Methods for forming high-K crystalline films and related devices
This disclosure provides a method of fabricating a semiconductor stack and associated device, such as a capacitor or DRAM cell. In such a device, a high-K zirconia-based layer may be used as the primary dielectric together with a relatively inexpensive metal electrode based on titanium nitride. To prevent corruption of the electrode during device formation, a thin barrier layer can be used seal the electrode prior to the use of a high temperature process and a (high-concentration or dosage) ozone reagent (i.e., to create a high-K zirconia-based layer). In some embodiments, the barrier layer can also be zirconia-based, for example, a thin layer of doped or un-doped amorphous zirconia. Fabrication of a device in this manner facilitates formation of a device with dielectric constant of greater than 40 based on zirconia and titanium nitride, and generally helps produce less costly, increasingly dense DRAM cells and other semiconductor structures.
1. A method of fabricating a semiconductor layer assembly, the method comprising:
depositing a first metal oxide layer above an electrode,
the first metal oxide layer comprises zirconium oxide and having a first crystalline form,
wherein the first metal oxide layer is deposited using a first oxygen reagent at or below 220 degrees centigrade; and
depositing a second metal oxide layer using a second oxygen reagent on the first metal oxide layer,
the second metal oxide layer comprises zirconium oxide and having a second crystalline form different from the first crystalline form,
wherein the second oxygen reagent is more reactive than the first oxygen reagent.
2. The method of claim 1 , wherein the depositing of the second metal oxide layer occurs at a temperature above 220 degrees centigrade.
3. The method of claim 1 , wherein the first metal oxide layer has a median thickness of between 0.5 nanometers and 2.0 nanometers.
4. The method of claim 1 , wherein the electrode consists of a metal nitride.
5. The method of claim 4 , wherein the metal nitride is titanium nitride.
6. The method of claim 1 , wherein the first metal oxide layer further comprises one of aluminum, germanium, yttrium, or magnesium.
7. The method of claim 1 , wherein each of the depositing the first metal oxide layer and the depositing the second metal oxide layer is performed using atomic layer deposition.
8. The method of claim 1 , wherein the oxygen reagent comprises ozone.
9. The method of claim 8 , wherein the first oxygen reagent comprises ozone, and wherein a concentration of the ozone in the first oxygen reagent is less than a concentration of the ozone in the second oxygen reagent as the reagent.
10. The method of claim 1 , wherein the second metal oxide layer is deposited at or above 260 degrees centigrade.
11. The method of claim 1 , wherein the first crystalline form is amorphous and wherein the second crystalline form is one of cubic or tetragonal.
12. The method of claim 1 , wherein the first metal oxide layer is deposited using a first metal precursor, and wherein the second metal oxide layer is deposited using a second metal precursor different from the first metal precursor.
13. The method of claim 12 , wherein the first metal precursor comprises an alkylamido-based precursor and wherein the second metal oxide layer comprises alkylamido cyclopendadienyl.
14. The method of claim 12 , wherein the first metal precursor decomposes at a lower temperature than the second metal precursor.
15. The method of claim 1 , wherein the first metal oxide layer consists substantially of zirconium oxide.
16. The method of claim 1 , wherein substantially no oxygen is introduced into the electrode during depositing the first metal oxide layer above the electrode.
17. The method of claim 1 , wherein the first metal oxide layer directly interfaces the electrode.
18. The method of claim 1 , wherein the second metal oxide layer is at least four times thicker than the first metal oxide layer.
19. The method of claim 1 , wherein the second oxygen reagent comprises water.
20. The method of claim 1 , wherein the first metal oxide layer comprises a first dopant having a first concentration, and wherein the second metal oxide layer comprises a second dopant having a second concentration lower than the first concentration.