Method of forming and the resulting membrane composition for surgical site preservation
A method of forming and the resulting membrane composition for securement to a patient's bone or tissue to reduce the formation of tissue adhesions following a surgical procedure comprises a first component and a second component. The first component comprises a hydrogel including at least one crosslinked polymer. The second component comprises a textile component. The composition has a thickness between about two tenths of a millimeter (0.2 mm) to about six tenths of a millimeter (0.6 mm), a suture retention strength between about one Newton (1 N) to about thirteen Newtons (13 N), a static coefficient of friction between about one hundredth (0.01) and about one-half (0.5), a kinetic coefficient of friction between about one hundredth (0.01) and about one-half (0.5) and a flexibility of less than thirty millimeters (30 mm) bend length. A method of reducing the occurrence of tissue adhesions following surgery comprises applying the membrane composition to a surgical site.
1. A membrane for securement to a patient's bone or soft tissue to reduce the formation of tissue adhesions following a surgical procedure comprising a hydrogel including poly(vinyl alcohol) crosslinked to a second polymer, wherein a ratio of the poly(vinyl alcohol) to the second polymer ranges from about 75:1 to about 200:1, wherein the membrane has a static coefficient of friction between about one hundredth (0.01) and about one-half (0.5), a kinetic coefficient of friction between about one hundredth (0.01) and about one-half (0.5), and flexibility of less than thirty millimeters (30 mm) bend length, and wherein the membrane is formed into a single, planar sheet.
2. The membrane of claim 1 , wherein the second polymer is selected from the group consisting of poly(vinyl pyrrolidone), poly(hydroxyethylmethacrylate), poly(acrylamide), poly(acrylic acid), poly(acrylonitrile), polyethylene imine and poly(ethylene glycol).
3. The membrane of claim 1 , wherein the second polymer is poly(vinyl pyrrolidone).
4. The membrane of claim 1 , wherein the ratio ranges from about 75:1 to about 110:1.
5. The membrane of claim 1 , wherein the poly(vinyl alcohol) and the second polymer are crosslinked by a method selected from the group consisting of cryogelation, dehydration processing, radiation and exposure to chemicals.
6. The membrane of claim 1 , wherein the membrane has a thickness between about two tenths of a millimeter (0.2 mm) to about three millimeters (3 mm).
7. The membrane of claim 1 , wherein the membrane has a thickness between about three tenths of a millimeter (0.3 mm) to about one and one-half millimeters (1.5 mm).
8. The membrane of claim 1 , further comprising radiopaque markings.
9. A membrane composition for securement to a patient's bone or tissue comprising a hydrogel including poly(vinyl alcohol) and a second polymer selected from the group consisting of poly(vinyl pyrrolidone), poly(hydroxyethylmethacrylate), poly(acrylamide), poly(acrylic acid), poly(acrylonitrile), polyethylene imine and poly(ethylene glycol), wherein the poly(vinyl alcohol) and the second polymer are crosslinked and a ratio of the poly(vinyl alcohol) to the second polymer ranges from about 75:1 to about 200:1, wherein the composition has sufficient thickness, lubricity and flexibility to reduce the formation of tissue adhesions following a surgical procedure, and wherein the composition is formed into a single, planar sheet configured to adhere to the patient's spine to provide a plane of dissection between the spine and tissue.
10. The composition of claim 9 , wherein the second polymer is poly(vinyl pyrrolidone).
11. The composition of claim 9 , wherein the ratio ranges from about 75:1 to about 110:1.
12. The composition of claim 9 , wherein the poly(vinyl alcohol) and the second polymer are crosslinked by a method selected from the group consisting of cryogelation, dehydration processing, radiation and exposure to chemicals.
13. The composition of claim 9 , wherein the composition has a thickness between about two tenths of a millimeter (0.2 mm) to about three millimeters (3 mm).
14. The composition of claim 9 , wherein the composition has a thickness between about three tenths of a millimeter (03 mm) to about one and one-half millimeters (1.5 mm).
15. The composition of claim 9 , further comprising radiopaque markings.
16. The composition of claim 9 , wherein the composition has a water content between about fifty percent (50%) and about eighty-five percent (85%).
17. A membrane for use as a surgical implant comprising: a hydrogel including poly(vinyl alcohol) and poly(vinyl pyrrolidone), wherein a ratio of the poly(vinyl alcohol) to the poly(vinyl pyrrolidone) is between about 75:1 and about 200:1, wherein the membrane has a thickness between about three tenths of a millimeter (0.3 mm) and about one and one-half millimeters (1.5 mm), wherein the poly(vinyl alcohol) and the poly(vinyl pyrrolidone) are crosslinked by cryogelation, wherein the membrane has a water content between about sixty-eight percent (68%) and about seventy-five percent (75%).
18. The membrane of claim 17 , wherein the ratio is between about 75:1 and about 110:1.