Zirconia sintered bodies with high total light transmission and high strength, uses of the same, and process for producing the same
The invention relates to the use of a sintered body obtained by subjecting a primary sintered body having a relative density of 95% or higher produced from a fine yttria-containing zirconia powder to HIP sintering at a temperature of 1,200-1,600° C. and a pressure of 50 MPa or higher. This sintered body is either a sintered body which has a total light transmittance, as measured at a thickness of 0.5 mm, of 43% or higher and a three-point bending strength of 1,700 MPa or higher or a zirconia sintered body which has a total light transmittance, as measured at a thickness of 1 mm, of 40% or higher and a three-point bending strength of 500 MPa or higher and which combines high strength and total light transmission.
1. A zirconia sintered body which comprises zirconia containing 2-4 mol % yttria and has a three-point bending strength of 1,700 MPa or higher and a total light transmittance, as measured at a thickness of 0.5 mm, of 43% or higher.
2. The zirconia sintered body according to claim 1 , which has a three-point bending strength of 1,900 MPa or higher and a total light transmittance, as measured at a thickness of 0.5 mm, of 45% or higher.
3. The zirconia sintered body according to claim 1 , characterized by being made of crystal phases which are constituted only of a fluorite structure tetragonal crystal phase (I) containing 3 mol % or less yttria or constituted of a mixed phase comprising a fluorite structure tetragonal crystal phase (I) containing 3 mol % or less yttria and a fluorite structure tetragonal crystal phase (II) containing 5 mol % or more yttria, the proportion of the fluorite structure tetragonal crystal phase (I) being 50-100%.
4. The zirconia sintered body according to claim 1 , characterized by containing no voids of 10 μm or larger and having a porosity of 0.5% or lower.
5. A dental material comprising the zirconia sintered body according to claim 1 .
6. An orthodontic bracket comprising the zirconia sintered body according to claim 1 .
7. An artificial tooth comprising the zirconia sintered body according to claim 1 .
8. A mill blank for dental materials which comprised the zirconia sintered body according to claim 1 .