Propylene-based impact copolymers
A propylene-based impact copolymer (ICP) and composition including the ICP, the ICP comprising a polypropylene homopolymer and within the range of from 10 wt % to 45 wt % of propylene copolymer based on the weight of the ICP, wherein the copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer, the propylene-based impact copolymer having a Melt Flow Rate (230° C./2.16 kg) within the range of from 10 g/10 min to 50 g/10 min and an Elongation at Break of greater than 70%.
1. A propylene-based impact copolymer (ICP) comprising:
a polypropylene homopolymer having an Mw/Mn within a range of from 3.0 to 5.0; and
within a range of from 10 wt % to 45 wt % of single-reactor propylene copolymer based on the weight of the ICP, wherein the propylene copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer, the propylene copolymer having a Mw/Mn within a range of from 3.0 to 9.0 and a Mz/Mw of less than 3.0;
the propylene-based impact copolymer having a melt flow rate (230° C./2.16 kg) within a range of from 10 g/10 min to 50 g/10 min and an elongation at break of greater than 60%.
2. An exterior automotive component comprising the propylene-based impact copolymer of claim 1 .
3. A propylene-based impact copolymer (ICP) comprising:
a polypropylene homopolymer having an Mw/Mn within a range of from 3.0 to 5.0; and
within a range of from 10 wt % to 45 wt % of single-reactor propylene copolymer based on the weight of the ICP, wherein the propylene copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer, the propylene copolymer having a Mz/Mw of less than 3.0;
the propylene-based impact copolymer having a melt flow rate (230° C./2.16 kg) within a range of from 10 g/10 min to 50 g/10 min and an elongation at break of greater than 60% and
wherein the polypropylene homopolymer forms a continuous phase and the propylene copolymer forms rubber domains having an average size within a range of from 0.40 μm to 0.90 μm.
4. The propylene-based impact copolymer of claim 3 , wherein the gloss (60°) is within a range of from 40 to 90% (ASTM D523).
5. The propylene-based impact copolymer of claim 3 , wherein the heat deflection temperature is within a range of from 70° C. to 125° C.
6. The propylene-based impact copolymer of claim 3 , wherein the flexural modulus (1% Secant, ASTM D 790A) is within a range of from 120 kpsi to 300 kpsi.
7. The propylene-based impact copolymer of claim 3 , wherein the propylene copolymer comprises within a range of from 20 to 34 wt % ethylene derived units.
8. The propylene-based impact copolymer of claim 3 , having within the range of from 22 wt % to 30 wt % of the propylene copolymer based on the weight of the ICP.
9. The propylene-based impact copolymer of claim 3 , wherein the gloss (60°) is within a range of from 40 to 90% (ASTM D523).
10. The propylene-based impact copolymer of claim 3 , wherein the heat deflection temperature is within a range of from 70° C. to 125° C.
11. The propylene-based impact copolymer of claim 3 , wherein the flexural modulus (1% Secant, ASTM D 790A) is within a range of from 120 kpsi to 300 kpsi.
12. The propylene-based impact copolymer of claim 3 , wherein the propylene copolymer comprises within a range of from 20 to 34 wt % ethylene derived units.
13. The propylene-based impact copolymer of claim 3 , having within a range of from 22 wt % to 30 wt % of the propylene copolymer based on the weight of the ICP.
14. The propylene-based impact copolymer of claim 3 , wherein the impact copolymer is reactor grade granules having an average particle size within a range of from 1200 μm to 2800 μm and produced at a rate greater than 30,000 lbs/hr (13,620 kg/hr).
15. An exterior automotive component comprising the propylene-based impact composition of claim 3 .
16. A thermoplastic polyolefin composition comprising a propylene-based impact copolymer (ICP) comprising a polypropylene homopolymer and within a range of from 10 wt % to 45 wt % of propylene copolymer based on the weight of the ICP,
wherein the propylene copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer,
the propylene-based impact copolymer having a melt flow rate (230° C./2.16 kg) within a range of from 10 g/10 min to 50 g/10 min and an elongation at break of greater than 60%; and the composition comprising
within a range of from 5 wt % to 30 wt % of an ethylene-based plastomer, within the range from 6 to 30 wt % of filler, and within a range of from 20 wt % to 80 wt % of the ICP, wherein the weight percentages are based on the total weight of the composition; and
wherein the polypropylene homopolymer forms a continuous phase and the propylene copolymer forms rubber domains having an average size within a range of from 0.40 μm to 0.90 μm.
17. The thermoplastic polyolefin composition of claim 16 , wherein a impact copolymer is reactor grade granules having an average particle size within the range of from 1200 μm to 2800 μm and produced at a rate greater than 30,000 lbs/hr (13,620 kg/hr).
18. The thermoplastic polyolefin composition of claim 16 , wherein the impact copolymer has a gloss (60°) within a range of from 40 to 90% (ASTM D523).
19. The thermoplastic polyolefin composition of claim 16 , wherein the impact copolymer has a heat deflection temperature within a range of from 70° C. to 125° C.
20. The thermoplastic polyolefin composition of claim 16 , wherein the impact copolymer has a flexural modulus (1% Secant, ASTM D 790A) within a range of from 120 kpsi to 300 kpsi.
21. The thermoplastic polyolefin composition of claim 16 , wherein the impact copolymer has a tensile strength at yield within a range of from 2500 psi to 5500 psi.
22. The thermoplastic polyolefin composition of claim 16 , wherein the impact copolymer has a notched Izod impact at 23° C. as measured by ASTM D256A of greater than 4 ft-lb/in (213 J/m).
23. The thermoplastic polyolefin composition of claim 16 , wherein the impact copolymer has a notched Izod impact at 23° C. as measured by ISO 180/A of greater than 8 kJ/m 2 .
24. The thermoplastic polyolefin composition of claim 16 , wherein the polypropylene homopolymer has a molecular weight distribution (Mw/Mn) within a range of from 3.0 to 9.0; and wherein the propylene copolymer has a Mw/Mn within a range of from 3.0 to 9.0.
25. The thermoplastic polyolefin composition of claim 16 , wherein the propylene copolymer is an ethylene-propylene copolymer.
26. The thermoplastic polyolefin composition of claim 6 , having a notched Izod impact at 23° C. as measured by ISO 180/A of at least 48 kJ/m 2 at 23° C.; and a notched Izod impact of at least 4 kJ/m 2 at −30° C.
27. The thermoplastic polyolefin composition of claim 16 , having an elongation at break (ISO 527) of at least 70%.
28. The thermoplastic polyolefin composition of claim 16 , having a flexural modulus (chord, ISO 178) of at least 200 MPa.
29. The thermoplastic polyolefin composition of claim 16 , wherein the Mw/Mn of the polypropylene homopolymer is within a range of from 3.0 to 5.0.
30. The thermoplastic polyolefin composition of claim 16 , wherein the propylene copolymer comprises within a range of from 20 to 34 wt % ethylene derived units.
31. An exterior automotive component comprising the composition of claim 16 .
32. A thermoplastic polyolefin composition comprising a propylene-based impact copolymer (ICP), comprising a polypropylene homopolymer and within a range of from 10 wt % to 45 wt % of propylene copolymer based on the weight of the ICP;
wherein the propylene copolymer comprises from 20 wt % to 44 wt % ethylene, 1-butene, 1-hexene and/or 1-octene derived units and from 80 to 56 wt % propylene-derived units based on the weight of the propylene copolymer
the propylene-based impact copolymer having a melt flow rate (230° C./2.16 kg) within a range of from 10 g/10 min to 50 g/10 min and an elongation at break of greater than 60%; and the composition comprising
within a range of from 2 wt % to 25 wt % of an ethylene-based plastomer, within a range from 0.5 to 6 wt % of filler, and within a range of from 70 wt % to 98 wt % of the ICP, wherein the weight percentages are based on the total weight of the composition.
33. The thermoplastic polyolefin composition of claim 32 , having a notched Izod impact at 23° C. as measured by ISO 180/A of at least 48 kJ/m 2 at 23° C.; and a notched Izod impact of at least 4 kJ/m 2 at −30° C.
34. The thermoplastic polyolefin composition of claim 32 , having an elongation at break (ISO 527) of at least 60%.
35. The thermoplastic polyolefin composition of claim 32 , having a flexural modulus (chord, ISO 178) of at least 500 MPa.
36. The thermoplastic polyolefin composition of claim 32 , wherein the Mw/Mn of the polypropylene homopolymer is within a range of from 3.0 to 5.0.
37. The thermoplastic polyolefin composition of claim 32 , wherein the propylene copolymer comprises within a range of from 20 to 34 wt % ethylene derived units.
38. An interior automotive component comprising the thermoplastic polyolefin composition of claim 32 .