Method for hot isostatic pressing a substrate
Disclosed is a method for hot isostatic pressing a substrate. At first, a metal container is provided. Powder is filled in the metal container before the metal container is located in an oven. The metal container is subjected to isostatic pressing that includes heating and pressing. Thus, the metal container shrinks and presses on the powder evenly and turns the powder into a nugget. The metal container is moved out of the oven and broken to release the nugget. A substrate is cut from the nugget. With the hot isostatic pressing, the substrate exhibits only a few flaws and is large, fine, homogenous and strong so that the substrate is not vulnerable to deformation in a high-pressure environment.
1. A method for hot isostatic pressing a substrate including the steps of:
providing a metal container in the form of a barrel, a feeding pipe connected to the metal container, a cover closing the feeding pipe and with a plurality of vents defined therein, and a check valve arranged between the feeding pipe and the cover;
filling powder in the metal container;
providing an oven containing, heating, and hot isostatic pressing the metal container filled with the powder so as to heat and deform the metal container evenly to press the powder evenly into a nugget and such that excess gasses from the metal container are vented from the container and external gases are blocked from entering the container during the hot isostatic pressing;
removing the metal container from the oven;
breaking the metal container;
removing the nugget from the metal container; and
slicing the nugget into a plurality of substrates.
2. The method for hot isostatic pressing a substrate in accordance with claim 1 , wherein the check valve includes:
a membrane movably provided on the feeding pipe; and
a spring compressed between the cover and the membrane.
3. The method for hot isostatic pressing a substrate in accordance with claim 1 , wherein the powder is made of aluminum nitride so that the nugget is made of aluminum nitride and that the substrates are made of aluminum nitride substrate.
4. The method for hot isostatic pressing a substrate in accordance with claim 1 , wherein the temperature is 1000° C. to 3000° C. and the pressure is 6894800 Pa to 275792000 Pa in the oven for hot isostatic pressing the metal container.
5. The method for hot isostatic pressing a substrate in accordance with claim 1 , further including the step of introducing an inert gas, as a medium for exerting even pressure on and evenly deforming the metal container so as to evenly press the powder, into the oven during the hot isostatic pressing.
6. The method for hot isostatic pressing a substrate in accordance with claim 5 , wherein the inert gas is selected from the group consisting of Ar (g) and N 2(g) .