Coating systems for metal substrates and a method for protective metal substrates using the coating systems
Disclosed are methods of treating a metal to improve the metal's corrosion resistance. In one such method, the method is carried out by applying, to the surface of the metal, a coating which includes magnesium powder and a UV-curable or other radiation-curable binder. In another such method, the method is carried out by applying, to the surface of the metal, a coating which includes magnesium powder and an inorganic binder. In another such method, a coating that includes a magnesium alloy powder and a binder is applied to the surface of the metal. The magnesium alloy powder is selected such that it has a corrosion potential that is from about 0.01 volt to about 1.5 volt more negative than the metal's corrosion potential. Also disclosed are methods of treating a ferrous metals and magnesium alloys to improve the corrosion resistance of these materials.
1. A method of treating a metal to improve the metal's corrosion resistance, said method comprising:
applying, to the surface of the metal, a coating which consists essentially of magnesium powder and an inorganic binder,
wherein the inorganic binder comprises a tetraalkyl orthosilicate; or
wherein the inorganic binder comprises one or more trialkoxy monoalkyl silanes and one or more tetraalkyl orthosilicates; or
wherein the inorganic binder comprises two or more trialkoxy monoalkyl silanes and one or more tetraalkyl orthosilicates and wherein at least one of the trialkoxy monoalkyl silanes is an amine-containing trialkoxy monoalkyl silane; or
wherein the inorganic binder comprises two or more trialkoxy monoalkyl silanes and one or more tetraalkyl orthosilicates and wherein at least one of the trialkoxy monoalkyl silanes is an acrylate-containing or methacrylate-containing trialkoxy monoalkyl silane; or
wherein the inorganic binder comprises two or more trialkoxy monoalkyl silanes and one or more tetraalkyl orthosilicates and wherein at least one of the trialkoxy monoalkyl silanes is an amine-containing trialkoxy monoalkyl silane and wherein another of the trialkoxy monoalkyl silanes is an acrylate-containing or methacrylate-containing trialkoxy monoalkyl silane.
2. A method according to claim 1 , wherein the metal is aluminum or an aluminum alloy.
3. A method according to claim 2 , wherein the metal is an aluminum alloy.
4. A method according to claim 3 , wherein the aluminum alloy is a copper-containing aluminum alloy.
5. A method according to claim 3 , wherein the aluminum alloy is selected from Al 2024, Al 7075, Al 5052, and Al 6061.
6. A method according to claim 1 , wherein the trialkoxy monoalkyl silanes and the tetraalkyl orthosilicates are present in a volume ratio of from about 1:10 to about 10:1.
7. A method according to claim 1 , wherein the trialkoxy monoalkyl silanes and the tetraalkyl orthosilicates are present in a volume ratio of from about 1:1 to about 10:1.
8. A method according to claim 1 , wherein the magnesium powder is a powder of a magnesium alloy comprising (i) magnesium and (ii) calcium, manganese, lithium, carbon, zinc, potassium, aluminum, silicon, zirconium, and/or a rare earth metal.
9. A method according to claim 1 , wherein the magnesium powder is a magnesium alloy powder having a corrosion potential that is from about 0.01 volt to about 1.5 volt more negative than the metal's corrosion potential.