Active energy ray-curable ink, ink cartridge containing ink, image or cured product forming method, and image or cured product forming device
An active energy ray-curable ink which contains: polymerizable compounds containing a monofunctional polymerizable monomer a homopolymer of which has Tg of 90° C. or higher, wherein a cured product obtained by forming a coating film having an average thickness of 10 μm on a polycarbonate substrate using the ink, and 15 seconds later, and applying active energy rays having a light quantity of 1,500 mJ/cm 2 to the coating film to cure satisfies the following (1) and (2): (1) a stretchability of the cured product represented by the following equation is 2 or greater, when the cured product is stretched by a tensile tester at a tensile speed of 20 mm/min, and temperature of 180° C., and Stretchability=(length after tensile test)/(length before tensile test) (2) adhesion between the substrate and the cured product as measured by a cross-cut test in accordance with JIS K5400 is 70 or greater.
1. An active energy ray-curable ink comprising:
polymerizable compounds,
wherein the polymerizable compounds contain a monofunctional polymerizable monomer, a homopolymer of which has glass transition temperature of 90° C. or higher, and
wherein a cured product obtained by forming a coating film having an average thickness of 10 μm on a polycarbonate substrate using the active energy ray-curable ink, and 15 seconds later, and applying active energy rays having a light quantity of 1,500 mJ/cm 2 to the coating film to cure satisfies the following conditions (1) and (2):
(1) a stretchability of the cured product, which is represented by the following equation, is 2 or greater, when the cured product is stretched by means of a tensile tester at a tensile speed of 20 mm/min, and temperature of 180° C., and
Stretchability=(length after a tensile test)/(length before the tensile test)
(2) adhesion between the polycarbonate substrate and the cured product as measured by a cross-cut test in accordance with JIS K5400 is 70 or greater.
2. The active energy ray-curable ink according to claim 1 , wherein the monofunctional polymerizable monomer has a cyclic structure.
3. The active energy ray-curable ink according to claim 1 , wherein the monofunctional polymerizable monomer is a monomer containing a hydroxyl group, and an amount of the monomer containing a hydroxyl group is 15% by mass or less relative to a total amount of the polymerizable compounds.
4. The active energy ray-curable ink according to claim 1 , wherein the polymerizable compounds contain a combination of a first monomer a homopolymer of which has glass transition temperature of 90° C. or higher, and a second monomer capable of dissolving the polycarbonate substrate, or the polymerizable compounds contain a third monomer a homopolymer of which has glass transition temperature of 90° C. or higher, and which is capable of dissolving the polycarbonate substrate.
5. The active energy ray-curable ink according to claim 4 , wherein the first monomer is hydroxyethyl(meth)acrylamide, isobornyl (meth)acrylate, adamantyl (meth)acrylate, dicyclopentenyl (meth)acrylate, dicyclopentanyl (meth)acrylate, or dicyclopentenyloxyethyl (meth)acrylate, or any combination thereof.
6. The active energy ray-curable ink according to claim 4 , wherein the second monomer is tetrahydrofurfuryl (meth)acrylate, cyclohexyl (meth)acrylate, benzyl (meth)acrylate, (meth)acryloylmorpholine, dimethylaminopropyl(meth)acrylamide, (cyclohexanespiro-2-(1,3-dioxolan-4-yl))methylacrylate, or (2-methyl-2-ethyl-1,3-dioxolan-4-yl)methylacrylate, or any combination thereof.
7. The active energy ray-curable ink according to claim 1 , wherein the active energy ray-curable ink is an inkjet ink, is free from a diluent solvent, and has a viscosity of 3 mPa·s to 40 mPa·s at 25° C., or 7 mPa·s to 15 mPa·s at 60° C.
8. The active energy ray-curable ink according to claim 1 , wherein the polymerizable compounds consist of monofunctional polymerizable monomers.
9. The active energy ray-curable ink according to claim 4 , wherein an amount of the first monomer is 50% by mass or greater relative to a total amount of the polymerizable compounds.
10. The active energy ray-curable ink according to claim 4 , wherein an amount of the second monomer is 30% by mass or greater relative to a total amount of the polymerizable compounds.
11. The active energy ray-curable ink according to claim 4 , wherein the polymerizable compounds contain the third monomer, an amount of the monofunctional polymerizable monomer a homopolymer of which has glass transition temperature of 90° C. or higher is 50% by mass or greater relative to a total amount of the polymerizable compounds, and an amount of the monofunctional polymerizable monomer capable of dissolving the polycarbonate substrate is 30% by mass or greater relative to the total amount of the polymerizable compounds.
12. The active energy ray-curable ink according to claim 1 , wherein the active energy ray-curable ink is capable of dissolving the polycarbonate substrate.
13. An ink cartridge, comprising:
an active energy ray-curable ink; and
a container housing the active energy ray-curable ink,
wherein the active energy ray-curable ink, comprises: polymerizable compounds,
wherein the polymerizable compounds contain a monofunctional polymerizable monomer, a homopolymer of which has glass transition temperature of 90° C. or higher, and
wherein a cured product obtained by forming a coating film having the average thickness of 10 μm on a polycarbonate substrate using the active energy ray-curable ink, and 15 seconds later, and applying active energy rays having a light quantity of 1,500 mJ/cm 2 to the coating film to cure satisfies the following conditions (1) and (2):
(1) a stretchability of the cured product, which is represented by the following equation, is 2 or greater, when the cured product is stretched by means of a tensile tester at a tensile speed of 20 mm/min, and temperature of 180° C., and
Stretchability=(length after a tensile test)/(length before the tensile test)
(2) adhesion between the polycarbonate substrate and the cured product as measured by a cross-cut test in accordance with JIS K5400 is 70 or greater.
14. An image or cured product forming device, comprising:
an ink ejecting unit configured to eject an active energy ray-curable ink onto a surface of a substrate through an inkjet recording system;
a curing unit configured to apply active energy rays to the active energy ray-curable ink ejected onto the surface of the substrate, to thereby cure the active energy ray-curable ink; and
an ink cartridge,
wherein the ink cartridge comprises:
the active energy ray-curable ink; and
a container housing the active energy ray-curable ink,
wherein the active energy ray-curable ink comprises:
polymerizable compounds,
wherein the polymerizable compounds contain a monofunctional polymerizable monomer, a homopolymer of which has glass transition temperature of 90° C. or higher, and
wherein a cured product obtained by forming a coating film having the average thickness of 10 μm on a polycarbonate substrate using the active energy ray-curable ink, and 15 seconds later, and applying active energy rays having a light quantity of 1,500 mJ/cm 2 to the coating film to cure satisfies the following conditions (1) and (2):
(1) a stretchability of the cured product, which is represented by the following equation, is 2 or greater, when the cured product is stretched by means of a tensile tester at a tensile speed of 20 mm/min, and temperature of 180° C., and
Stretchability=(length after a tensile test)/(length before the tensile test)
(2) adhesion between the polycarbonate substrate and the cured product as measured by a cross-cut test in accordance with JIS K5400 is 70 or greater.