Polyacrylic acid-type water absorbent resin and method for producing same
Provided is a method for producing a water absorbent resin, which promotes the formation of interconnected voids (continuous gas bubbles) in a foamed polymer (foam-like water absorbent resin) by a more convenient method, and produces with high efficiency a water absorbent resin which exhibits a high water absorption rate even when stepped into a sheet form or a powder form in hygiene articles and the like. Disclosed is a a method for producing a polyacrylic acid-type water absorbent resin, comprising (A) a step of obtaining an aqueous solution of acrylic acid-type monomers containing gas bubbles dispersed therein; (B) a step of polymerizing the aqueous monomer solution and thereby obtaining a foamed polymer; and (C) a step of heating and drying the foamed polymer, wherein gas bubbles are incorporated such that the volumetric expansion factor defined by the following formula (1); [Formula 1] Volumetric expansion factor=(Volume of aqueous monomer solution after gas bubble dispersion)/(volume of aqueous mononer solution before gas bubble dispersion) Formula (1); exceeds 1.1 times, and the aqueous monomer solution having a monomer concentration defined by the following formula (2); [Formula 2] Monomer concentration [wt %]=(Weight of a monomer)/{(weight of a monomer)+(weight of solvent)}×100 Formula (2); of 40% by weight or greater is boiling polymerized at a temperature of 100° C. or higher.
1. A method for producing a polyacrylic acid-type water absorbent resin, comprising (A) a step of obtaining an aqueous solution of acrylic acid-type monomers containing gas bubbles dispersed therein; (B) a step of polymerizing the aqueous monomer solution and thereby obtaining a foamed polymer; and (C) a step of heating and drying the foamed polymer, in which the gas bubbles that are dispersed are formed by an inert gas,
Wherein the gas bubbles are incorporated such that the volumetric expansion factor defined by the following formula (1):
[Formula 1]
Volumetric expansion factor =(Volume of aqueous monomer solution after gas bubble dispersion)/(volume of aqueous monomer solution before gas bubble dispersion) Formula (1)
exceeds 1.1 times, and the aqueous monomer solution having a monomer concentration defined by the following formula (2):
[Formula 2]
Monomer concentration [wt %]=(Weight of a monomer)/{(weight of a monomer) +(weight of solvent)}×100 Formula (2)
of 40% by weight or greater is boiling polymerized at a temperature of 100° C. or higher.
2. The method according to claim 1 , further comprising (D) a step of uniforming gas bubbles in the aqueous monomer solution.
3. The method according to claim 1 , wherein the step (B) is carried out after the step (D).
4. The method according to claim 2 , wherein in the step (D), the aqueous monomer solution containing gas bubbles is circulated in a circulation tank.
5. The method according to claim 4 , wherein in the step (D), the oxygen concentration in the headspace of the circulation tank is 1% by volume or greater.
6. The method according to claim 1 , wherein the aqueous solution of acrylic acid-type monomers comprises a surfactant.
7. The method according to claim 1 , wherein in the step (B), the polymerization initiation temperature is 40° C. or higher.
8. The method according to claim 1 , further comprising a step of surface crosslinking the foamed polymer, after the step (C).
9. The method according to claim 1 , wherein in the step (B), the time period between the supply of the aqueous solution of acrylic acid-type monomers to a polymerization apparatus and the subsequent initiation of polymerization is 5 minutes or less.
10. The method according to claim 1 , further comprising a pulverization step and/or a classification step, and a fine powder recycling step after the step (C), wherein 1% to 40% by weight of the fine powder is recycled prior to the classification step.
11. The method according to claim 1 , further comprising a molded step simultaneously with the step (B), or after the step (B).
12. The method according to claim 1 , wherein the aqueous solution of acrylic acid-type monomers contains p-methoxyphenol in an amount of 200ppm or less relative to the content of acrylic acid.