High-strength brass alloy for sliding member, and sliding member
High-strength brass alloy having superior wear maintains single-structure β phase and Fe-Cr-Si-based intermetallic compounds dispersed in the β phase. A high-strength brass alloy for sliding member comprises, Zn from 17% to 28%, Al from 3% to 10%, Fe from 1% to 4%, Cr from 0.1% to 4%, Si from 0.5% to 3%, mass ratio, and the remnant including Cu and inevitable impurities. The high-strength brass alloy has structure in which the matrix shows single-phase structure of β phase and Fe-Cr-Si-based intermetallic compounds are dispersed in the β phase. The high-strength brass alloy for sliding member has the structure in which the matrix shows single-structure of β phase and hard Fe-Cr-Si-based intermetallic compounds are dispersed in the β phase. Thus the hardness is increased and wear resistance is improved.
1. A sliding member, comprising:
a cylindrical body made of a high-strength brass alloy;
a plurality of holes or grooves formed at least in an inner periphery as a sliding surface of the cylindrical body; and
solid lubricant filled and fixed in the holes or grooves, wherein:
the high-strength brass alloy consists only of, in terms of mass ratios, Zn in a range of from 17% or more to 28% or less, Al in a range of from 3% or more to 10% or less, Fe in a range of from 1% or more to 4% or less, Cr in a range of from 0.1% or more to 4% or less, Si in a range of from 0.5% or more to 3% or less, a remnant including Cu, and inevitable impurities; and
a matrix shows single-phase structure of β phase, while in the structure Fe-Cr-Si-based intermetallic compounds are dispersed in the β phase.
2. A sliding member, comprising:
a plate body made of a high-strength brass alloy;
a plurality of holes, grooves or recesses formed in a surface as a sliding surface of the plate body; and
solid lubricant filled and fixed in the holes, grooves or recesses, wherein:
the high-strength brass alloy consists only of, in terms of mass ratios, Zn in a range of from 17% or more to 28% or less, Al in a range of from 3% or more to 10% or less, Fe in a range of from 1% or more to 4% or less, Cr in a range of from 0.1% or more to 4% or less, Si in a range of from 0.5% or more to 3% or less, a remnant including Cu, and inevitable impurities; and
a matrix shows single-phase structure of β phase, while in the structure Fe-Cr-Si-based intermetallic compounds are dispersed in the β phase.
3. The sliding member of claim 1 , wherein: an area of the solid lubricant is in a range of from 10% or more to 40% or less of an area of the inner periphery as the sliding surface.
4. The sliding member of claim 2 , wherein: an area of the solid lubricant is in a range of from 10% or more to 40% or less of an area of the surface as the sliding surface.