Porogen compositions, methods of making and uses
The present specification discloses porogen compositions comprising a core material and shell material, methods of making such porogen compositions, methods of forming such porous materials using such porogen compositions, biocompatible implantable devices comprising such porous materials, and methods of making such biocompatible implantable devices.
1. A method for forming a breast implant, the method comprising the steps of:
(a) coating a base material with an uncured elastomer base to form an elastomer coated base shell, wherein the uncured elastomer base comprises a silicon-based elastomer and a solvent;
(b) coating the elastomer coated base shell with porogens to form an elastomer coated porogen mixture, wherein each of the porogens comprises a shell material and a core material, wherein the core material comprises at least two compounds, wherein the shell material has a melting temperature that is lower than a melting temperature of the core material;
(c) repeating step (a);
(d) repeating step (b);
(e) treating the elastomer coated porogen mixture such that the porogens are fused to form a porogen scaffold and the uncured elastomer base is cured; and
(f) removing the porogen scaffold, wherein the removing the porogen scaffold results in the base material with porous material.
2. The method of claim 1 , wherein the core material comprises sucrose and starch, and the shell material comprises polyethylene glycol.
3. The method of claim 2 , wherein the porogen composition comprises about 35% to about 50% sucrose, about 10% to about 15% starch, and about 40% to 50% polyethylene glycol, by weight.
4. The method of claim 3 , wherein the porogen composition comprises about 45% sucrose, about 10% starch, and about 45% polyethylene glycol, by weight.
5. The method of claim 3 , wherein the porogen composition comprises about 40% sucrose, about 15% starch, and about 45% polyethylene glycol, by weight.
6. The method of claim 3 , wherein the porogen composition comprises a mean porogen diameter of about 300 μm to about 650 μm.
7. The method of claim 1 , wherein steps (a)-(d) are conducted at about 20° C. to about 30° C., and step (e) is conducted in the range of about 100° C. to about 150° C.
8. The method of claim 1 , wherein steps (a)-(d) are conducted at about 20° C. to about 25° C., and step (e) is conducted in the range of about 110° C. to about 135° C.
9. The method of claim 1 , wherein step (e) is conducted at about 126° C. for about 85 minutes.