Superabsorbent polymer containing clay particulate, and method of making same
A process for the preparation of superabsorbent polymer containing clay, the process including the steps of (I) polymerizing a polymerization mixture comprising: (a) one or more ethylenically unsaturated carboxyl-containing monomers, (b) one or more crosslinking agents, (c) optionally one or more comonomers copolymerizable with the carboxyl-containing monomer, (d) neutralizing agent to partially neutralize the polymer to from about 50% to about 99%, by weight, and (e) a polymerization medium, to form a crosslinked partially neutralized hydrogel, (II) admixing a clay with the crosslinked partially neutralized hydrogel to form partially neutralized superabsorbent polymer-clay hydrogel; (III) drying the crosslinked partially neutralized hydrogel at a temperature from about 190° C. to about 210° C. and for a time period of from about 15 minutes to about 120 minutes, and (IV) comminuting the dried partially neutralized superabsorbent polymer-clay hydrogel to particles.
1. A superabsorbent polymer containing hydrous kaolin particulate comprising:
a) a superabsorbent polymer particulate comprising an intimately admixed blend of from about 95 wt % to about 99.5 wt % of a neutralized superabsorbent polymer hydrogel and from about 5 wt % to about 10 wt % of a hydrous kaolin; wherein the admixed blend is dried and comminuted into superabsorbent polymer particulate wherein the superabsorbent polymer hydrogel is neutralized to from about 50 mol % to about 80 mol %;
b) wherein the superabsorbent polymer particulate of a) is surface treated with from about 0.001 wt % to about 5 wt % of a surface crosslinking agent to form a surface crosslinked superabsorbent polymer particulate; and
c) wherein the surface crosslinked particulate composition of b) is surface treated with from about 0.01 wt % to about 5 wt % of a multivalent salt to form the superabsorbent polymer containing hydrous kaolin particulate;
wherein the superabsorbent polymer containing hydrous kaolin particulate has a Centrifuge Retention Capacity of from about 25 g/g to about 40 g/g as measured by the Centrifuge Retention Capacity Test, and wherein, after surface crosslinking, the superabsorbent polymer particulate is dried at a temperature of 195° C. for 18 minutes such that the superabsorbent polymer particulate exhibits a Centrifuge Retention Capacity about 3 g/g greater than if the superabsorbent polymer particulate had been dried at 185° C. for 18 minutes.
2. The superabsorbent polymer containing hydrous kaolin particulate of claim 1 wherein at least about 40% by weight of the superabsorbent polymer particulate have a particle size from about 300 μm to about 600 μm as measured by screening through a U.S. standard 30 mesh screen and retained on a U.S. standard 50 mesh screen and wherein the hydrous kaolin is nonswelling.
3. The superabsorbent polymer containing hydrous kaolin particulate of claim 1 further comprising e) from about 0.01 wt % to about 0.5 wt % of a thermoplastic polymer wherein the thermoplastic polymer is added with the surface crosslinking agent of step b).
4. The superabsorbent polymer containing hydrous kaolin particulate of claim 1 having a vortex time of from about 30 seconds to about 50 seconds as measured by the Vortex Time Test.
5. The superabsorbent polymer containing hydrous kaolin particulate of claim 1 having an absorption under load at 0.9 psi of from about 10 g/g to about 20 g/g as measured by the Absorbency Under Load (AUL0.9 psi) Test.
6. The superabsorbent polymer containing hydrous kaolin particulate of claim 1 having a free swell gel bed permeability of from about 10 Darcy to about 100 Darcy as measured by the Free Swell Gel Bed Permeability Test.
7. An absorbent composition comprising the superabsorbent polymer containing hydrous kaolin particulate of claim 1 .
8. A sanitary article comprising the superabsorbent polymer containing hydrous kaolin particulate of claim 7 .
9. A diaper comprising the superabsorbent polymer containing hydrous kaolin particulate of claim 1 .
10. A diaper having a core, said core comprising at least 10% by weight of the superabsorbent polymer containing hydrous kaolin particulate of claim 1 .
11. The diaper of claim 10 wherein the core comprises 20-80% by weight of the superabsorbent polymer containing hydrous kaolin particulate.
12. The diaper of claim 10 further comprising a topsheet in contact with a first surface of the core, and a backsheet in contact with a second surface of the core, said second core surface opposite from said first core surface.
13. The diaper of claim 12 further comprising an acquisition layer disposed between the topsheet and the core.
14. The superabsorbent polymer containing hydrous kaolin particulate of claim 1 wherein said superabsorbent polymer containing hydrous kaolin particulate has a water content of up to about 10% by weight.