Multilayer ceramic capacitor and method of manufacturing the same
There is provided a multilayer ceramic capacitor including: a ceramic body having first and second side surfaces opposite to each other, and third and fourth end surfaces connecting the first and second side surfaces; a plurality of internal electrodes formed in the ceramic body and having one ends thereof exposed to the third or fourth end surface; and first and second side margin parts formed from the first and second side surfaces to respective edges of the internal electrodes, the first and second side margin parts having an average thickness of 18 μm or less, wherein when a boundary surface between a cover layer and the first or second side margin part in the ceramic body is divided into two regions in a thickness direction of the ceramic body, a region adjacent to the internal electrode is S1, and a porosity of S1 is P1, 1≦P1≦20 is satisfied.
1. A multilayer ceramic capacitor comprising:
a ceramic body having first and second side surfaces opposite to each other, and third and fourth end surfaces connecting the first and second side surfaces;
a plurality of internal electrodes formed in the ceramic body and having one ends thereof exposed to the third or fourth end surface; and
first and second side margin parts formed from the first and second side surfaces to respective edges of the internal electrodes, the first and second side margin parts having an average thickness of 18 μm or less,
wherein when a boundary surface between a cover layer and the first or second side margin part in the ceramic body is divided into two regions in a thickness direction of the ceramic body, a region adjacent to the internal electrode is S1, and a porosity of S1 is P1, 1≦P1≦20 is satisfied.
2. The multilayer ceramic capacitor of claim 1 , wherein the first and second side margin parts are formed of ceramic slurry.
3. The multilayer ceramic capacitor of claim 1 , wherein the plurality of internal electrodes include:
a first internal electrode having one end exposed to the third end surface and the other end spaced apart from the fourth end surface by a predetermined interval; and
a second internal electrode having one end exposed to the fourth end surface and the other end spaced apart from the third end surface by a predetermined interval.
4. A multilayer ceramic capacitor comprising:
a ceramic body having first and second side surfaces opposite to each other, and third and fourth end surfaces connecting the first and second side surfaces;
a plurality of internal electrodes formed in the ceramic body and having one ends thereof exposed to the third or fourth end surface; and
first and second side margin parts formed from the first and second side surfaces to respective edges of the internal electrodes, the first and second side margin parts having an average thickness of 18 μm or less,
wherein when a boundary surface between a cover layer and the first or second side margin part in the ceramic body is divided into two regions in a thickness direction of the ceramic body, a region adjacent to the internal electrode is S1, a region adjacent to an upper surface or a lower surface of the ceramic body is S2, a porosity of S1 is P1, and a porosity of S2 is P2, P1/P2>2 is satisfied.
5. The multilayer ceramic capacitor of claim 4 , wherein the first and second side margin parts are formed of ceramic slurry.
6. The multilayer ceramic capacitor of claim 4 , wherein the plurality of internal electrodes include:
a first internal electrode having one end exposed to the third end surface and the other end spaced apart from the fourth end surface by a predetermined interval; and
a second internal electrode having one end exposed to the fourth end surface and the other end spaced apart from the third end surface by a predetermined interval.
7. A method of manufacturing a multilayer ceramic capacitor, the method comprising:
preparing a first ceramic green sheet including a plurality of stripe shaped first internal electrode patterns having a predetermined interval therebetween and a second ceramic green sheet including a plurality of stripe shaped second internal electrode patterns having a predetermined interval therebetween;
forming a ceramic green sheet multilayer body by stacking the first and second ceramic green sheets while allowing the stripe shaped first internal electrode patterns and the stripe shaped second internal electrode patterns to intersect with each other, and forming a cover layer by stacking a plurality of ceramic green sheets on at least one of an upper surface and a lower surface of the ceramic green sheet multilayer body;
cutting the ceramic green sheet multilayer body into multilayer bodies while traversing the stripe shaped first and second internal electrode patterns such that first and second internal electrodes have a uniform width, each multilayer body having side surfaces to which edges of the first and second internal electrodes are exposed in a width direction of the multilayer body; and
forming first and second side margin parts on the side surfaces to which the edges of the first and second internal electrodes are exposed, respectively, by using ceramic slurry,
wherein the first and second side margin parts have an average thickness of 18 μm or less, and
when a boundary surface between the cover layer and the first or second side margin part in the multilayer body is divided into two regions in a thickness direction of the multilayer body, a region adjacent to the internal electrode is S1, and a porosity of S1 is P1, 1≦P1≦20 is satisfied.
8. The method of claim 7 , wherein in the forming of the ceramic green sheet multilayer body, a central portion of the stripe shaped first internal electrode pattern and the predetermined interval between the stripe shaped second internal electrode patterns are overlapped with each other.
9. The method of claim 7 , wherein the cutting of the ceramic green sheet multilayer body includes:
cutting the ceramic green sheet multilayer body into bar shaped multilayer bodies each having the side surfaces to which the edges of the first and second internal electrodes are exposed; and
cutting a central portion of the first internal electrode and a predetermined interval between the second internal electrodes along the same cutting line to form the multilayer body having a third end surface and a fourth end surface to which one ends of the first and second internal electrodes are exposed, respectively, after the forming of the first and second side margin parts.
10. The method of claim 7 , wherein the cutting of the ceramic green sheet multilayer body includes:
cutting the ceramic green sheet multilayer body into bar shaped multilayer bodies each having the side surfaces to which the edges of the first and second internal electrodes are exposed; and
cutting a central portion of the first internal electrode and a predetermined interval between the second internal electrodes in the bar shaped multilayer body along the same cutting line to form the multilayer body having a third end surface and a fourth end surface to which one ends of the first and second internal electrodes are exposed, respectively, before the forming of the first and second side margin parts.
11. The method of claim 7 , wherein the forming of the first side margin part and the second side margin part is performed by applying the ceramic slurry to the side surfaces to which the edges of the first and second internal electrodes are exposed.
12. The method of claim 7 , wherein the forming of the first side margin part and the second side margin part is performed by dipping the side surfaces, to which the edges of the first and second internal electrodes are exposed, into the ceramic slurry.
13. The method of claim 7 , wherein when the boundary surface between the cover layer and the first or second side margin part in the ceramic green sheet multilayer body is divided into two regions in the thickness direction, a region adjacent to an upper surface or a lower surface of the ceramic green sheet multilayer body is S2, and a porosity of S2 is P2, P1/P2>2 is satisfied.