Electroless gap fill

1. A method for providing copper filled features, comprising:

providing features in a layer on a substrate and forming at least one liner in the features composed of metal;

providing a simultaneous electroless copper plating and anneal, which fills the features with copper deposit, wherein the simultaneous electroless copper plating and anneal occurs in an electroless copper bath that is maintained at an anneal temperature and for an anneal time sufficient to perform the electroless copper plating and annealing simultaneously, such that the features are filled without the formation of voids or seams, wherein the anneal temperature of the electroless copper bath is between 150° C. and 250° C., wherein the electroless copper bath comprises one or more solvents having boiling points above the boiling point of water; and

chemical-mechanical polishing the copper deposit without an annealing after the simultaneous electroless copper plating and anneal and before the chemical-mechanical polishing; and

removing the metal from a bevel of the substrate after providing the features in a layer on the substrate and before providing the simultaneous electroless copper plating and anneal.

2. The method, as recited in claim 1 , wherein the electroless copper bath is maintained at the anneal temperature for an anneal time that is at least two minutes.

3. The method, as recited in claim 2 , further comprising providing a high temperature anneal at a temperature of at least 250° C. after chemical-mechanically polishing the copper deposit.

4. The method, as recited in claim 3 , wherein the simultaneous electroless copper plating and anneal causes copper grains to grow.

5. The method, as recited in claim 4 , wherein the simultaneous electroless copper plating and anneal does not distribute alloying components.

6. The method, as recited in claim 3 , wherein the high temperature anneal distributes an alloying component.

7. The method, as recited in claim 3 , further comprising forming a cap layer over the features after the chemical-mechanically polishing.

8. The method, as recited in claim 2 , wherein the anneal time is between 5 and 15 minutes.

9. The method, as recited in claim 1 further comprising forming the at least one liner in the features before providing the simultaneous electroless copper plating and anneal.

10. The method, as recited in claim 9 , wherein the at least one liner comprises a barrier layer.

11. The method, as recited in claim 9 , wherein the at least one liner comprises a seed layer.

12. The method, as recited in claim 1 , wherein the anneal time of exposure to the copper deposition bath is between 5 and 15 minutes.

13. A method for providing copper filled features, comprising:

providing features in a layer on a substrate and forming at least one liner in the features composed of metal;

providing a simultaneous electroless copper plating and anneal, which fills the features with copper deposit, wherein the simultaneous electroless copper plating and anneal occurs in an electroless copper bath that is maintained at an anneal temperature and for an anneal time sufficient to perform the electroless copper plating and annealing simultaneously, such that the features are filled without the formation of voids or seams, wherein the providing a simultaneous electroless copper plating and anneal comprises:

providing a copper deposition bath comprising one or more solvents having boiling points above the boiling point of water;

maintaining a temperature of the copper deposition bath at the anneal temperature; and

exposing the etched features to the copper deposition bath for the anneal time, wherein the anneal temperature of the copper deposition bath is between 150° C. and 250° C.; and

chemical-mechanical polishing the copper deposit without an annealing after the simultaneous electroless copper plating and anneal and before the chemical-mechanical polishing; and

removing the metal from a bevel of the substrate after providing the features in a layer on the substrate and before providing the simultaneous electroless copper plating and anneal.