Modulus, lithium free glass
An R-glass composition including SiO 2 in an amount from 59.0 to 64.5% by weight, Al 2 O 3 in an amount from 14.5 to 20.5% by weight, CaO in an amount from 11.0 to 16.0% by weight, MgO in an amount from 5.5 to 11.5% by weight, Na2O in N an amount from 0.0 to 4.0% by weight, TiO 2 in an amount from 0.0 to 2.0% by weight, Fe 2 O 3 in an amount from 0.0 to 1.0% by weight, B 2 O 3 in an amount from 0.0 to about 3.0% by weight, K 2 O, Fe 2 O 3 , ZrO 2 , and Fluorine, each of which is present in an amount from 0.0 to about 1.0% by weight, and SrO and ZnO, each of which is present in an amount from 0.0 to about 2.0% by weight. In exemplary embodiments, the glass composition does not contain lithium or boron.
1. A composition for preparing R-glass fibers comprising:
SiO 2 in an amount from 60.0 to 64.5% by weight of the total composition;
Al 2 O 3 in an amount from 14.5 to 20.5% by weight of the total composition;
CaO in an amount from 11.0 to 13.2% by weight of the total composition;
MgO in an amount from 9.4 to 10.9% by weight of the total composition;
Na 2 O in an amount from 0.0 to 4.0% by weight of the total composition; and
TiO 2 in an amount from 0.0 to 2.0% by weight of the total composition,
wherein said composition has a ΔT of at least 60° C., a log 3 temperature from about 1285° C. to about 1320° C., and is substantially free of Li 2 O.
2. The composition of claim 1 , further comprising B 2 O 3 in an amount from 0.0 to about 1.0% by weight of the total composition.
3. The composition of claim 2 , further comprising:
K 2 O in an amount from 0.0 to about 1.0% by weight of the total composition.
4. The composition of claim 1 , wherein said composition has a ΔT up to about 135° C.
5. The composition of claim 4 , wherein said composition has a ΔT from about 75° C. to about 105° C.
6. The composition of claim 1 , wherein said composition has a log 3 temperature from about 1285° C. to about 1300° C.
7. The composition of claim 1 , wherein said composition has a liquidus temperature no greater than about 1330° C.
8. The composition of claim 1 , wherein components of said composition are melted in a refractory tank melter.
9. The composition of claim 1 , wherein said composition has a specific modulus of at least about 3.24×10 6 meters.
10. The composition of claim 9 , wherein said composition has a specific modulus from about 3.24×10 6 meters to about 3.43×10 6 meters.
11. A continuous R-glass fiber produced from a composition comprising:
SiO 2 in an amount from 59.0 to 64.5% by weight of the total composition;
Al 2 O 3 in an amount from 14.5 to 20.5% by weight of the total composition;
CaO in an amount from 11.0 to 12.96% by weight of the total composition;
MgO in an amount from 9.4 to 10.9% by weight of the total composition;
Na 2 O in an amount from 0.0 to 4.0% by weight of the total composition; and
TiO 2 in an amount from 0.0 to 2.0% by weight of the total composition,
wherein said composition has a ΔT of at least 60° C. and is substantially free of Li 2 O, and
wherein said composition has a density of between 2.606 and 2.638 g/cm3.
12. The glass fiber of claim 11 , further comprising at least one of
B 2 O 3 in an amount from 0.0 to about 1.0% by weight of the total composition;
K 2 O in an amount from 0.0 to about 1.0% by weight of the total composition.
13. A method of forming an R-glass fiber comprising:
providing a molten glass composition including:
SiO 2 in an amount from 60.0 to 64.5% by weight of the total composition;
Al 2 O 3 in an amount from 14.5 to 20.5% by weight of the total composition;
CaO in an amount from 11.0 to 13.2% by weight of the total composition;
MgO in an amount from 9.4 to 10.9% by weight of the total composition;
Na 2 O in an amount from 0.0 to 4.0% by weight of the total composition; and
TiO 2 in an amount from 0.0 to 2.0% by weight of the total composition,
wherein said composition has a ΔT of at least 60° C., a log 3 temperature from about 1285° C. to about 1320° C., and is substantially free of Li 2 O; and
drawing said molten glass composition through orifices in a bushing to form an R-glass fiber.
14. The method of claim 13 , further comprising B 2 O 3 in an amount from 0.0 to about 1.0% by weight of the total composition.
15. The method of claim 13 , wherein said composition has a ΔT up to about 135° C.
16. The method of claim 13 , wherein said composition has a specific modulus of at least 3.24×10 6 meters.
17. The method of claim 13 , wherein said composition has a log 3 temperature from about 1285° C. to about 1300° C.
18. The method of claim 13 , further comprising:
melting components of said glass composition in a refractory melter.