Superhydrophobic films
Superhydrophobic films and methods of making such films are disclosed. More particularly, superhydrophobic films having durable nanostructures with high contrast ratios and various methods of producing such films are disclosed.
1. A superhydrophobic film comprising:
a first major surface;
a second major surface opposite the first major surface, the second major surface comprising a plurality of prismatic microstructures each comprising a triangular cross-section in a plane transverse to the second major surface; and
a plurality of nanoposts formed protruding from the surface of the plurality of microstructures, wherein the nanoposts each extend between a base and a peak along a longitudinal structure axis thereof, the base being embedded in the surface of the plurality of microstructures, the nanoposts each have an average length-to-base ratio of at least 5 to 1, and the plurality of nanoposts comprises a material having a slower etching rate than a material of the surface of the plurality of microstructures;
wherein the superhydrophobic film has a water contact angle of over 150 degrees and a sliding angle of less than 3 degrees.
2. The superhydrophobic film of claim 1 , wherein the nanoposts have a length-to-base ratio of at least 10 to 1.
3. The superhydrophobic film of claim 1 , wherein the microstructures comprise a silicone polymer.
4. The superhydrophobic film of claim 3 , wherein the silicone polymer is PDMS.
5. The superhydrophobic film of claim 1 , wherein the nanoposts are at least partially covered in a fluorochemical coating.
6. The superhydrophobic film of claim 1 , wherein the nanoposts comprise a crystalline, organic material.
7. The superhydrophobic film of claim 6 , wherein the crystalline, organic material is perylene red (PR149).
8. The superhydrophobic film of claim 1 , wherein the nanoposts are coated in a slow-etching metal.
9. The superhydrophobic film of claim 8 , wherein the metal-coated nanoposts are coated with a low surface energy coating.
10. The superhydrophobic film of claim 1 , wherein the microstructures have a height of between about 1 micron and about 1000 microns.
11. The superhydrophobic film of 1 , wherein the microstructures have an average peak-to-peak distance of between about 0 to about 5 times the average height of the microstructures.
12. The superhydrophobic film of claim 1 , wherein the film reflects less than 2% of incident light.
13. A method of creating a superhydrophobic film, comprising:
providing a first film, the film comprising a plurality of microstructures on a first surface of the film;
applying a layer of nanoposts protruding from the first film;
coating the first film in a curable composition, and curing the composition to create a negative of the first film;
separating the negative from the first film, wherein the nanoposts protruding from the first film remain embedded in the negative after separating the negative;
etching the negative, resulting in a superhydrophobic film comprising:
a first major surface;
a second major surface opposite the first major surface, the second major surface comprising a plurality of prismatic microstructures each comprising a triangular cross-section in a plane transverse to the second major surface; and
a plurality of nanoposts formed protruding from the surface of the plurality of microstructures, wherein the nanoposts each extend between a base and a peak along a longitudinal structure axis thereof, the base being embedded in the surface of the plurality of microstructures, the nanoposts each have an average length-to-base ratio of at least 5 to 1, and the plurality of nanoposts comprises a material having a slower etching rate than a material of the surface of the plurality of microstructures,
wherein the superhydrophobic film has a water contact angle of over 150 degrees and a sliding angle of less than 3 degrees.
14. The method of claim 13 , wherein the curable composition is at least 95 wt. % PDMS.
15. The method of claim 13 , wherein the nanoposts protruding from the first film are applied by vacuum deposition.
16. The method of claim 13 , wherein the nanoposts are provided at a density of between about 3 billion/cm 2 to about 5 billion/cm 2 .
17. The method of claim 13 , wherein the nanoposts have an average spacing of between about 20 nm and about 100 nm from the closest adjacent nanopost.
18. The method of claim 13 , wherein the nanoposts have an average length of between about 0.5 and 2 microns.
19. The method of claim 13 , wherein the nanoposts protruding from the first film are produced by self-assembling through annealing of a vacuum deposited organic pigment coating.
20. The method of claim 13 , further comprising the step of coating the microstructures with a fluorochemical coating.
21. The method of claim 13 , wherein the nanoposts having a length-to-base ratio of at least 10 to 1.