Polyvinylidene chloride coating, process for producing a coating and use thereof
A coating 8 made of polyvinylidene chloride contains particles 12 made of HDPE. Other particles can also be embedded in the coating, such as polymers from the group LDPE, LLDPE, PP, PVDC, PVC, polyamides, polyurethanes, polyacrylates, polystyrenes, acrylonitrile-butadiene styrene polymerizates (ABS), PTFE, hard waxes, synthetic resins, as well as mixtures and copolymerizates thereof. The coating 8 is applied to a film 9 of a composite which features a carrier film 11 , to which the film 9 is laminated by means of an adhesion promoter 10 (FIG. 2 ).
1. A coating on plastic films, paper sheets, or metal foils, said coating comprising polyvinylidene chloride which further contains particles, wherein (i) a number of particles protrudes out of the coating and forms spacers and the density of the particles is in the range of 0.1 to 2.0 g/cm 3 , (ii) the largest particle diameter is equal to/larger than the thickness of the coating, and (iii) the particles consist of HDPE, in an amount ranging from 0.2 to 2% by weight of dry coating mass.
2. A coating, as claimed in claim 1 , wherein said coating is applied to a multiple layer composite made of PVC-PE composite films and one metal foil.
3. A coating as claimed in claim 1 , wherein said coating is applied to a PVDC film of multilayer composites consisting of PVDC film, adhesion promoter, carrier film; PVDC film, adhesion promoter, polyethylene film, adhesion promoter, carrier film; PVDC film, adhesion promoter, cycloolefin copolymer, adhesion promoter, PVC; or PVDC film, adhesion promoter, PE, adhesion promoter, PVC.
4. Coating according to claim 1 , wherein the particles have a dry portion of from 0.1 to 10 wt % of the PVDC dry weight.
5. Coating according to claim 1 , wherein the particles have a dry portion of from 0.3 to 8 wt % of the PVDC dry weight.
6. Coating according to claim 1 , wherein the particles feature a dry portion of 0.2 to 2 wt % of the PVDC dry weight.
7. Coating according to claim 1 , wherein the particles in powder form are added to the PVDC.
8. Coating according to claim 1 , wherein said coating is liquid and consists of a mixture of an anionic PVDC dispersion and an anionic dispersion made of micronized particles.
9. Coating according to claim 1 , wherein the largest particle diameter is larger than the thickness of the coating.
10. A coating on a PVDC layer, said coating comprising a polyvinylidene chloride which further contains particles consisting of (i) polymers or (ii) particles having, a surface coating consisting of polymers, wherein a number of particles protrudes out of the coating and forms spacers,
said coating is directly disposed on said PVDC layer,
and the polymer consists of HDPE, polyurethanes, acrylonitrile butadiene styrene polymerizates, polytetrafluoroethylene, had waxes, as well as mixtures and copolymerizates thereof.
11. Coating according to claim 10 , wherein the particles are particles having a surface coating consisting of HDPE, polyurethanes, acrylonitrile butadiene styrene polymerizates, polytetrafluoroethylene, had waxes, as well as mixtures and copolymerizates thereof.
12. A coating as claimed in claim 10 , wherein the particles are polymer consisting of HDPE, polyurethanes, acrylonitrile butadiene-styrene polymerizates, polytetrafluoroethylene, hard waxes or mixtures thereof.
13. A coating on a PVDC layer, said coating comprising a polyvinylidene chloride which further contains (i) particles consisting of polymers or (ii) particles having a surface coating consisting of polymers, wherein a number of particles protrudes out of the coating and forms spacers,
said coating is directly disposed on said PVDC layer,
the particles are HDPE and the mean diameter of said particles is in the range from 6 μm to 13 μm.
14. A coating directly contacting a PVDC layer, said coating consisting of polyvinylidene chloride which farther contains particles consisting of HDPE, a number of particles protruding out of the coating and forming spacers,
wherein said coating includes an anionic dispersion and the anionic dispersion consists of micronized particles, one or several emulsifying agents, anionic tensides, pigment dispersers and dispersion additives.
15. A coating directly contacting a PVDC layer, said coating consisting of polyvinylidene chloride, particles, and optionally (i) one or several emulsifying agents, (ii) pigment dispersers or (in) other dispersion-promoting additives,
wherein a number of particles protrudes out of the coating and forms spacers and the particles consist of HDPE, LDPE, LLDPE, PTFE, polypropylene, polyurethanes, acrylonitrile butadiene styrene polymerizates, hard waxes, as well as mixtures and copolymerizates thereof.
16. A composite film consisting of a carrier film, an adhesion promoter, PVDC film and a coating made of PVDC, wherein the PVDC coating comprises particles consisting of polymers, hard waxes, or mixtures thereof,
the mean particle diameter is in the range from 1 μm to 100 μm; a number of particles protrude out of the coating and form spacers and the largest particle diameter is equal to or larger than the thickness of the PVDC coating,
and the particles made of polymer consist of HDPE, polyurethanes, acrylonitrile butadiene styrene polymerizates, polytetrafluoroethylene, hard waxes, as well as mixtures and copolymerizates thereof.