Method for producing glass substrate and method for producing magnetic recording medium
Disclosed is a method for producing a glass substrate, which involves a first polishing step and a second polishing step both for polishing the surface of the glass substrate with a polishing solution containing a polishing agent. The method is characterized by additionally involving a heating step for heating the glass substrate, wherein the heating step is carried out after the first polishing step and before the second polishing step.
1. A method for producing a glass substrate comprising successively:
polishing a surface of the glass substrate with a first polishing liquid containing a first polishing agent;
heating the glass substrate in a heating chamber at or between 100° C. to 300° C. to heat all of the glass substrate so as to dry the glass substrate; and
subsequent to the heating, polishing the surface of the glass substrate with a second polishing liquid containing a second polishing agent.
2. The method of claim 1 , wherein the polishing of the surface of the glass substrate with the second polishing liquid is performed just after the heating of the glass substrate.
3. The method of claim 1 further comprising, between the polishing of the surface of the glass substrate with the first polishing liquid and the heating of the glass substrate: cleaning the glass substrate; and drying the glass substrate.
4. The method of claim 3 , wherein the drying of the glass substrate comprises blowing, gas is against the glass substrate.
5. The method of claim 3 , wherein the polishing of the surface of the glass substrate with the second polishing liquid is performed before the glass substrate, heated via the heating the glass substrate, cools.
6. The method of claim 1 wherein the first and second polishing agents are the same.
7. The method of claim 6 wherein the second polishing agent has smaller diameter particles than the first polishing agent.
8. The method of claim 1 , wherein the polishing of the surface of the glass substrate with the second polishing liquid is performed before the glass substrate, heated via the heating the glass substrate, cools.
9. The method of claim 1 , wherein the heating of the glass substrate comprises heating the glass substrate for 5 to 30 minutes.
10. A method for producing a magnetic recording medium, the method comprising:
producing a glass substrate by performing the following processes successively:
polishing a surface of the glass substrate with a first polishing liquid containing a first polishing agent;
heating the glass substrate in a heating chamber at or between 100° C. to 300° C. to heat all of the glass substrate so as to dry the glass substrate; and
subsequent to the heating, polishing the surface of the glass substrate with a second polishing liquid containing a second polishing agent; and
forming a magnetic film on the glass substrate.
11. The method of claim 10 , wherein the heating of the glass substrate comprises heating the glass substrate for 5 to 30 minutes.