Toner, developer and image forming apparatus
A toner including: a binder resin containing a non-crystalline resin and a crystalline resin; a colorant; and, a releasing agent, wherein the releasing agent has a melting point of 55° C. to 80° C., and wherein the toner satisfies the following Expressions 1 and 2: (Expression 1): 20,000 Pa·s≦G 1 ≦50,000 Pa·s; and (Expression 2): (G 4 /G 2 )/(G 3 /G 1 ) 1.00, where G 1 is a storage modulus, G 2 is a loss modulus, G 3 is a storage modulus and G 4 is a loss modulus, and the storage modulus G 1 and the loss modulus G 2 are measured at 80° C. when the toner is heated from 70° C. to 150° C. and the storage modulus G 3 and the loss modulus G 4 are measured at 80° C. when the toner heated to 150° C. is cooled to 70° C.
1. A toner comprising:
a binder resin containing a non-crystalline resin and a crystalline resin;
a colorant; and,
a releasing agent,
wherein the releasing agent is an ester wax and has a melting point of 55° C. to 80° C., and
wherein the toner satisfies the following Expressions 1 and 2:
20,000 Pa·s≦ G 1≦50,000 Pa·s; and (Expression 1)
( G 4/ G 2)/( G 3/ G 1)≦1.00, (Expression 2)
where G 1 is a storage modulus, G 2 is a loss modulus, G 3 is a storage modulus and G 4 is a loss modulus, and the storage modulus G 1 and the loss modulus G 2 are measured at 80° C. when the toner is heated from 70° C. to 150° C. and the storage modulus G 3 and the loss modulus G 4 are measured at 80° C. when the toner heated to 150° C. is cooled to 70° C.
wherein
the crystalline resin in the binder resin comprises a crystalline polyester resin, and the non-crystalline resin in the binder resin comprises an unmodified polyester resin and a modified polyester resin,
the modified polyester resin is contained in the toner in an amount of 1% by mass to 20% by mass of the toner,
the crystalline polyester resin is contained in the toner in an amount of 0.1% by mass to 10% by mass of the toner, and
the ester wax comprises ester compounds having 44 or more carbon atoms in an amount of 45% to 48%, based on the total amount of the ester wax.
2. The toner according to claim 1 ,
wherein the toner satisfies the following Expression 1a:
30,000 Pa·s≦ G 1≦46,000 Pa·s. (Expression 1a)
3. The toner according to claim 1 ,
wherein the toner satisfies the following Expression 3:
1.00≦ G 2/ G 1≦1.30. (Expression 3)
4. The toner according to claim 1 ,
wherein the toner satisfies the following Expression 4:
0.80≦ G 3/ G 1. (Expression 4)
5. The toner according to claim 1 ,
wherein the toner is produced by: dissolving or dispersing, in an organic solvent, the binder resin containing the non-crystalline resin and the crystalline resin, an active hydrogen group-containing compound, a binder resin precursor containing a site reactive with the active hydrogen group-containing compound, the colorant and the releasing agent, to thereby prepare a solution or dispersion liquid; emulsifying the solution or dispersion liquid in an aqueous medium, to thereby prepare an emulsion; allowing the binder resin precursor and the active hydrogen group-containing compound to react in the emulsion; and removing the organic solvent.
6. A developer comprising:
a toner,
wherein the toner comprises:
a binder resin containing a non-crystalline resin and a crystalline resin;
a colorant; and,
a releasing agent,
wherein the releasing agent is an ester wax and has a melting point of 55° C. to 80° C., and
wherein the toner satisfies the following Expressions 1 and 2:
20,000 Pa·s≦ G 1≦5 50,000 Pa·s; and (Expression 1)
( G 4/ G 2)/( G 3/ G 1)≦1.00, (Expression 2)
where G 1 is a storage modulus, G 2 is a loss modulus, G 3 is a storage modulus and G 4 is a loss modulus, and the storage modulus G 1 and the loss modulus G 2 are measured at 80° C. when the toner is heated from 70° C. to 150° C. and the storage modulus G 3 and the loss modulus G 4 are measured at 80° C. when the toner heated to 150° C. is cooled to 70° C. wherein
the crystalline resin in the binder resin comprises a crystalline polyester resin, and the non-crystalline resin in the binder resin comprises an unmodified polyester resin and a modified polyester resin,
the modified polyester resin is contained in the toner in an amount of 1% by mass to 20% by mass of the toner,
the crystalline polyester resin is contained in the toner in an amount of 0.1% by mass to 10% by mass of the toner, and
the ester wax comprises ester compounds having 44 or more carbon atoms in an amount of 45% to 48%, based on the total amount of the ester wax.