat treating the composite to convert the precursors and fill void space with monazite, xenotime, or combinations thereof.
2. The method of claim 1 , wherein the monazite-based material comprises LaPO 4 .
3. The method of claim 1 , wherein the solution comprises ions, complexes or combinations thereof.
4. The method of claim 3 , wherein the ions, complexes or combinations thereof combine to form rare earth phosphates in solution.
5. The method of claim 4 , wherein the rare earth phosphates are formed by evaporation, decomposition, fluid exchange or a combination thereof.
6. The method of claim 5 , wherein the rare earth phosphates are further formed by heat treatment.
7. The method of claim 1 , further comprising providing a plurality of suspended particles in the solution.
8. The method of claim 7 , wherein at least part of the plurality of suspended particles comprise aluminum oxide.
9. The method of claim 6 , wherein the steps of infiltrating and forming by heat treatment are repeated until a desired matrix density is reached.
10. The method of claim 1 , wherein the precursors are aqueous.
11. The method of claim 10 , wherein the precursors for at least one monazite-based material include rare earth nitrates and a source of phosphorous.
12. The method of claim 11 , wherein the source of phosphorous includes phosphorous acid, phytic acid, methylphosphonic acid or combinations thereof.
13. The method of claim 11 , further comprising
detecting for excess rare earth nitrates or phosphorous by heat-treating a sample of the precursors to form solid rare earth phosphate powder,
mixing the powder with sapphire to form sapphire pieces, and
heat-treating the mixture at a temperature of at least 1400° C. in air.
14. The method of claim 13 , further comprising
scanning the sapphire pieces with electron microscopy for evidence of reaction with excess RE or P.
15. The method of claim 1 wherein said coatings comprise monazite, a xenotime, or a combination therefore.
16. The method of claim 1 comprising the step of filling voids in the composite with monazite, at xenotime, or a combination therefore.
17. A method of forming an oxide composite comprising:
providing a composite comprising oxide-reinforcing fibers and a porous matrix of oxide materials,
infiltrating the porosity in the matrix with a solution that contains aqueous precursors for at least one monazite-based material, at least one xenotime-based material or a combination thereof,
applying the precursors as coatings on the fibers,
filling void space in the matrix with the precursors,
heat treating the composite to convert the precursors and fill void space with monazite, xenotime, or combinations thereof,
wherein the precursors for at least one monazite-based material include rare earth nitrates and a source of phosphorous, and
detecting for excess rare earth nitrates or phosphorous by heat-treating a sample of the precursors to form solid rare earth phosphate powder by
mixing the powder with sapphire to form sapphire pieces,
heat-treating the mixture at a temperature of at least 1400° C. in air, and
scanning the sapphire pieces with electron microscopy for evidence of reaction with excess RE or P.