Titanium-aluminum alloy deposition with titanium-tetrahydroaluminate bimetallic molecules

Inventors: Julien Gatineau (Tsuchiura, JP); Satoko Gatineau (Tsuchiura, JP); Jean-Marc Girard (Tokyo, JP); Changhee Ko (Tsukuba, JP)
Assignee: L'Air Liquide, Société Anonyme pour l'Etude et l'Exploitation des Procédés Georges Claude
C07F19/005C07F5/06
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 9,187,511
App. No.
13/780,212
Granted
Nov 17, 2015
Kind
B2
Abstract

Disclosed are titanium-tetrahydroaluminates precursors, their method of manufacture, and their use in the deposition of titanium-aluminum-containing films. The disclosed precursors have the formulae Ti(AlH 4 ) 3 —X, Ti(AlH 4 ) 2 L and Ti(AlH 4 )L 2 . The disclosed precursors may be used to deposit pure titanium-aluminum (TiAl), titanium-aluminum nitride (TiAlN), titanium-aluminum carbide (TiAlC), titanium-aluminum carbonitride (TiAlCN), titanium-aluminum silicide ((TiAl)Si), titanium-aluminum siliconitride ((TiAl)SiN), titanium-aluminum boron ((TiAl)B), titanium-aluminum boron nitride ((TiAl)BN), or titanium-aluminum oxide (TiAlO). or any other titanium-aluminum-containing films. The titanium-aluminum-containing films may be deposited using the disclosed precursors in thermal and/or plasma-enhanced CVD, ALD, pulse CVD or any other type of depositions methods.

Claims (29)

1. A method of depositing a titanium-aluminum containing film, the method comprising:

introducing at least one titanium-tetrahydroaluminate precursor into a reactor having at least one substrate disposed therein, the at least one titanium-tetrahydroaluminate precursor being selected from the group consisting of:

(i) Ti(AlH 4 ) 3 —X n

wherein

0<n≦2; and

X is selected among:

compounds of N, P, As, Sb or Bi in oxidation state 3;

compounds of O, S, Se or Te in oxidation state 2;

carbon monoxide, aromatic hydrocarbons, or dichloromethane;

(ii) Ti(AlH 4 ) 2 L, wherein L is selected from the group consisting of pentadienyl, cyclopentadienyl, hexadienyl, cyclohexadienyl, allyl, diimine (DAD), N-heterocyclic carbenes (NHCs), amidinate, silyl-amidinate, formamidinate, dialkylethylenediamine (R1N—CH 2 —CH 2 —NR2), dialkylaminoalkylborane (R1N—BR2-NR3), dialkylaminoalkylalane (R1N—AlR2-NR3), dialkylaminoalkylgallium (R1N—GaR2-NR3), β-acetylacetonate, β-diketonate, β-diketimine, and pyrrolecarbaldiminate;

(iii) Ti(AlH 4 )L 1 L 2 , wherein each of L 1 and L 2 is independently selected from the group consisting of pentadienyl, cyclopentadienyl, hexadienyl, cyclohexadienyl, allyl, diimine (DAD), N-heterocyclic carbenes (NHCs), amidinate, silyl-amidinate, formamidinate, dialkylethylenediamine (R1N—CH 2 —CH 2 —NR2), dialkylaminoalkylborane (R1N—BR2-NR3), dialkylaminoalkylalane (R1N—AlR2-NR3), dialkylaminoalkylgallium (R1N—GaR2-NR3), β-acetylacetonate, β-diketonate, β-diketimine, and pyrrolecarbaldiminate, wherein L 1 and L 2 do not both equal non-substituted cyclopentadienyl ligands;

depositing at least part of the titanium-tetrahydroaluminate precursor onto the at least one substrate to form the titanium-aluminum containing film.

2. The method of claim 1 , wherein the titanium-tetrahydroaluminate precursor of formula (i) is selected from the group consisting of Ti(AlH 4 ) 3 -(methanol) n , Ti(AlH 4 ) 3 -(ethanol) n , Ti(AlH 4 ) 3 -(n-propanol) n , Ti(AlH 4 ) 3 -(i-propanol) n , Ti(AlH 4 ) 3 -(ethylene oxide) n , Ti(AlH 4 ) 3 -(dimethylether) n , Ti(AlH 4 ) 3 -(diethylether) n , Ti(AlH 4 ) 3 -(dimethoxymethane) n , Ti(AlH 4 ) 3 -(dimethoxyethane) n , Ti(AlH 4 ) 3 -(acetone) n , Ti(AlH 4 ) 3 -(THF) n , Ti(AlH 4 ) 3 -(methyl-THF) n , Ti(AlH 4 ) 3 -(benzene) n , Ti(AlH 4 ) 3 -(toluene) n , Ti(AlH 4 ) 3 -(mesytylene) n , Ti(AlH 4 ) 3 -(methoxybenzene) n , Ti(AlH 4 ) 3 -(dimethoxybenzene) n , Ti(AlH 4 ) 3 -(diglyme) n , Ti(AlH 4 ) 3 -(triglyme) n , Ti(AlH 4 ) 3 -(tetraglyme) n , Ti(AlH 4 ) 3 -(pyridine) n , Ti(AlH 4 ) 3 -(1-methylpyridine) n , Ti(AlH 4 ) 3 -(2-methylpyridine) n , Ti(AlH 4 ) 3 -(3-methylpyridine) n , Ti(AlH4) 3 -(bipyridine) n , Ti(AlH 4 ) 3 -(pyridazine) n , Ti(AlH 4 ) 3 -(pyrimidine) n , Ti(AlH 4 ) 3 -(pyrazine) n , Ti(AlH 4 ) 3 -(Me 3 N) n , Ti(AlH 4 ) 3 -(tBuMe 2 N) n , Ti(AlH 4 ) 3 -(Et 3 N) n , Ti(AlH 4 ) 3 -(nPr 3 N) n , Ti(AlH 4 ) 3 -(iPr 3 N) n , Ti(AlH 4 ) 3 -(Me 2 NH) n , Ti(AlH 4 ) 3 -(Et 2 NH) n , Ti(AlH 4 ) 3 -(iPr 2 NH) n , Ti(AlH 4 ) 3 -(nPr 2 NH) n , Ti(AlH 4 ) 3 -(MeNH 2 ) n , Ti(AlH 4 ) 3 -(EtNH 2 ) n , Ti(AlH 4 ) 3 -(nPrNH 2 ) n , Ti(AlH 4 ) 3 -(iPrNH 2 ) n , Ti(AlH 4 ) 3 -(Me 3 P) n , Ti(AlH 4 ) 3 -(tBuMe 2 P) n , Ti(AlH 4 ) 3 -(Et 3 P) n , Ti(AlH 4 ) 3 -(nPr 3 P) n , Ti(AlH 4 ) 3 -(iPr 3 P) n , Ti(AlH 4 ) 3 -(Me 2 PH) n , Ti(AlH 4 ) 3 -(Et 2 PH) n , Ti(AlH 4 ) 3 -(iPr 2 PH) n , Ti(AlH 4 ) 3 -(nPr 2 PH) n , Ti(AlH 4 ) 3 -(MePH 2 ) n , Ti(AlH 4 ) 3 -(EtPH 2 ) n , Ti(AlH 4 ) 3 -(nPrPH 2 ) n , Ti(AlH 4 ) 3 -(iPrPH 2 ) n , Ti(AlH 4 ) 3 -(Me 3 As) n , Ti(AlH 4 ) 3 -(tBuMe 2 As) n , Ti(AlH 4 ) 3 -(Et 3 As) n , Ti(AlH 4 ) 3 -(nPr 3 As) n , Ti(AlH 4 ) 3 -(iPr 3 As) n , Ti(AlH 4 ) 3 -(Me 2 AsH) n , Ti(AlH 4 ) 3 -(Et 2 AsH) n , Ti(AlH 4 ) 3 -(iPr 2 AsH) n , Ti(AlH 4 ) 3 -(nPr 2 AsH) n , Ti(AlH 4 ) 3 -(MeAsH 2 ) n , Ti(AlH 4 ) 3 -(EtAsH 2 ) n , Ti(AlH 4 ) 3 -(nPrAsH 2 ) n , and Ti(AlH 4 ) 3 -(iPrAsH 2 ) n .

3. The method of claim 1 , wherein the titanium-tetrahydroaluminate precursor of formula (ii) is selected from the group consisting of Ti(AlH 4 ) 2 (H 2 -DAD)), Ti(AlH 4 ) 2 (Me 2 -DAD), Ti(AlH 4 ) 2 (Et 2 -DAD), Ti(AlH 4 ) 2 (iPr 2 -DAD), Ti(AlH 4 ) 2 (nPr 2 -DAD), Ti(AlH 4 ) 2 (nBu 2 -DAD), Ti(AlH 4 ) 2 (sBu 2 -DAD), Ti(AlH 4 ) 2 (iBu 2 -DAD), Ti(AlH 4 ) 2 (tBu 2 -DAD), Ti(AlH 4 ) 2 (iPr 2 -MDAD), Ti(AlH 4 ) 2 (Me 2 -DMDAD), Ti(AlH 4 ) 2 (iPr 2 -DMDAD), Ti(AlH 4 ) 2 (H 2 -fAM), Ti(AlH 4 ) 2 (Me 2 -fAMD), Ti(AlH 4 ) 2 (Et 2 -fAMD), Ti(AlH 4 ) 2 (iPr 2 -fAMD), Ti(AlH 4 ) 2 (nPr 2 -fAMD), Ti(AlH 4 ) 2 (nBu 2 -fAMD), Ti(AlH 4 ) 2 (iBu 2 -fAMD), Ti(AlH 4 ) 2 (tBu 2 -fAMD), Ti(AlH 4 ) 2 (sBu 2 -fAMD), Ti(AlH 4 ) 2 (H 2 -AMD), Ti(AlH 4 ) 2 (Me 2 -AMD), Ti(AlH 4 ) 2 (Et 2 -AMD), Ti(AlH 4 ) 2 (iPr 2 -AMD), Ti(AlH 4 ) 2 (nPr 2 -AMD), Ti(AlH 4 ) 2 (tBu 2 -AMD), Ti(AlH 4 ) 2 (nBu 2 -AMD), Ti(AlH 4 ) 2 (sBu 2 -AMD), Ti(AlH 4 ) 2 (iBu 2 -AMD), Ti(AlH 4 ) 2 (H 2 —SiAMD), Ti(AlH 4 ) 2 (Me 2 -SiAMD), Ti(AlH 4 ) 2 (Et 2 -SiAMD), Ti(AlH 4 ) 2 (iPr 2 —SiAMD), Ti(AlH 4 ) 2 (nPr 2 —SiAMD), Ti(AlH 4 ) 2 (tBu 2 -SiAMD), Ti(AlH 4 ) 2 (nBu 2 -SiAMD), Ti(AlH 4 ) 2 (sBu 2 -SiAMD), Ti(AlH 4 ) 2 (iBu 2 -SiAMD), Ti(AlH 4 ) 2 (H 2 -NacNac), Ti(AlH 4 ) 2 (Me 2 -NacNac), Ti(AlH 4 ) 2 (Et 2 -NacNac), Ti(AlH 4 ) 2 (iPr 2 -NacNac), Ti(AlH 4 ) 2 (nPr 2 -NacNac), Ti(AlH 4 ) 2 (tBu 2 -NacNac), Ti(AlH 4 ) 2 (nBu 2 -NacNac), Ti(AlH 4 ) 2 (sBu 2 -NacNac), Ti(AlH 4 ) 2 (iBu 2 -NacNac), Ti(AlH 4 ) 2 (H-acNac), Ti(AlH 4 ) 2 (Me-acNac), Ti(AlH 4 ) 2 (Et-acNac), Ti(AlH 4 ) 2 (iPr-acNac), Ti(AlH 4 ) 2 (nPr-acNac), Ti(AlH 4 ) 2 (tBu-acNac), Ti(AlH 4 ) 2 (nBu-acNac), Ti(AlH 4 ) 2 (sBu-acNac), Ti(AlH 4 ) 2 (iBu-acNac), Ti(AlH 4 ) 2 (acac), Ti(AlH 4 ) 2 Cp, Ti(AlH 4 ) 2 (Me-Cp), Ti(AlH 4 ) 2 (Et-Cp), Ti(AlH 4 ) 2 (iPr-Cp), Ti(AlH 4 ) 2 (Me 3 -Cp), Ti(AlH 4 ) 2 (Me 4 -Cp), Ti(AlH 4 ) 2 (Me 5 -Cp), Ti(AlH 4 ) 2 (iPr 3 -Cp), Ti(AlH 4 ) 2 (tBu 3 -Cp), Ti(AlH 4 ) 2 Op, Ti(AlH 4 ) 2 (Me-Op), Ti(AlH 4 ) 2 (Et-Op), Ti(AlH 4 ) 2 (iPr-Op), Ti(AlH 4 ) 2 (Me 3 -Op), Ti(AlH 4 ) 2 (Me 4 -Op), Ti(AlH 4 ) 2 (Me 5 -Op), Ti(AlH 4 ) 2 (iPr 3 -Op), Ti(AlH 4 ) 2 (tBu 3 -Op), Ti(AlH 4 ) 2 (CHDI), Ti(AlH 4 ) 2 (Me-CHDI), Ti(AlH 4 ) 2 (Et-CHDI), Ti(AlH 4 ) 2 (iPr-CHDI), Ti(AlH 4 ) 2 (Me 3 -CHDI), Ti(AlH 4 ) 2 (Me 4 CHDI), Ti(AlH 4 ) 2 (Me 5 -CHDI), Ti(AlH 4 ) 2 (iPr 3 -CHDI), Ti(AlH 4 ) 2 (tBu 3 -CHDI), Ti(AlH 4 ) 2 (HDI), Ti(AlH 4 ) 2 (Me-HDI), Ti(AlH 4 ) 2 (Et-HDI), Ti(AlH 4 ) 2 (iPr-HDI), Ti(AlH 4 ) 2 (Me 3 -HDI), Ti(AlH 4 ) 2 (Me 4 -HDI), Ti(AlH 4 ) 2 (Me 5 -HDI), Ti(AlH 4 ) 2 (iPr 3 -HDI), Ti(AlH 4 ) 2 (tBu 3 HDI), Ti(AlH 4 ) 2 (allyl), Ti(AlH 4 ) 2 (Me-allyl), Ti(AlH 4 ) 2 (Et-allyl), Ti(AlH 4 ) 2 (iPr-allyl), Ti(AlH 4 ) 2 (Me 2 -allyl), Ti(AlH 4 ) 2 (Me 3 -allyl), Ti(AlH 4 ) 2 (Me 2 -DAAB), Ti(AlH 4 ) 2 (Et 2 -DAAB), Ti(AlH 4 ) 2 (iPr 2 -DAAB), Ti(AlH 4 ) 2 (nPr 2 -DAAB), Ti(AlH 4 ) 2 (tBu 2 -DAAB), Ti(AlH 4 ) 2 (nBu 2 -DAAB), Ti(AlH 4 ) 2 (sBu 2 -DAAB), Ti(AlH 4 ) 2 (iBu 2 -DAAB), Ti(AlH 4 ) 2 (MeEt-DAAB), Ti(AlH 4 ) 2 (Me 2 -DAAA), Ti(AlH 4 ) 2 (Et 2 -DAAA), Ti(AlH 4 ) 2 (iPr 2 -DAAA), Ti(AlH 4 ) 2 (nPr 2 -DAAA), Ti(AlH 4 ) 2 (tBu 2 -DAAA), Ti(AlH 4 ) 2 (nBu 2 -DAAA), Ti(AlH 4 ) 2 (sBu 2 -DAAA), Ti(AlH 4 ) 2 (iBu 2 -DAAA), Ti(AlH 4 ) 2 (MeEt-DAAA), Ti(AlH 4 ) 2 (Me 2 -DAAG), Ti(AlH 4 ) 2 (Et 2 -DAAG), Ti(AlH 4 ) 2 (iPr 2 -DAAG), Ti(AlH 4 ) 2 (nPr 2 -DAAG), Ti(AlH 4 ) 2 (tBu 2 -DAAG), Ti(AlH 4 ) 2 (nBu 2 -DAAG), Ti(AlH 4 ) 2 (sBu 2 -DAAG), Ti(AlH 4 ) 2 (iBu 2 -DAAG), Ti(AlH 4 ) 2 (MeEt-DAAG), Ti(AlH 4 ) 2 (Me 2 -EDA), Ti(AlH 4 ) 2 (Et 2 -EDA), Ti(AlH 4 ) 2 (iPr 2 -EDA), Ti(AlH 4 ) 2 (nPr 2 -EDA), Ti(AlH 4 ) 2 (nBu 2 -EDA), Ti(AlH 4 ) 2 (tBu 2 -EDA), Ti(AlH 4 ) 2 (sBu 2 -EDA), Ti(AlH 4 ) 2 (iBu 2 -EDA), Ti(AlH 4 ) 2 (MeEt-EDA), Ti(AlH 4 ) 2 (Me-PCAI), Ti(AlH 4 ) 2 (Et-PCAI), Ti(AlH 4 ) 2 (iPr-PCAI), Ti(AlH 4 ) 2 (Me 2 -NHCs), Ti(AlH 4 ) 2 (Et 2 -NHCs), Ti(AlH 4 ) 2 (nPr 2 -NHCs), Ti(AlH 4 ) 2 (iPr 2 -NHCs), Ti(AlH 4 ) 2 (nBu 2 -NHCs), Ti(AlH 4 ) 2 (tBu 2 -NHCs), Ti(AlH 4 ) 2 (TMS 2 —NHCs), and Ti(AlH 4 ) 2 (Me 2 -Me 2 NHCs).

4. The method of claim 1 , wherein the titanium-tetrahydroaluminate precursor of formula (iii) is selected from the group consisting of Ti(AlH 4 )(H 2 -DAD) 2 , Ti(AlH 4 )(Me 2 -DAD) 2 , Ti(AlH 4 )(Et 2 -DAD) 2 , Ti(AlH 4 )(iPr 2 -DAD) 2 , Ti(AlH 4 )(nPr 2 -DAD) 2 , Ti(AlH 4 )(nBu 2 -DAD) 2 , Ti(AlH 4 )(sBu 2 -DAD) 2 , Ti(AlH 4 )(iBu 2 -DAD) 2 , Ti(AlH 4 )(tBu 2 -DAD) 2 , Ti(AlH 4 )(iPr 2 -MDAD) 2 , Ti(AlH 4 )(Me 2 -DMDAD) 2 , Ti(AlH 4 )(iPr 2 -DMDAD) 2 , Ti(AlH 4 )(H 2 -fAMD) 2 , Ti(AlH 4 )(Me 2 -fAMD) 2 , Ti(AlH 4 )(Et 2 -fAMD) 2 , Ti(AlH 4 )(iPr 2 -fAMD) 2 , Ti(AlH 4 )(nPr 2 -fAMD) 2 , Ti(AlH 4 )(nBu 2 -fAMD) 2 , Ti(AlH 4 )(iBu 2 -fAMD) 2 , Ti(AlH 4 )(tBu 2 -fAMD) 2 , Ti(AlH 4 )(sBu 2 -fAMD) 2 , Ti(AlH 4 )(H 2 -AMD) 2 , Ti(AlH 4 )(Me 2 -AMD) 2 , Ti(AlH 4 )(Et 2 -AMD) 2 , Ti(AlH 4 )(iPr 2 -AMD) 2 , Ti(AlH 4 )(nPr 2 -AMD) 2 , Ti(AlH 4 )(tBu 2 -AMD) 2 , Ti(AlH 4 )(nBu 2 -AMD) 2 , Ti(AlH 4 )(sBu 2 -AMD) 2 , Ti(AlH 4 )(iBu 2 -AMD) 2 , Ti(AlH 4 )(H 2 —SiAMD) 2 , Ti(AlH 4 )(Me 2 -SIAMD) 2 , Ti(AlH 4 )(Et 2 -SiAMD) 2 , Ti(AlH 4 )(iPr 2 —SiAMD) 2 , Ti(AlH 4 )(nPr 2 —SiAMd) 2 , Ti(AlH 4 )(tBu 2 -SiAMD) 2 , Ti(AlH 4 )(nBu 2 -SiAMD) 2 , Ti(AlH 4 )(sBu 2 -SiAMD) 2 , Ti(AlH 4 )(iBu 2 -SiAMD) 2 , Ti(AlH 4 )(H 2 -NacNac) 2 , Ti(AlH 4 )(Me 2 -NacNac) 2 , Ti(AlH 4 )(Et 2 -NacNac) 2 , Ti(AlH 4 )(iPr 2 -NacNac) 2 , Ti(AlH 4 )(nPr 2 -NacNac) 2 , Ti(AlH 4 )(tBu 2 -NacNac) 2 , Ti(AlH 4 )(nBu 2 -NacNac) 2 , Ti(AlH 4 )(sBu 2 -NacNac) 2 , Ti(AlH 4 )(iBu 2 -NacNac) 2 , Ti(AlH 4 )(H-acNac) 2 , Ti(AlH 4 )(Me-acNac) 2 , Ti(AlH 4 )(Et-acNac) 2 , Ti(AlH 4 )(iPr-acNac) 2 , Ti(AlH 4 )(nPr-acNac) 2 , Ti(AlH 4 )(tBu-acNac) 2 , Ti(AlH 4 )(nBu-acNac) 2 , Ti(AlH 4 )(sBu-acNac) 2 , Ti(AlH 4 )(iBu-acNac) 2 , Ti(AlH 4 )(acac) 2 , Ti(AlH 4 )Cp 2 , Ti(AlH 4 )(Me-Cp) 2 , Ti(AlH 4 )(Et-Cp) 2 , Ti(AlH 4 )(iPr-Cp) 2 , Ti(AlH 4 )(Me 3 -Cp) 2 , Ti(AlH 4 )(Me 4 -Cp) 2 , Ti(AlH 4 )(Me 5 -Cp) 2 , Ti(AlH 4 )(iPr 3 -Cp) 2 , Ti(AlH 4 )(tBu 3 -Cp) 2 , Ti(AlH 4 )Op 2 , Ti(AlH 4 )(Me-Op) 2 , Ti(AlH 4 )(Et-Op) 2 , Ti(AlH 4 )(iPr-Op) 2 , Ti(AlH 4 )(Me 3 -Op) 2 , Ti(AlH 4 )(Me 4 -Op) 2 , Ti(AlH 4 )(Me 5 -Op) 2 , Ti(AlH 4 )(iPr 3 -Op) 2 , Ti(AlH 4 )(tBu 3 -Op) 2 , Ti(AlH 4 )(CHDI) 2 , Ti(AlH 4 )(Me-CHDI) 2 , Ti(AlH 4 )(Et-CHDI) 2 , Ti(AlH 4 )(iPr-CHDI) 2 , Ti(AlH 4 )(Me 3 -CHDI) 2 , Ti(AlH 4 )(Me 4 -CHDI) 2 , Ti(AlH 4 )(Me 5 -CHDI) 2 , Ti(AlH 4 )(iPr 3 -CHDI) 2 , Ti(AlH 4 )(tBu 3 -CHDI) 2 , Ti(AlH 4 )(HDI) 2 , Ti(AlH 4 )(Me-HDI) 2 , Ti(AlH 4 )(Et-HDI) 2 , Ti(AlH 4 )(iPr-HDI) 2 , Ti(AlH 4 )(Me 3 -HDI) 2 , Ti(AlH 4 )(Me 4 -HDI) 2 , Ti(AlH 4 )(Me 5 -HDI) 2 , Ti(AlH 4 )(iPr 3 -HDI) 2 , Ti(AlH 4 )(tBu 3 -HDI) 2 , Ti(AlH 4 )(allyl) 2 , Ti(AlH 4 )(Me-allyl) 2 , Ti(AlH 4 )(Et-allyl) 2 , Ti(AlH 4 )(iPr-allyl) 2 , Ti(AlH 4 )(Me 2 -allyl) 2 , Ti(AlH 4 )(Me 3 -allyl) 2 , Ti(AlH 4 )(Me 2 -DAAB) 2 , Ti(AlH 4 )(Et 2 -DAAB) 2 , Ti(AlH 4 )(iPr 2 -DAAB) 2 , Ti(AlH 4 )(nPr 2 -DAAB) 2 , Ti(AlH 4 )(tBu 2 -DAAB) 2 , Ti(AlH 4 )(nBu 2 -DAAB) 2 , Ti(AlH 4 )(sBu 2 -DAAB) 2 , Ti(AlH 4 )(iBu 2 -DAAB) 2 , Ti(AlH 4 )(MeEt-DAAB) 2 , Ti(AlH 4 )(Me 2 -DAAA) 2 , Ti(AlH 4 )(Et 2 -DAAA) 2 , Ti(AlH 4 )(iPr 2 -DAAA) 2 , Ti(AlH 4 )(nPr 2 -DAAA) 2 , Ti(AlH 4 )(tBu 2 -DAAA) 2 , Ti(AlH 4 )(nBu 2 -DAAA) 2 , Ti(AlH 4 )(sBu 2 -DAAA) 2 , Ti(AlH 4 )(iBu 2 -DAAA) 2 , Ti(AlH 4 )(MeEt-DAAA) 2 , Ti(AlH 4 )(Me 2 -DAAG) 2 , Ti(AlH 4 )(Et 2 -DAAG) 2 , Ti(AlH 4 )(iPr 2 -DAAG) 2 , Ti(AlH 4 )(nPr 2 -DAAG) 2 , Ti(AlH 4 )(tBu 2 -DAAG) 2 , Ti(AlH 4 )(nBu 2 -DAAG) 2 , Ti(AlH 4 )(sBu 2 -DAAG) 2 , Ti(AlH 4 )(iBu 2 -DAAG) 2 , Ti(AlH 4 )(MeEt-DAAG) 2 , Ti(AlH 4 )(Me 2 -EDA) 2 , Ti(AlH 4 )(Et 2 -EDA) 2 , Ti(AlH 4 )(iPr 2 -EDA) 2 , Ti(AlH 4 )(nPr 2 -EDA) 2 , Ti(AlH 4 )(nBu 2 -EDA) 2 , Ti(AlH 4 )(tBu 2 -EDA) 2 , Ti(AlH 4 )(sBu 2 -EDA) 2 , Ti(AlH 4 )(iBu 2 -EDA) 2 , Ti(AlH 4 )(MeEt-EDA) 2 , Ti(AlH 4 )(Me-PCAI) 2 , Ti(AlH 4 )(Et-PCAI) 2 , Ti(AlH 4 )(iPr-PCAI) 2 , Ti(AlH 4 )(Me 2 -NHCs) 2 , Ti(AlH 4 )(Et 2 -NHCs) 2 , Ti(AlH 4 )(nPr 2 -NHCs) 2 , Ti(AlH 4 )(iPr 2 -NHCs) 2 , Ti(AlH 4 )(nBu 2 -NHCs) 2 , Ti(AlH 4 )(tBu 2 -NHCs) 2 , Ti(AlH 4 )(TMS 2 —NHCs) 2 , and Ti(AlH 4 )(Me 2 -Me 2 NHCs) 2 .

5. The method of claim 1 , wherein the method is performed at a temperature between about 20° C. and about 800° C.

6. The method of claim 1 , wherein the method is performed at a pressure between about 0.1 Pa and about 10 5 Pa.

7. The method of claim 1 , wherein the deposition method is selected from the group consisting of chemical vapor deposition (CVD), atomic layer deposition (ALD), plasma CVD, plasma ALD, pulse CVD, low pressure CVD, subatmospheric CVD, and atmospheric pressure CVD.

8. The method of claim 1 , wherein the titanium-aluminum containing film is selected from the group consisting of pure titanium-aluminum (TiAl), titanium-aluminum nitride (TiAlN), titanium-aluminum carbide (TiAlC), titanium-aluminum carbonitride (TiAlCN), titanium-aluminum silicide ((TiAl)Si), titanium-aluminum siliconitride ((TiAl)SiN), titanium-aluminum boron ((TiAl)B), titanium-aluminum boron nitride ((TiAl)BN), titanium-aluminum oxide (TiAlO), and titanium-aluminum nitroxide (TiAlNO).

9. The method of claim 1 , further comprising:

introducing a reaction gas into the reactor at the same time or at an alternate time as the introduction of the titanium-tetrahydroaluminate precursor;

wherein at least part of the titanium-tetrahydroaluminate precursor is deposited onto the at least one substrate to form the titanium-aluminum containing film by reacting the reaction gas with the titanium-tetrahydroaluminate precursor.

10. The method of claim 9 , wherein the reaction gas is a reducing agent.

11. The method of claim 10 , wherein the reducing agent is selected from the group consisting of: N 2 , H 2 ; SiH 4 ; Si 2 H 6 ; Si 3 H 8 ; NH 3 ; (CH 3 ) 2 SiH 2 ; (C 2 H 5 ) 2 SiH 2 ; (CH 3 )SiH 3 ; (C 2 H 5 )SiH 3 ; phenyl silane; N 2 H 4 ; N(SiH 3 ) 3 ; N(CH 3 )H 2 ; N(C 2 H 5 )H 2 ; N(CH 3 ) 2 H; N(C 2 H 5 ) 2 H; N(CH 3 ) 3 ; N(C 2 H 5 ) 3 ; (SiMe 3 ) 2 NH; (CH 3 )HNNH 2 ; (CH 3 ) 2 NNH 2 ; phenyl hydrazine; B 2 H 6 ; 9-borabicyclo[3,3,1]nonane; dihydrobenzenfuran; pyrazoline; trimethylaluminum; dimethylzinc; diethylzinc; radical species thereof; and mixtures thereof.

12. The method of claim 9 , wherein the reaction gas is an oxidizing agent.

13. The method of claim 12 , wherein the oxidizing agent is selected from the group consisting of: O 2 ; O 3 ; H 2 O; H 2 O 2 ; NO; NO 2 ; carboxylic acids; radical species thereof; and mixtures thereof.

14. The method of claim 4 , wherein the titanium-tetrahydroaluminate precursor of formula (iii) is selected from the group consisting of Ti(AlH 4 )Cp 2 , Ti(AlH 4 )(Me-Cp) 2 , Ti(AlH 4 )(Et-Cp) 2 , Ti(AlH 4 )(iPr-Cp) 2 , Ti(AlH 4 )(Me 3 -Cp) 2 , Ti(AlH 4 )(Me 4 -Cp) 2 , Ti(AlH 4 )(Me 5 -Cp) 2 , Ti(AlH 4 )(iPr 3 -Cp) 2 , and Ti(AlH 4 )(tBu 3 -Cp) 2 .

15. The method of claim 14 , wherein the reaction gas is a reducing agent.

16. The method of claim 15 , wherein the reducing agent is selected from the group consisting of: N 2 , H 2 ; SiH 4 ; Si 2 H 6 ; Si 3 H 8 ; NH 3 ; (CH 3 ) 2 SiH 2 ; (C 2 H 5 ) 2 SiH 2 ; (CH 3 )SiH 3 ; (C 2 H 5 )SiH 3 ; phenyl silane; N 2 H 4 ; N(SiH 3 ) 3 ; N(CH 3 )H 2 ; N(C 2 H 5 )H 2 ; N(CH 3 ) 2 H; N(C 2 H 5 ) 2 H; N(CH 3 ) 3 ; N(C 2 H 5 ) 3 ; (SiMe 3 ) 2 NH; (CH 3 )HNNH 2 ; (CH 3 ) 2 NNH 2 ; phenyl hydrazine; B 2 H 6 ; 9-borabicyclo[3,3,1]nonane; dihydrobenzenfuran; pyrazoline; trimethylaluminum; dimethylzinc; diethylzinc; radical species thereof; and mixtures thereof.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Apr 4, 2013
From: GATINEAU, JULIEN; GATINEAU, SATOKO; GIRARD, JEAN-MARC; KO, CHANGHEE
To: L'AIR LIQUIDE, SOCIETE ANONYME POUR L'ETUDE ET L'EXPLOITATION DES PROCEDES GEORGES CLAUDE
Reel/Frame 030155/0394 →
Continuity (2)
Provisional Application 61640954 · May 1, 2012
Related Publication 20130295298A1 · Nov 7, 2013