Low density polyolefin resins with low molecular weight and high molecular weight components, and films made therefrom
Disclosed herein are ethylene-based polymers produced using dual metallocene catalyst systems. These polymers have low densities, high molecular weights, and broad molecular weight distributions, as well as having the majority of the long chain branches in the lower molecular weight component of the polymer, and the majority of the short chain branches in the higher molecular weight component of the polymer. Films produced from these polymers have improved impact and puncture resistance.
1. An ethylene polymer composition comprising a higher molecular weight component and a lower molecular weight component, wherein:
a ratio of the Mp of the higher molecular weight component to the Mp of the lower molecular weight component is in a range from about 5:1 to about 100:1;
a number of LCB of the lower molecular weight component is in a range from about 5 to about 50 LCB per million total carbon atoms; and
a number of LCB of the higher molecular weight component is less than or equal to about 5 LCB per million total carbon atoms.
2. The polymer composition of claim 1 , wherein:
the lower molecular weight component has a Mp in a range from about 15 to about 80 kg/mol;
the higher molecular weight component has a Mp in a range from about 150 to about 800 kg/mol;
a ratio of the number of LCB of the ethylene polymer composition to the number of LCB of the higher molecular weight component, per millions total carbon atoms, is in a range from about 2:1 to about 100:1; and
a number of LCB of the ethylene polymer composition is in a range from about 2 to about 30 LCB per million total carbon atoms.
3. The polymer composition of claim 1 , wherein the amount of the higher molecular weight component, based on the weight of the ethylene polymer composition, is in a range from about 10 to about 60 area %.
4. The polymer composition of claim 1 , wherein the polymer composition has:
a melt index of less than or equal to about 0.4 g/10 min;
a high load melt index in a range from about 4 to about 30 g/10 min; and
a density in a range from about 0.915 to about 0.935 g/cm 3 .
5. The polymer composition of claim 4 , wherein the polymer composition has:
a ratio of Mw/Mn in a range from about 8 to about 35;
a ratio of Mz/Mw in a range from about 3 to about 6;
a Mw in a range from about 120 to about 500 kg/mol;
a Mn in a range from about 10 to about 50 kg/mol; or any combination thereof.
6. The polymer composition of claim 1 , wherein the polymer composition has:
a zero-shear viscosity at 190° C. in a range from about 10,000 to about 500,000 Pa-sec;
a CY-a parameter at 190° C. in a range from about 0.20 to about 0.45; and
a Tau(η) parameter at 190° C. in a range from about 0.2 to about 2 sec.
7. The polymer composition of claim 1 , wherein the polymer composition is an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, or an ethylene/1-octene copolymer.
8. The polymer composition of claim 7 , wherein the polymer composition has a reverse comonomer distribution.
9. An article comprising the polymer composition of claim 8 .
10. A film comprising the polymer composition of claim 8 .
11. A blown film comprising the polymer composition of claim 1 .
12. The film of claim 11 , wherein the film has a dart impact strength greater than or equal to about 300 g/mil.
13. The film of claim 12 , wherein the polymer composition comprises an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, an ethylene/1-octene copolymer, or a combination thereof, and is characterized by:
a reverse comonomer distribution;
a density in a range from about 0.915 to about 0.935 g/cm 3 ; and
a ratio of Mw/Mn in a range from about 8 to about 35.
14. The film of claim 12 , wherein the film has:
a dart impact strength in a range from about 400 to about 2000 g/mil;
a haze of greater than or equal to about 55%;
a MD shrink at 250° F. in a range from about 20 to about 70%;
a MD Elmendorf tear strength in a range from about 10 to about 150 g/mil; and
a kinetic COF in a range from about 0.3 to about 0.5.
15. The polymer composition of claim 1 , wherein the polymer composition has:
a density in a range from about 0.913 to about 0.93 g/cm 3 ;
a ratio of Mw/Mn in a range from about 6 to about 20; and
a Mn in a range from about 10 to about 25 kg/mol.
16. An article comprising the polymer composition of claim 15 .
17. A blown film comprising the polymer composition of claim 15 , wherein the film has a dart impact strength greater than or equal to about 300 g/mil.
18. The polymer composition of claim 15 , wherein the polymer composition is an ethylene/α-olefin copolymer characterized by:
a reverse comonomer distribution; and
a high load melt index in a range from about 3 to about 60 g/10 min.
19. The polymer composition of claim 18 , wherein:
the ratio of the Mp of the higher molecular weight component to the Mp of the lower molecular weight component is in a range from about 7:1 to about 20:1;
the number of LCB of the lower molecular weight component is in a range from about 5 to about 15 LCB per million total carbon atoms; and
the number of LCB of the higher molecular weight component is less than or equal to about 3 LCB per million total carbon atoms.
20. An article comprising the polymer composition of claim 19 .
21. A blown film comprising the polymer composition of claim 19 , wherein the film has a dart impact strength in a range from about 400 to about 2000 g/mil.