Method of manufacturing a graphene monolayer on insulating substrates
A method of manufacturing a graphene monolayer on insulating substrates from CVD graphene synthesis, comprising: applying a thermal release adhesive tape to the bottom graphene layer deposited at the bottom of the metal foil in the CVD graphene synthesis, detaching the thermal release adhesive tape and the bottom graphene layer from the metal foil via the application of heat, from 1° C. up to 5° C. higher than the release temperature of the thermal release adhesive tape so that the thermal release adhesive tape with the bottom graphene layer can be removed, obtaining a metal foil with a top graphene layer sample, and transferring the top graphene layer onto a substrate via a sacrificial protective layer.
1. A method of manufacturing a graphene monolayer on insulating substrates from Chemical Vapor Deposition graphene synthesis, wherein a metal foil catalyst with a top graphene layer and a bottom graphene layer is obtained, comprising:
applying a thermal release adhesive tape to the bottom graphene layer deposited at the bottom of the metal foil in the Chemical Vapor Deposition graphene synthesis, by at least a roller from one edge of the thermal release adhesive tape to the opposite edge, so that it allows the sticking of the thermal release adhesive tape onto the graphene bottom layer;
detaching the thermal release adhesive tape and the bottom graphene layer from the metal foil via the application of heat, from 1° C. up to 5° C. higher than the release temperature of the thermal release adhesive tape so that the thermal release adhesive tape with the bottom graphene layer can be removed, obtaining a metal foil with a top graphene layer sample; and
transferring the top graphene layer onto a substrate via a sacrificial protective layer.
2. The Method according to claim 1 , wherein the transfer step of the top graphene layer onto a substrate, comprises:
coating the metal foil with the top graphene layer sample with a sacrificial protective layer;
etching the metal foil catalyst resulting a film consisting of the sacrificial protective layer with the top graphene layer;
depositing the top graphene layer with the sacrificial protective layer onto the desired substrate; and
removing the sacrificial protective layer via dissolution or thermal treatment.
3. The Method according to claim 1 , wherein the thermal release adhesive tape releases at 90° C.
4. The Method according to claim 1 , wherein the thermal release adhesive tape detaches at 150° C.
5. The Method according to claim 1 , wherein the thermal release adhesive tape is an adhesive polymer based on polyester selected from the group consisting of polyvinyl acetate, polyethylene vinyl acetate, polyacrylates, and polymethacrylates.
6. The Method according to claim 1 , wherein the application of the thermal release adhesive tape on the graphene bottom layer is done by a roller with controlling pressure and speed means.
7. The Method according to claim 6 , wherein the controlling pressure and speed means are pneumatic cylinders and accuracy valves.