Additive for skim coat mortar and skim coat mortar composition containing the same
Provided are an additive for skim coat mortar and a skim coat mortar composition including the same, and the additive is a blend of cellulose ether having hydroxyalkylalkyl cellulose cross-linked with an aldehyde compound and hydroxyalkyl cellulose cross-linked with an aldehyde compound. By applying the additive to a skim coat mortar composition, it is possible to improve workability, surface luster, and a creamy property while maintaining a water retention property.
1. A skim coat mortar composition, comprising:
(i) a cement-based raw material;
(ii) a cellulose ether additive, comprising a blend of cellulose ether having hydroxyalkylalkyl cellulose cross-linked with an aldehyde compound and hydroxyalkyl cellulose cross-linked with an aldehyde compound; and
(iii) water.
2. The skim coat mortar composition of claim 1 , wherein the skim coat mortar composition includes 0.1 to 2 parts by weight of the cellulose ether additive and 30 to 50 parts by weight of the water with respect to 100 parts by weigh of the cement-based raw material.
3. The skim coat mortar composition of claim 1 , wherein the hydroxyalkylalkyl cellulose cross-linked with the aldehyde compound has 20 to 26% degree of alkyl group substitution and 5% or more degree of hydroxyalkyl group substitution, and the hydroxyalkyl cellulose cross-linked with an aldehyde compound has 30.0 to 65.0% degree of hydroxyalkyl group substitution.
4. The skim coat mortar composition of claim 1 , wherein the hydroxyalkylalkyl cellulose is hydroxypropylmethyl cellulose or hydroxyethylmethyl cellulose, and the hydroxyalkyl cellulose is hydroxyethyl cellulose.
5. The skim coat mortar composition of claim 1 , wherein a blending ratio of the hydroxyalkylalkyl cellulose and the hydroxyalkyl cellulose by weight is 90:10 to 99:1.
6. The skim coat mortar composition of claim 1 , wherein the aldehyde compound that cross-links the cellulose ether includes one or more kinds selected from the group consisting of formaldehyde, acetaldehyde, glyoxal, methylglyoxal, and phenylglyoxal.
7. The skim coat mortar composition of claim 1 , wherein the aldehyde compound that cross-links the cellulose ether is used in a range of 0.1 to 2.5 wt % with respect to the total weight of the cellulose ether.
8. The skim coat mortar composition of claim 1 , wherein the cellulose ether, on the basis of a 2% solution, exhibits viscosity in a range of 1,000 to 200,000 cps as measured by a Brookfield viscometer under conditions of 20° C. and 20 rpm.