Stent with a coating or a basic body containing a lithium salt and use of lithium salts for prevention of restenosis
The invention relates to a stent with in particular a coated basic body made of an implant material the use of lithium salts as a coating material or a component of an implant material for stents and the use of lithium salts in a method for restenosis prevention. The inventive stent having a basic body made of an implant material is characterized in that (i) the basic body has a coating which comprises or consists of a lithium salt, and/or (ii) the implant material is biocorrodible and the basic body contains a lithium salt.
1. A cardiovascular stent having a basic body of an implant material, characterized in that
the basic body is coated with a coating consisting of a lithium salt for localized delivery of lithium ions, wherein the lithium salt is selected from the group consisting of lithium carbonate, lithium bicarbonate, lithium hydroxide, lithium nitride and a lithium salt of a carboxylic acid compound.
2. The stent according to claim 1 , wherein the implant material comprises a biocorrodible material and a lithium salt.
3. The stent according to claim 1 , wherein the lithium salt is basic.
4. The stent according to claim 1 , wherein the implant material is a biocorrodible magnesium alloy.
5. The stent according to claim 1 , wherein the localized delivery provides a localized lithium ion concentration of 5 to 30 mmol/liter.
6. The stent according to claim 1 , wherein the basic body comprises more than 1 wt % and less than or equal to 15 wt % of lithium ions.
7. The stent according to claim 1 , wherein lithium content is from 5 to 200 μg per mm stent length.
8. The stent according to claim 1 , wherein entire surface of the basic body of the stent is covered by the coating.
9. The stent according to claim 1 , wherein the stent is configured to deliver the lithium salt in an amount sufficient to stop a cell cycle in the S-phase at a stented lesion.
10. A cardiovascular stent, the stent having a basic body formed from a biocorrodible magnesium alloy and coated with a coating consisting essentially of a lithium salt dispersed in a polymeric carrier matrix, wherein the lithium salt is selected from the group consisting of lithium carbonate, lithium bicarbonate, lithium hydroxide, lithium nitride and a lithium salt of a carboxylic acid compound, further wherein the basic body comprises more than 1 wt % and less than or equal to 15 wt % of lithium ions.
11. The stent according to claim 10 , wherein the coating comprises at least 10% lithium salt.
12. The stent according to claim 11 , wherein the coating comprises at least 30% lithium salt.
13. The stent according to claim 10 , wherein the body comprises 15 wt % lithium ions.
14. The stent according to claim 10 , wherein the lithium salt is the lithium carboxylate, optionally selected from the group consisting of lithium formate, lithium acetate, lithium lactate, lithium glycinate and lithium bis(oxalto)borate.