Method for producing glass substrate for information storage medium, and information storage medium
For an information storage medium a glass substrate is produced in a method including the steps of: polishing a glass substrate with a polishing agent applied thereon; and subsequently, chemically strengthening a major surface of the glass substrate. The polishing agent contains cerium oxide at a purity equal to or larger than 99% by mass for CeO 2 /TREO, and has an alkaline earth metal content having a total mass equal to or smaller than 10 ppm by mass. The step of polishing is performed with a soft polishing pad to polish the glass substrate.
1. A method for producing a glass substrate for an information storage medium including a glass substrate and a magnetic recording layer on a major surface of said glass substrate, comprising:
polishing said major surface of said glass substrate with a polishing agent applied thereon, wherein said glass substrate is aluminosilicate glass wherein said glass substrate comprises a composition including 0.02-1% by mass of Ce and said polishing comprises coarse polishing and subsequent finishing polishing; and
chemically strengthening said major surface of said glass substrate, wherein said chemically strengthening occurring subsequent to said coarse polishing;
during said coarse polishing, said polishing agent comprising cerium oxide at a purity equal to or larger than 99% by mass for CeO 2 /TREO and comprising an alkaline earth metal content having a total mass equal to or smaller than 10 ppm by mass, wherein TREO regards a total amount of rare earth oxide element/elements,
said coarse polishing being performed with a soft polishing pad to polish said glass substrate.
2. The method for producing a glass substrate for an information storage medium according to claim 1 , wherein said polishing agent in said coarse polishing comprises cerium oxide at a purity equal to or larger than 99.99% by mass for CeO 2 /TREO, and comprises an alkaline earth metal content having a total mass equal to or smaller than 5 ppm by mass.
3. The method for producing a glass substrate for an information storage medium according to claim 1 , wherein said polishing agent in said coarse polishing comprises a solid content with cerium oxide contained therein at a ratio equal to or larger than 90% by mass relative to said solid content.
4. The method for producing a glass substrate for an information storage medium according to claim 1 , wherein said polishing agent in said coarse polishing has a particle diameter having a maximum value equal to or smaller than 3.5 μm, and a mean particle diameter (a D50 value) of 0.4-1.6 μm.
5. The method for producing a glass substrate for an information storage medium according to claim 1 , wherein:
a polishing slurry comprising a moisture content and comprising said polishing agent in said coarse polishing dispersed in said moisture content is employed; and
said polishing slurry comprises 3-15% by mass of cerium oxide.
6. The method for producing a glass substrate for an information storage medium according to claim 1 , wherein:
said soft polishing pad comprises a base and a nap layer; and
said nap layer has a thickness of 430-620 μm.
7. The method for producing a glass substrate for an information storage medium according to claim 1 , comprising after said polishing cleaning said glass substrate so that a total amount of alkaline earth metal that remains on an entire surface, including said major surface, of said glass substrate and a circumferential surface of said glass substrate is equal to or smaller than 10 ng/cm 2 .