Catalyst ink preparation for fuel cell electrode fabrication
Methods of fabricating gas diffusion electrodes and gas diffusion electrodes made from such methods are disclosed herein. One method of fabricating a gas diffusion electrode for a fuel cell comprises preparing a catalyst ink of a predetermined viscosity. Preparing the catalyst ink comprises mixing a catalyst solution comprising catalyst particles, an ionomer and a solvent at a first speed for a first period of time and homogenizing the catalyst solution at a second speed in a temperature controlled environment for a second period of time, wherein the second period of time is longer than the first period of time, the second period of time and the second speed selected to preserve a structure of the catalyst particles during homogenization. An active electrode layer is formed by spraying the catalyst ink directly on a gas diffusion layer in a single application and a uniform loading.
1. A method of fabricating a gas diffusion electrode for a fuel cell comprising:
preparing a catalyst ink of a predetermined viscosity comprising:
mixing a catalyst solution comprising catalyst particles, an ionomer and a solvent at a mixing speed for a first period of time; and
homogenizing the catalyst solution at a homogenizing speed in a temperature controlled environment for a second period of time, wherein the second period of time is longer than the first period of time, the second period of time being greater than ten times as long as the first period of time and the homogenizing speed being greater than ten times the mixing speed; and
forming an active electrode layer by spraying the catalyst ink directly on a gas diffusion layer in a single application and a uniform loading.
2. The method of claim 1 , further comprising:
drying the sprayed gas diffusion layer in an oven for a third period of time.
3. The method of claim 2 , wherein drying is performed between 75° C. and 85° C. and the third period of time is between twenty and thirty minutes.
4. The method of claim 1 , wherein the second period of time is about three hours.
5. The method of claim 1 , wherein the homogenizing speed is about 10,000 RPM.
6. The method of claim 1 , wherein the catalyst particles include carbon and the catalyst solution has a ratio of ionomer to carbon of about 0.9/1.0 by weight.
7. The method of claim 1 , wherein the catalyst particles include carbon and the solvent comprises water, with the catalyst solution having a ratio of water to carbon in a range of 25/1 to 30/1 by weight.
8. The method of claim 1 , wherein the catalyst particles include carbon and the solvent comprises isopropanol, with the catalyst solution having a ratio of isopropanol to carbon in a range of 12/1 to 13/1 by weight.
9. The method of claim 1 , wherein the catalyst particles comprise platinum particles supported on carbon particles.
10. The method of claim 1 , wherein the ionomer is a perfluorosulfonic acid.
11. The method of claim 1 , wherein the solvent is deionized water and isopropanol.
12. The method of claim 1 , wherein the temperature controlled environment is a water bath.
13. The method of claim 1 , wherein the catalyst particles comprise platinum, the ionomer is a perfluorosulfonic acid and the solvent is deionized water and propanol.
14. The method of claim 13 , wherein the uniform loading is about 0.35 mg platinum/cm 2 with a uniform thickness.
15. A method of fabricating a gas diffusion electrode for a fuel cell comprising:
preparing a catalyst ink of a predetermined viscosity comprising:
wetting a catalyst solution comprising a catalyst, an ionomer and a solvent, wherein the catalyst comprises at least one noble metal supported on carbon, the ionomer is perfluorosulfonic acid and the solvent is deionized water and isopropanol; and
homogenizing the catalyst solution at a homogenizing speed in a temperature controlled environment for a predetermined period of time that is greater than 2 hours; and
spraying the catalyst ink directly on a gas diffusion layer in a single application and with a uniform loading.
16. The method of claim 15 , wherein the predetermined period of time is about three hours.
17. The method of claim 15 , wherein the homogenizing speed is about 10,000 RPM.
18. The method of claim 15 , wherein wetting comprises mixing the catalyst solution at a mixing speed lower than the homogenizing speed, the homogenizing speed being greater than 10 times the mixing speed.