Sintering aids for lanthanide ceramics
This disclosure relates to a method of densifying a lanthanide chromite ceramic or a mixture containing a lanthanide chromite ceramic. The method comprises mixing one or more lanthanide chromite ceramics with one or more sintering aids, and sintering the mixture. The one or more lanthanide chromite ceramics are represented by the formula (Ln 1-x AE x ) z Cr 1-y B y O 3-δ , wherein Ln is a lanthanide element or yttrium, AE is one or more alkaline earth elements, B is one or more transition metals, x is a value less than 1, y is a value less than or equal to 0.5, and z is a value from 0.8 to 1.2. The sintering aids comprise one or more spinel oxides. The one or more spinel oxides are represented by the formula AB 2 O 4 or A 2 BO 4 wherein A and B are cationic materials having an affinity for B-site occupancy in a lanthanide chromite ceramic structure, e.g., ZnMn 2 O 4 , MgMn 2 O 4 , MnMn 2 O 4 and CoMn 2 O 4 . This disclosure also relates in part to products, e.g., dense ceramic structures produced by the above method.
1. A method selected from:
a) a method of densifying a lanthanide chromite ceramic, said method comprising:
mixing the lanthanide chromite ceramic with sintering aids, the sintering aids comprising one or more spinel oxides; and
sintering the mixture at a sintering temperature from about 1100° C. to about 1500° C.;
b) a method of densifying a multi-phase conducting ceramic mixture containing a lanthanide chromite ceramic and one or more ionically conducting ceramics said method comprising:
mixing the lanthanide chromite ceramic, the one or more ionically conducting ceramics, and sintering aids, the sintering aids comprising one or more spinel oxides, and
sintering the mixture at a sintering temperature from about 1100° C. to about 1500° C.; and
c) a method of densifying a multi-phase conducting ceramic mixture comprising a lanthanide chromite ceramic and one or more ionically conducting ceramics, said method comprising:
mixing the lanthanide chromite ceramic and the one or more ionically conducting ceramic with sintering aids, the sintering aids comprising one or more spinel oxides, and
sintering the mixture at a sintering temperature from about 1100° C. to about 1500° C. in an air atmosphere, wherein the one or more spinel oxides are selected from the group consisting ZnMn 2 O 4 , MgMn 2 O 4 , MnMn 2 O 4 and CoMn 2 O 4 .
2. The method of claim 1 wherein the sintering temperature is between about 1200° C. to about 1450° C.
3. The method of claim 1 wherein the one or more spinel oxides are incorporated into a matrix of the lanthanide chromite and/or the ionically conductive ceramic to enable liquid phase sintering and/or reaction-based sintering, as the one or more spinel oxides form solid solutions with the matrix of lanthanide chromite and/or the ionically conductive ceramic.
4. The method of claim 1 wherein the sintering is performed in an air atmosphere or a reducing atmosphere.
5. The method of claim 1 wherein the lanthanide chromite ceramic is represented by the formula: (Ln 1-x AE x ) z Cr 1-y B y O 3-δ ;
wherein Ln is a lanthanide element or yttrium, AE is one or more alkaline earth elements, B is one or more transition metals, x is a value less than 1, y is a value less than or equal to 0.5, and z is a value from 0.8 to 1.2.
6. The method of claim 5 wherein x is less than or equal to 0.25, Ln is lanthanum, AE is strontium, and B comprises B′ y-n B″ n , wherein B′ and B″ are transition metals and n is a value less than 0.5.
7. The method of claim 5 wherein the lanthanide chromite ceramic is represented by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.72 Mn 0.26 V 0.02 O 3-δ .
8. The method of claim 5 wherein the lanthanide chromite is represented by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.74 Mn 0.26 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.75 Mn 0.25 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.60 Mn 0.40 O 3-δ .
9. A product produced by the method of claim 1 .
10. The product of claim 9 wherein the product comprises an interconnector for a solid oxide fuel cell (SOFC), a mixed conducting separation layer for an electrochemical membrane system, a catalyst or other component for use in combustion reactions for hydrocarbons and methane reforming, or a component of an electrochemical sensor.
11. A composition selected from:
a) a dense lanthanide chromite ceramic composition comprising:
a lanthanide chromite ceramic represented by the formula (Ln 1-x AE x ) z Cr 1-y B y O 3-δ , wherein Ln is a lanthanide element or yttrium, AE is one or more alkaline earth elements, B is one or more transition metals, x is a value less than 1, y is a value less than or equal to 0.5, and z is a value from 0.8 to 1.2; and
a sintering aid comprising one or more spinel oxides selected from the group consisting ZnMn 2 O 4 , MgMn 2 O 4 MnMn 2 O 4 and CoMn 2 O 4 , and wherein the density of the ceramic composition is enhanced by sintering the composition at a sintering temperature from about 1100° C. to about 1500° C.; and
b) a dense, multi-phase ceramic composition comprising:
a lanthanide chromite ceramic represented by the formula (Ln 1-x AE x ) z Cr 1-y B y O 3-δ , wherein Ln is a lanthanide element or yttrium, AE is one or more alkaline earth elements, B is one or more transition metals, x is a value less than 1, y is a value less than or equal to 0.5, and z is a value from 0.8 to 1.2;
one or more ionically conducting ceramics; and
a sintering aid comprising one or more spinel oxides, and wherein the density of the ceramic composition is enhanced by sintering the composition at a sintering temperature from about 1100° C. to about 1500° C.
12. The composition of claim 11 wherein the sintering temperature is between about 1200° C. to about 1450° C.
13. The composition of claim 11 wherein the one or more spinel oxides are incorporated into a matrix of the lanthanide chromite and/or the ionically conductive ceramic to enable liquid phase sintering and/or reaction-based sintering, as the one or more spinel oxides form solid solutions with the matrix of lanthanide chromite and/or the ionically conductive ceramic.
14. The composition of claim 11 wherein the sintering is performed in an air atmosphere or a reducing atmosphere.
15. The composition of claim 11 wherein the lanthanide chromite ceramic is represented by the formula: (Ln 1-x AE x ) z Cr 1-y B y O 3-δ ;
wherein Ln is a lanthanide element or yttrium, AE is one or more alkaline earth elements, B is one or more transition metals, x is a value less than 1, y is a value less than or equal to 0.5, and z is a value from 0.8 to 1.2.
16. The composition of claim 15 wherein x is less than or equal to 0.25, Ln is lanthanum, AE is strontium, and B comprises B′ y-n B″ n , wherein B′ and B″ are transition metals and n is a value less than 0.5.
17. The composition of claim 15 wherein the lanthanide chromite ceramic is represented by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.72 Mn 0.26 V 0.02 O 3-δ .
18. The method of claim 15 wherein the lanthanide chromite is represented by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.74 Mn 0.26 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.75 Mn 0.25 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.60 Mn 0.40 O 3-δ .
19. A method selected from:
a) a method of densifying a lanthanide chromite ceramic, said method comprising:
mixing the lanthanide chromite ceramic with sintering aids, the sintering aids comprising one or more spinel oxides; and
sintering the mixture at a sintering temperature from about 1100° C. to about 1500° C.;
b) a method of densifying a multi-phase conducting ceramic mixture containing a lanthanide chromite ceramic and one or more ionically conducting ceramics said method comprising:
mixing the lanthanide chromite ceramic, the one or more ionically conducting ceramics, and sintering aids, the sintering aids comprising one or more spinel oxides, and
sintering the mixture at a sintering temperature from about 1100° C. to about 1500° C.; and
c) a method of densifying a multi-phase conducting ceramic mixture comprising a lanthanide chromite ceramic and one or more ionically conducting ceramics, said method comprising:
mixing the lanthanide chromite ceramic and the one or more ionically conducting ceramic with sintering aids, the sintering aids comprising one or more spinel oxides, and
sintering the mixture at a sintering temperature from about 1100° C. to about 1500° C. in an air atmosphere,
wherein the lanthanide chromite ceramic is represented by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.72 Mn 0.26 V 0.02 O 3-δ , or by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.74 Mn 0.26 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.75 Mn 0.25 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.60 Mn 0.40 O 3-δ .
20. The method of claim 19 wherein the one or more spinel oxides are represented by the formula: AB 2 O 4 or A 2 BO 4 , where A and B are cationic materials having an affinity for B-site occupancy in a lanthanide chromite ceramic structure.
21. The method of claim 20 wherein the one or more spinel oxides are selected from the group consisting ZnMn 2 O 4 , MgMn 2 O 4 , MnMn 2 O 4 and CoMn 2 O 4 .
22. The composition of claim 19 wherein the one or more spinel oxides are incorporated into a matrix of the lanthanide chromite and/or the ionically conductive ceramic to enable liquid phase sintering and/or reaction-based sintering, as the one or more spinel oxides form solid solutions with the matrix of lanthanide chromite and/or the ionically conductive ceramic.
23. A composition selected from:
a) a dense lanthanide chromite ceramic composition comprising:
a lanthanide chromite ceramic represented by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.72 Mn 0.26 V 0.02 O 3-δ , or by the formula (La 0.825 Sr 0.175 ) 0.95 Cr 0.74 Mn 0.26 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.75 Mn 0.25 O 3-δ , or by the formula (La 0.75 Sr 0.25 ) 0.95 Cr 0.60 Mn 0.40 O 3-δ ; and
a sintering aid comprising one or more spinel oxides, and wherein the density of the ceramic composition is enhanced by sintering the composition at a sintering temperature from about 1100° C. to about 1500° C.; and
b) a dense, multi-phase ceramic composition comprising:
a lanthanide chromite ceramic represented by the formula (Ln 1-x AE x ) z Cr 1-y B y O 3-δ , wherein Ln is a lanthanide element or yttrium, AE is one or more alkaline earth elements, B is one or more transition metals, x is a value less than 1, y is a value less than or equal to 0.5, and z is a value from 0.8 to 1.2;
one or more ionically conducting ceramics; and
a sintering aid comprising one or more spinel oxides, and wherein the density of the ceramic composition is enhanced by sintering the composition at a sintering temperature from about 1100° C. to about 1500° C.
24. The composition of claim 23 wherein the one or more spinel oxides are represented by the formula: AB 2 O 4 or A 2 BO 4 , where A and B are cationic materials having an affinity for B-site occupancy in a lanthanide chromite ceramic structure.
25. The composition of claim 23 wherein the one or more spinel oxides are selected from the group consisting ZnMn 2 O 4 , MgMn 2 O 4 , MnMn 2 O 4 and CoMn 2 O 4 .
26. The composition of claim 23 wherein the one or more spinel oxides are incorporated into a matrix of the lanthanide chromite and/or the ionically conductive ceramic to enable liquid phase sintering and/or reaction-based sintering, as the one or more spinel oxides form solid solutions with the matrix of lanthanide chromite and/or the ionically conductive ceramic.