Plastic optical fiber comprising cyclic block copolymer

1. A plastic optical fiber core comprising a cyclic block copolymer characterized by a:

A. Weight ratio of hydrogenated conjugated diene polymer block to hydrogenated vinyl aromatic polymer block of 35:65 to 10:90;

B. Number average molecular weight (Mn) of from 40,000 to 150,000 g/mol;

C. Hydrogenation level such that each hydrogenated vinyl aromatic polymer block and each hydrogenated conjugated diene polymer block has a hydrogenation level of at least 95 percent;

D. Tensile modulus greater than 1380 kilopascals (kPa) (200,000 pounds per square inch (psi)); and

E. Room temperature (23° C.) un-notched Izod impact toughness of at least 110 Joules per meter (J/m) (2 foot-pounds per inch (ft-lb/in.)).

2. The plastic optical fiber core of claim 1 in which the cyclic block copolymer is further characterized by a glass transition temperature of at least 120° C.

3. The plastic optical fiber core of claim 2 further comprising a cladding over and in contact with the core, the core and cladding each having a refractive index, the refractive index of the cladding different from the refractive index of the core.

4. The plastic optical fiber core of claim 3 in which the refractive index of the cladding is at least 0.012 lower than the refractive index of the core.

5. The plastic optical fiber core of claim 4 in which the cladding comprises at least one of a fluorine-containing olefin resin, a fluorinated methacrylate polymer, a silicone resin, poly(4-methyl-1-pentene) and an ethylene-vinyl acetate.

6. The plastic optical fiber core of claim 4 in which the cladding comprises at least one of a (i) substantially fully hydrogenated vinyl aromatic block copolymer with fluorine modification, (ii) cyclic olefin polymer, and (iii) fluorine modified cyclic olefin copolymer.

7. The plastic optical fiber core of claim 1 in which the cyclic block copolymer is further characterized a change in attenuation between 105° C. and 25° C. of not more than 1 dB/m measured at a wavelength of 650 nm.

8. The plastic optical fiber core of claim 7 in which the cyclic block copolymer, prior to hydrogenation, has at least one block comprising a conjugated diene and at least two blocks comprising a vinyl aromatic monomer.

9. The plastic optical fiber core of claim 8 in which the vinyl aromatic polymer block comprises units derived from at least one of styrene and alpha-methylstyrene.

10. The plastic optical fiber core of claim 9 in which the styrenic block copolymer, prior to hydrogenation, is a styrene-butadiene-styrene-butadiene-styrene pentablock copolymer.

11. The plastic optical fiber core of claim 10 in which the polymerized vinyl aromatic content of the cyclic block copolymer, prior to hydrogenation, is from 70 to 85 wt %, each weight percent being based upon total block copolymer weight prior to hydrogenation.

12. The plastic optical fiber core of claim 11 in which the number average molecular weight (Mn) of the cyclic block copolymer is from 50,000 to 90,000 g/mol.

13. The optical fiber core of claim 12 in which the

A. Weight ratio of hydrogenated conjugated diene polymer block to hydrogenated vinyl aromatic polymer block of 30:70 to 15:85;

B. Number average molecular weight (Mn) of from 60,000 to 90,000 g/mol; and

C. Hydrogenation level such that each hydrogenated vinyl aromatic polymer block and each hydrogenated conjugated diene polymer block has a hydrogenation level of at least 98 percent.

14. An automotive, industrial, medical or consumer system comprising the plastic optical fiber core of claim 13 .

15. A plastic optical fiber comprising a core-cladding configuration in which the core comprises a cyclic block copolymer characterized by a:

A. Weight ratio of hydrogenated conjugated diene polymer block to hydrogenated vinyl aromatic polymer block of 35:65 to 10:90;

B. Number average molecular weight (Mn) of from 40,000 to 150,000 g/mol;

C. Hydrogenation level such that each hydrogenated vinyl aromatic polymer block and each hydrogenated conjugated diene polymer block has a hydrogenation level of at least 95 percent; and

D. Tensile modulus greater than 1380 kilopascals (kPa) (200,000 pounds per square inch (psi)).