Rigid polyurethane foam having excellent insulating properties and method for preparing the same
The present invention provides rigid polyurethane foam comprising thermally expandable particles which are displaced to penetrate a strut of a structure of the polyurethane foam so that the particles are exposed into one or more cells of the polyurethane foam during foaming. Further, the rigid polyurethane foam can comprise hollow thermally expanded particles which are displaced to penetrate a surface of a cell in the polyurethane foam so that the particles are exposed into one or more cells of the polyurethane foam during foaming. The rigid polyurethane of the present invention can have excellent insulating properties.
1. Rigid polyurethane foam comprising thermally expanded particles which are displaced during foaming to penetrate a strut of a structure of the polyurethane foam so that the particles are exposed into one or more cells of the polyurethane foam, wherein the rigid polyurethane foam comprises said thermally expanded particles in an amount of about 0.5 to about 10 parts by weight per 100 parts by weight of urethane resin forming the polyurethane foam, and wherein the mean diameter of the cells of the polyurethane foam is about 100 to about 350 μm.
2. The rigid polyurethane foam of claim 1 , wherein the thermally expanded particles comprise hollow thermally expanded particles which are displaced during foaming to penetrate a surface of a cell in the polyurethane foam so that the particles are exposed into one or more cells of the polyurethane foam.
3. The rigid polyurethane foam of claim 1 , wherein the cells of the polyurethane foam are formed by foaming a non-encapsulated blowing agent.
4. The rigid polyurethane foam of claim 3 , wherein the weight ratio between the non-encapsulated blowing agent and the thermally expanded particles is about 1:0.2 to about 1:2.
5. The rigid polyurethane foam of claim 1 , wherein the mean volume diameter of the thermally expanded particles before being foamed is about 5 to about 40 μm.
6. The rigid polyurethane foam of claim 1 , wherein the thermally expanded particles are derived from thermally expandable polymer particles containing an encapsulated hydrocarbon based foaming agent, wherein the boiling point of the hydrocarbon based foaming agent is about −10 to about 50° C. and wherein the glass transition temperature (Tg) of the polymer particles is about 40 to about 100° C.
7. The rigid polyurethane foam of claim 6 , wherein the expansion starting temperature (Tstart) of the thermally expandable particles is 50 to 110° C. and the maximum expansion temperature (Tmax) of the thermally expandable particles is 60 to 140° C.
8. The rigid polyurethane foam of claim 7 , wherein the maximum expansion temperature (Tmax) of the thermally expandable particles is 70 to 120° C.
9. The rigid polyurethane foam of claim 3 , wherein the non-encapsulated blowing agent comprises a hydrocarbon based foaming agent, a physical blowing agent, a chemical blowing agent, or a mixture of two or more thereof.
10. The rigid polyurethane foam of claim 9 , wherein the non-encapsulated blowing agent comprises iso-pentane, cyclopentane, normal pentane, methylene chloride, hexane, acetone, water, or a mixture thereof.
11. A method for preparing a rigid polyurethane foam, comprising:
dispersing thermally expandable particles in a polyol mixture including a dispersing agent, a catalyst and water;
adding a non-encapsulated blowing agent to the polyol mixture including the thermally expandable particles dispersed therein; and
reacting isocyanate and the polyol mixture including the thermally expandable particles and the non-encapsulated blowing agent to form a rigid polyurethane foam,
wherein the thermally expandable particles are displaced during foaming to penetrate a strut of a structure of the polyurethane foam so that the particles are exposed into one or more cells of the polyurethane foam,
wherein the amount of the thermally expandable particles is about 0.5 to about 10 parts by weight per 100 parts by weight of the urethane resin,
wherein the mixture weight ratio between the non-encapsulated blowing agent and the thermally expandable particles is about 1:0.2 to about 1:2, and
wherein the mean diameter of the cells of the polyurethane foam is about 100 to about 350 μm.
12. The method for preparing a rigid polyurethane foam of claim 11 , wherein the mean volume diameter of the thermally expandable particles before being foamed is about 5 to about 40 μm.
13. The method for preparing a rigid polyurethane foam of claim 11 , wherein the thermally expandable particles are polymer particles including an encapsulated hydrocarbon based foaming agent, wherein the boiling point of the hydrocarbon based foaming agent is about −10 to about 50° C. and wherein the glass transition temperature (Tg) of the polymer particles is about 40 to about 100° C.
14. The method for preparing a rigid polyurethane foam of claim 11 , wherein the non-encapsulated blowing agent comprises a hydrocarbon foaming agent, a physical blowing agent, a chemical blowing agent, or a mixture of two or more thereof.
15. The method for preparing a rigid polyurethane foam of claim 14 , wherein the non-encapsulated blowing agent comprises iso-pentane, cyclopentane, normal pentane, methylene chloride, hexane, acetone, water, or a mixture thereof.
16. The method for preparing a rigid polyurethane foam of claim 15 , wherein the non-encapsulated blowing agent comprises iso-pentane, cyclopentane, normal pentane, methylene or a mixture thereof.
17. An insulating material for a refrigerator comprising the rigid polyurethane foam of claim 1 .
18. The rigid polyurethane foam of claim 1 , wherein the rigid polyurethane foam comprises said thermally expanded particles in an amount of about 0.5 to about 9 parts by weight per 100 parts by weight of urethane resin forming the polyurethane foam.
19. The rigid polyurethane foam of claim 1 , wherein the rigid polyurethane foam comprises said thermally expanded particles in an amount of about 0.5 to about 7 parts by weight per 100 parts by weight of urethane resin forming the polyurethane foam.
20. The rigid polyurethane foam of claim 1 , wherein the rigid polyurethane foam comprises said thermally expanded particles in an amount of about 0.5 to about 5 parts by weight per 100 parts by weight of urethane resin forming the polyurethane foam.
21. The rigid polyurethane foam of claim 1 , wherein the mean diameter of the cells of the polyurethane foam is about 250 to about 325 μm.
22. The rigid polyurethane foam of claim 1 , wherein the rigid polyurethane foam has a K-factor of about 150 to about 170 10 −4 kcal/m·h·° C.
23. The rigid polyurethane foam of claim 1 , wherein the rigid polyurethane foam comprises said thermally expanded particles in an amount of about 2 to about 8 parts by weight per 100 parts by weight of urethane resin forming the polyurethane foam.