Splice for jointing steel cord strips encased in thermoplastic material
A splice is described for jointing thermoplastic strips that include steel cords. In the splice a splice polymer is used that is a mixture of a co-polymer and a base polymer, wherein the co-polymer is a grafted co-polymer, a block co-polymer or a random co-polymer functionalized for enabling adhesion to the steel cords. Particular about the inventive splice is that the amount of co-polymer in the base polymer is such that in a test-till-break of a splice, part of the steel cords fracture in the test while the remaining cords are pulled out of the polymer without breaking. Surprisingly, a splice with such a failure behavior results in a better overall splice strength than a splice wherein a too large amount of co-polymer is added. When too much co-polymer is added all steel cords break in the test which strangely enough leads to a lower overall strength of the splice.
1. A splice connecting a first strip to a second strip, both strips comprising parallel steel cords embedded in a matrix of strip polymer, said steel cords having ends in said splice, said ends of said steel cords are embedded in a splice polymer, both said strip polymer and said splice polymer comprising thermoplastic polymers,
wherein
said splice polymer comprises a mixture of a co-polymer and a base polymer, said co-polymer being a grafted co-polymer functionalised for enabling adhesion to said steel cords and, wherein a fraction of said grafted co-polymer in said mixture is between 20 and 100% by weight, excluding 100%, while a degree of grafting by grafted substituent polar groups in said co-polymer is between 0.0001% and 1%, said fraction of said grafted co-polymer in said mixture being sufficient to make at least part of the steel cords break in said splice while steel cords that do not break in said splice are pulled out of said splice in a test-till-break.
2. The splice according to claim 1 wherein said fraction of said grafted co-polymer in said mixture is less than needed to have all of said steel cords break in a test-till-break of said splice.
3. The splice according to claim 1 wherein said base polymer
is a polyolefin polymer selected from the group comprising polyethylene, polypropylene, polybutylene, and higher olefinic polymers, co-polymers of ethylene, propylene, 1-butene, 2-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene and isomers thereof with each other and with other olefinically unsaturated monomers or
is an olefinically unsaturated aromatic polymer selected from the group comprising polystyrene and styrene copolymers or
is a polyester polymer selected from the group comprising polyethylene terephthalate or polybutylene terephthalate and terephthalate copolymers or
is a polyamide, or
is a polyurethane.
4. The splice according to claim 1 wherein said grafted co-polymer comprises substituent groups grafted to a base wherein said base polymer
is a polyolefin polymer selected from the group comprising polyethylene, polypropylene, polybutylene, and higher olefinic polymers, co-polymers of ethylene, propylene, 1-butene, 2-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene and isomers thereof with each other and with other olefinically unsaturated monomers or
is an olefinically unsaturated aromatic polymer selected from the group comprising polystyrene and styrene copolymers or
is a polyester polymer selected from the group comprising polyethylene terephthalate or polybutylene terephthalate and terephthalate copolymers or
is a polyamide, or
is a polyurethane,
said substituent groups originating from the group comprising unsaturated aliphatic acids, unsaturated aromatic acids, acid anhydrides, esters, alcohols or combinations thereof.
5. The splice according to claim 4 wherein said grafted co-polymer is one out of the group comprising acrylic acid or methacrylic acid functionalised polymers of polypropylene, polyethylene, polyethylene terephthalate, polybutylene terephthalate or the group comprising maleic anhydride functionalised polymers of polypropylene, polyethylene, ethylene-propylene rubber, polyamide, polyurethane.
6. The splice according to claim 1 wherein said strip polymer is the same as said base polymer.
7. The splice according to claim 1 wherein said strip polymer is a mixture of the same polymers as said splice polymer.
8. The splice according to claim 7 wherein said strip polymer is the same mixture as said splice polymer.
9. The splice according to claim 1 wherein said splice has a lay-out, and said lay-out of said splice is a plain stepped splice.
10. The splice according to claim 9 wherein a Splice Quality factor of said splice is larger than 1 and smaller than 2.
11. The splice according to claim 10 wherein said plain stepped splice has a breaking load that is larger than half of a lower breaking load of any one of said first and second strip.
12. The splice according to claim 9 wherein said plain stepped splice has a breaking load that is larger than half of a lower breaking load of any one of said first and second strip.
13. The splice according to claim 1 wherein said splice has a lay-out, and said lay-out of said splice is an interlaced stepped splice.
14. The splice according to claim 13 wherein said interlaced stepped splice has a breaking load that is larger than 60% of a lower breaking load of any one of said first and second strip.
15. The splice according to claim 13 wherein a Splice Quality factor of said splice is larger than 1 and smaller than 2.
16. The splice according to claim 15 wherein said interlaced stepped splice has a breaking load that is larger than 60% of a lower breaking load of any one of said first and second strip.
17. A strip comprising a splice according to claim 1 .
18. The splice according to claim 1 , wherein said fraction of said grafted co-polymer in said mixture is between 20 and 70% by weight.