Construction element

1. A construction element capable of forming an expansion joint, the construction element comprising

a polymeric foam containing at least one insecticide substantially distributed throughout the polymeric foam;

wherein the polymeric foam has a cell size of approximately 0.5 to 2 mm; and

wherein on at least one outer surface of the construction element there is a water resistant adhesive attached thereto and a removable cover releasably attached to the adhesive whereby the removable cover is adapted to be removed upon application of the construction element;

wherein the construction element acts as a physical and chemical barrier to impede the ingress of insects into a structure;

wherein the polymeric foam has a compression set at 22 hours of less than 6%;

wherein the polymeric foam is closed cell polymeric foam;

wherein the polymeric foam is manufactured at a temperature of less than 180° C. and is prepared primarily from a blend of a crosslinked polyethylene and a low melting ethylene-vinyl acetate (EVA) copolymer; and

wherein the polymeric foam has a density of between 23 to 28 kg/m 3 .

2. The construction element according to claim 1 , wherein the polymeric foam has a cell size of approximately 0.5 mm to 1 mm.

3. The construction element according to claim 1 , wherein the polymeric foam is approximately 0.5 to 30 mm thick.

4. The construction element according to claim 1 , wherein the polymeric foam is approximately 10 mm thick.

5. The construction element according to claim 1 , wherein the crosslinked ethylene is a crosslinked linear low density polyethylene (LLDPE).

6. The construction element according to claim 1 , wherein the polymeric foam is a composite comprising crosslinked LLDPE and low melting EVA polymer.

7. The construction element according to claim 1 , wherein the polymeric foam comprises a stabilizer and the stabilizer is kaolin.

8. The construction element according to claim 1 , wherein the insecticide exhibits control or repellent affects against termites.

9. The construction element according to claim 1 , wherein the insecticide is selected from any one or more of the group comprising pyrethrum, synthetic pyrethroids, organo-chlorines, organo-sulfurs, carbamates, organo-phosphates, formamidines, nicotinoids, spinosyns, phenylpyrazoles, pyrroles, pyrazoles, dinitrophenols, pyridazinones, quinazolines, and benzoylureas.

10. The construction element according to claim 1 , wherein the insecticide is a synthetic pyrethroid compound selected from the group comprising deltamethrin, permethrin, bifenthrin, and mixtures thereof.

11. The construction element according to claim 1 , wherein the insecticide is bifenthrin.

12. The construction element according to claim 1 , wherein the concentration of the insecticide is selected from the group comprising between approximately 0.25 to 2.0 wt. %, approximately 0.5 wt. %, 0.75 wt. % and 1 wt. %.

13. The construction element according to claim 1 , wherein the polymeric foam has a density of 25 kg/m 3 .

14. The construction element according to claim 1 , wherein the polymeric foam has a tear strength of between approximately 2.5 to 4.0 kg/cm 2 .

15. The construction element according to claim 1 , wherein the polymeric foam has an elongation of greater than 140%.

16. The construction element according to claim 1 , wherein the removable cover includes a motif.

17. The construction element according to claim 1 , wherein the removable cover includes a motif and the motif comprises words, logo, decorative design or construction element characteristic.

18. The construction element according to claim 1 , which includes at least one zipping strip to one top edge of the polymeric foam.

19. The construction element according to claim 1 , wherein the polymeric foam includes a UV stabilizer.

20. The construction element of claim 1 wherein the polymeric foam further comprises one more additives selected from the group comprising inorganic fillers, pigments, lubricants, stabilizers, antioxidants, antifungal agents, acid scavengers, ultraviolet absorbers, flame retardants, processing aids, dispersion aids and extrusion aids.

21. The construction element according to claim 20 , wherein a stabilizer is present in an amount between 0.1-10 wt. % and the stabilizers is selected from the group comprising inorganic silicate, silicone dioxide, hydrophobic silicone dioxide, montmorillonite clay, sodium bentonite clay with high montmorillonite content, magnesium aluminium silicate and aluminium silicate.

22. A method of protecting a structure against the ingress of insects into the structure, the method comprising the step of positioning one or more construction element(s) at a position(s) during the construction of the structure to form a barrier to at least impede the entry of insects, the construction element comprising

a polymeric foam containing at least one insecticide substantially distributed throughout the polymeric foam;

wherein the polymeric foam has a cell size of approximately 0.5 to 2 mm; and

wherein on at least one outer surface of the construction element there is a water resistant adhesive attached thereto and a removable cover releasably attached to the adhesive whereby the removable cover is adapted to be removed upon application of the construction element;

wherein the polymeric foam has a compression set at 22 hours of less than 6%;

wherein the polymeric foam is closed cell polymeric foam;

wherein the polymeric foam is manufactured at a temperature of less than 180° C. and is prepared primarily from a blend of a crosslinked polyethylene and a low melting ethylene-vinyl acetate (EVA) copolymer; and

wherein the polymeric foam has a density of between 23 to 28 kg/m 3 .