Dual coated optical fibers and methods for forming the same
Dual coated optical fibers and methods for forming dual coated optical fibers are disclosed herein. The dual coated optical fibers include a glass fiber comprising a core region, a cladding region and a dual coating layer surrounding the glass fiber. The dual coating layer includes an inner coating and an outer coating. The inner coating surrounds the glass fiber and includes a first polyimide material. In one embodiment the first polyimide material also includes an adhesion promoter. The outer coating surrounds and is in direct contact with the inner coating and includes a second polyimide material having a decomposition threshold temperature greater than the first polyimide material. The second polyimide material may also have a modulus of elasticity greater than the first polyimide material and a moisture uptake lower than the first polyimide material.
1. A dual coated optical fiber comprising:
a glass fiber comprising a core region and a cladding region;
a dual coating layer surrounding the glass fiber and in direct contact with the glass fiber, the dual coating layer comprising:
an inner coating surrounding the glass fiber, the inner coating comprising a first polyimide material, said first polyimide material comprising a mixture of a polyamic acid of benzophenone tetracarboxylic dianhydride/4,4-oxydianiline/m-phenylenediamine polymer and an organosilane adhesion promoter; and
an outer coating surrounding and in direct contact with the inner coating, the outer coating comprises a second polyimide material, said second polyimide material comprising an s-biphenyldianhydride/p-phenylenediamine polymer.
2. A dual coated optical fiber according to claim 1 , wherein a second polyimide material having a decomposition threshold temperature greater than the first polyimide material.
3. The dual coated optical fiber of claim 2 wherein the decomposition threshold temperature of the second polyimide material is greater than 550° C.
4. The dual coated optical fiber of claim 2 wherein the glass fiber has a radius in a range from 12.5 microns to 155 microns.
5. The dual coated optical fiber of claim 2 wherein the inner coating has a radial thickness in a range from 1 micron to 10 microns.
6. The dual coated optical fiber of claim 2 wherein the outer coating has a radial thickness in a range from 5 microns to 20 microns.
7. The dual coated optical fiber of claim 1 wherein a modulus of elasticity of the an outer coating-second polyimide material is greater than a modulus of elasticity of the first polyimide material.
8. The dual coated optical fiber of claim 1 wherein a moisture uptake of the second polyimide material is lower than a moisture uptake of the first polyimide material.
9. The dual coated optical fiber of claim 1 wherein the dual coating layer does not separate from the glass fiber after immersion in a deionized water bath at room temperature for seven days.
10. The dual coated optical fiber of claim 1 wherein a tensile strength of the dual coated optical fiber is greater than 300 kpsi after exposure to a temperature of 300° C. for 216 hours.
11. The dual coated optical fiber of claim 1 , further comprising a hermetic coating between the glass fiber and the inner coating.