Thermally tempered glass and methods and apparatuses for thermal tempering of glass

1. Process for strengthening a sheet, the process comprising:

cooling a sheet comprising a material, the sheet having first and second sheet surfaces, the material having a transition temperature, the sheet being at a temperature greater than the transition temperature at the start of the cooling, wherein the cooling is performed:

a. positioning the first sheet surface adjacent to a first heat sink surface with a first gap between the first sheet surface and the first heat sink surface such that thermal conduction from the first sheet surface to the first heat sink surface occurs, the first gap having a length across the first gap of g 1 and an area of the first gap of A g1 ,

b. positioning the second sheet surface adjacent to a second heat sink surface with a second gap between the second sheet surface and the second heat sink surface such that thermal conduction from the second sheet surface to the second heat sink surface occurs, the second gap having a length across the second gap of g 2 and an area of the second gap of A g2 ,

c. providing a first flow of a first gas to the first gap and providing a second flow of a second gas to the second gap, the first gas having a heat capacity C p1 and a thermal conductivity k 1 , the second gas having a heat capacity C p2 and a thermal conductivity k 2 , the flow provided at a mass flow rate {dot over (m)} 1 of the first gas, wherein {dot over (m)} 1 is greater than zero and less than (2k 1 A g1 )/(g 1 C p1 ), to the first gap, and at a mass flow rate {dot over (m)} 2 of the second gas, wherein {dot over (m)} 2 is greater than zero and less than (2k 2 A g2 )/(g 2 C p2 ), to the second gap, whereby the first and second flows contact the sheet, and the sheet is cooled, by conduction more than by convection,

d. sufficiently to cool the sheet to a temperature below the transition temperature.

2. The process according to claim 1 , wherein the first heat sink surface has multiple first apertures and the second heat sink has multiple second apertures, and wherein providing a first flow of a first gas to the first gap comprises flowing the first gas to the first gap only through the multiple first apertures and wherein providing a second flow of a second gas to the second gap consists of flowing the second gas to the second gap only through the multiple second apertures.

3. Process according to claim 2 , wherein the first and second gaps are about 100 μm or less.

4. Process according to claim 3 , wherein the first gas is air.

5. Process according to claim 3 , wherein the first gas is helium.

6. Process according to claim 2 , wherein the multiple first and second apertures have a cross-sectional dimension of less than 0.5 mm.

7. Process according to claim 6 , wherein the multiple apertures in the first and second heat sink surfaces are within 20 degrees of perpendicular to the respective first and second heat sink surfaces.

8. Process according to claim 2 , wherein the multiple first and second apertures have a cross-sectional dimension of less than 0.01 mm.

9. Process according to claim 1 , further comprising the step of heating the sheet principally by conduction through a gas from a heat source, the step of heating the sheet principally by conduction being performed prior to the step of cooling the sheet.

10. A process according claim 1 , further comprising imparting a surface fictive temperature of the first surface of the sheet, as measured by Raman shift, of at least 50° C. relative to a glass transition temperature of the sheet.

11. Process for strengthening a sheet, the process comprising:

a. supporting at least a portion of a sheet on a first surface thereof, at least in part, by a flow or a pressure of a gas delivered to a gap between the first surface and a first heat sink, wherein the sheet comprises a glass having a transition temperature and the sheet is at a temperature greater than the transition temperature of the glass;

b. cooling the sheet, by thermal conduction more than by convection, from the first surface of the sheet through the gas to the first heat sink, to a temperature below the transition temperature.

12. Process for strengthening a sheet, the process comprising:

Heating a sheet comprising a material having first and second sheet surfaces, the material having a transition temperature, the heating performed sufficiently to bring the sheet above the transition temperature;

positioning the first sheet surface adjacent to a first heat sink surface across a first gap, the first heat sink surface having first multiple apertures;

positioning the second sheet surface adjacent to a second heat sink surface across a second gap, the second heat sink surface having second multiple apertures;

delivering a gas into the first and second gaps through the first and second multiple apertures and cooling the sheet by conduction more than by convection, and to a temperature below the transition temperature.