Method for covering particles, especially a battery electrode material particles, and particles obtained with such method and a battery comprising such particle

1. A method of providing coated particles as an electrode material for a lithium ion battery, wherein the particles have a diameter of maximally 60 μm, comprise battery electrode material and lithium, and have a covering obtained by an atomic layer deposition method, comprising:

(a) fluidizing said particles comprising the battery electrode material having lithium ions in a fluidized bed reactor using a first reactant gas comprising a first reactant for substantially covering said particles with a monolayer of said first reactant;

(b) subsequently fluidizing said particles obtained in step (a) in said fluidized bed reactor using a second reactant gas comprising a second reactant for substantially covering the monolayer on said particles obtained in step (a); and

(c) repeating step (a) and step (b) sequentially to obtain the coated particles having a coating thickness of about 2 nm or less.

2. A method according to claim 1 , wherein:

said first reactant is chosen from any of:

a hydroxide providing component,

an oxide providing reactant,

an alkyl metal providing component, and

a metal alkanolate providing component, and

said second reactant is different from said first reactant and is chosen from any of:

a hydroxide providing component,

an oxide providing reactant,

an alkyl metal pro-viding component, and

a metal alkanolate providing component.

3. A method according to claim 1 , wherein said second reactant adsorbs to and/or reacts with said first reactant.

4. A method according to claim 1 , wherein step (a) and step (b) are at least partially performed repeatedly.

5. A method according to claim 1 , wherein step (b) is performed such that the fluidization between step (a) and step (b) is uninterrupted.

6. A method according to claim 1 , wherein the method comprises the steps of:

adding a first reactant that comprises a hydroxide or oxide providing reactant for providing a hydroxide monolayer or oxide monolayer on said material;

subsequently adding a second reactant that comprises an alkyl metal or metal alkanolate, and reacting said alkyl metal or metal alkanolate with said hydroxide monolayer or oxide monolayer so as to provide a metal alkyl or metal alkanolate monolayer on said material;

adding a further reactant comprising water for removing said alkyl or alkanolate groups from and adding OH groups onto said monolayer, and finally removing H 2 O, so as to obtain a dry metal oxide monolayer on said material.

7. A method according to claim 1 , wherein the diameter of said particles is within the range of 10 nm to 60 μm.

8. A method according to claim 6 , wherein said alkyl metal compound is comprised of tri-methyl-aluminum, wherein said alkyl groups are methyl groups and wherein said metal oxide monolayer is an alumina monolayer.

9. A method according to claim 4 , wherein step (a) and step (b) are at least partially performed repeatedly with different reactants in any of said at least one repeatedly performed step.

10. A method according to claim 7 , wherein the diameter of said particles is within the range of 10 nm to 500 nm.

11. A method according to claim 10 , wherein the diameter of said particles is within the range of 10 nm to 100 nm.

12. The method according to claim 1 , wherein the particles as an electrode material are configured as cathode material.

13. The method according to claim 1 , wherein the coated particles have a coating thickness of about 2 nm.

14. A method of providing coated particles as an electrode material for a lithium ion battery, wherein the particles have a diameter of maximally 60 μm, wherein the particles are comprised of battery electrode material, wherein the particles are lithium containing particles, and wherein the particles have a covering obtained by an atomic layer deposition method, said atomic layer deposition method comprising the steps of

(a) at least partially fluidizing said particles comprising the battery electrode material having lithium ions in a fluidized bed reactor using a first reactant gas comprising a first reactant for substantially covering said particles with a monolayer of said first reactant, wherein the pressure in the fluidized bed reactor is between 0.5 and 2 bar;

(b) subsequently at least partially fluidizing said particles obtained in step (a) in said fluidized bed reactor using a second reactant gas comprising a second reactant for substantially covering the monolayer on said particles obtained in step (a); and

(c) repeating step (a) and step (b) sequentially to obtain the coated particles having a coating thickness of about 2 nm or less.

15. The method according to claim 14 , wherein the pressure in the fluidized bed reactor is between 0.9 and 1.5 bar.

16. The method according to claim 14 , wherein the pressure in the fluidized bed reactor is about atmospheric pressure.