Biaxially oriented polyethylene terephthalate film and method for producing same
This film provides a polyethylene terephthalate film whereby dimensional variation in various steps can be reduced, particularly when the film is used as a substrate film for a flexible device, and that is suitable as a substrate film having minimal curl and excellent appropriateness for processing. This biaxially oriented polyethylene terephthalate film has a degree of crystallinity (Xc) of 0.35 to 0.50, the intrinsic viscosity (IV) of the resin constituting the film is 0.66-1.0 dl/g, the coefficient of thermal expansion at a temperature of 50-170° C. in each of the machine direction and transverse direction of the film is 0.29 ppm/° C., and the degree of thermal shrinkage at 180° C. in each of the machine direction and transverse direction of the film is 0.5%-1.0%.
1. A biaxially oriented polyethylene terephthalate film comprising:
at least polyethylene terephthalate resin and having a degree of crystallinity (Xc) of more than 0.35 and 0.50 or less,
the resin that constitutes the film having an intrinsic viscosity (IV) of 0.66 to 1.0 dl/g, and
the film having a coefficient of thermal expansion of 0 to 29 ppm/° C. in a temperature range of 50° C. to 170° C. in both the film's machine direction and transverse direction and a degree of thermal shrinkage of −0.5% to 1.0% at 180° C. in both the film's machine direction and transverse direction.
2. The biaxially oriented polyethylene terephthalate film as described in claim 1 , wherein the intrinsic viscosity (IV) of the resin that constitutes the film is 0.68 to 1.0 dl/g.
3. The biaxially oriented polyethylene terephthalate film as described in claim 1 , wherein both the coefficient of thermal expansion in the machine direction of the film and that in its transverse direction are 0 to 25 ppm/° C. in a temperature range of 50° C. to 170° C.
4. The biaxially oriented polyethylene terephthalate film as described in claim 1 , wherein a minor melting peak temperature (T-meta) occurs at 210° C. to 240° C.
5. The biaxially oriented polyethylene terephthalate film as described in claim 1 , wherein the film haze is 0% to 3%.
6. The biaxially oriented polyethylene terephthalate film as described in claim 1 , wherein the change in film haze is 0% to 3.0% when the film is heat-treated at 180° C. for 30 minutes.
7. The biaxially oriented polyethylene terephthalate film as described in claim 1 that is produced by:
melt-extruding polyethylene terephthalate resin while cooling for solidification to provide unstretched film,
biaxially stretching the unstretched film and heat-setting it in two or more stages differing in temperature, the heat set temperature at the anterior heat set stages, Ths1 (° C.), being 150° C. to 200° C., and the heat set temperature at the final stage, Ths2 (° C.), being 210° C. to 240° C., to provide biaxially stretched film,
cooling the biaxially stretched film at a temperature of 35° C. or lower after the heat set to provide cooled biaxially stretched film, and
subjecting the cooled biaxially stretched film to relaxation annealing treatment at a temperature higher than 200° C. and 235° C. or lower to provide the biaxially oriented polyethylene terephthalate film.
8. A production method for biaxially oriented polyethylene terephthalate film as described in claim 1 comprising:
melt-extruding polyethylene terephthalate resin while cooling for solidification to provide unstretched film,
biaxially stretching the unstretched film and heat-setting it in two or more stages differing in temperature, the heat set temperature at the anterior heat set stages, Ths1 (° C.), being 150° C. to 200° C., and the heat set temperature at the final stage, Ths2 (° C.), being 210° C. to 240° C., to provide biaxially stretched film,
cooling the biaxially stretched film at a temperature of 35° C. or lower after the heat set, and
subjecting the cooled biaxially stretched film to relaxation annealing treatment at a temperature higher than 200° C. and 235° C. or lower to provide the biaxially oriented polyethylene terephthalate film.
9. The film for organic EL substrates comprising biaxially oriented polyethylene terephthalate film as described in claim 1 .
10. The film for flexible solar battery substrates comprising biaxially oriented polyethylene terephthalate film as described in claim 1 .
11. The film for barrier substrates comprising biaxially oriented polyethylene terephthalate film as described in claim 1 .
12. The biaxially oriented polyethylene terephthalate film as described in claim 2 , wherein both the coefficient of thermal expansion in the machine direction of the film and that in its transverse direction are 0 to 25 ppm/° C. in a temperature range of 50° C. to 170° C.
13. The biaxially oriented polyethylene terephthalate film as described in claim 2 , wherein a minor melting peak temperature (T-meta) occurs at 210° C. to 240° C.
14. The biaxially oriented polyethylene terephthalate film as described in claim 3 , wherein a minor melting peak temperature (T-meta) occurs at 210° C. to 240° C.
15. The biaxially oriented polyethylene terephthalate film as described in claim 2 , wherein the film haze is 0% to 3%.
16. The biaxially oriented polyethylene terephthalate film as described in claim 3 , wherein the film haze is 0% to 3%.
17. The biaxially oriented polyethylene terephthalate film as described claim 4 , wherein the film haze is 0% to 3%.
18. The biaxially oriented polyethylene terephthalate film as described in claim 2 , wherein the change in film haze is 0% to 3.0% when the film is heat-treated at 180° C. for 30 minutes.
19. The biaxially oriented polyethylene terephthalate film as described in claim 3 , wherein the change in film haze is 0% to 3.0% when the film is heat-treated at 180° C. for 30 minutes.
20. The biaxially oriented polyethylene terephthalate film as described in claim 4 , wherein the change in film haze is 0% to 3.0% when the film is heat-treated at 180° C. for 30 minutes.